Influence of light-curing mode on the cytotoxicity of resin-based surface sealants

Antimicrobial Properties of the Triclosan-Loaded Polymeric Composite Based on Unsaturated Polyester Resin: Synthesis, Characterization and Activity

The manufacturing of sanitary and household furniture on a large scale with inherently antimicrobial properties is an essential field of research. This work focuses on the synthesis of polymer composites based on the unsaturated polyester of resin loaded with 5 wt.%-Triclosan produced by a co-mixing approach on automated technological complex with a potential for broad applications. According to findings, the polymer composite has a non-porous structure (surface area < 1.97 m2/g) suitable for sanitary applications to reduce the growth of bacteria. The chemical composition confirmed the presence of major elements, and the inclusion of Triclosan was quantitatively confirmed by the appearance of chlorine on XRF (1.67 wt.%) and EDS (1.62 wt.%) analysis. Thermal analysis showed the difference of 5 wt.% in weight loss, which confirms the loading of Triclosan into the polymer matrix. The polymer composite completely inhibited the strains of S. aureus 6538-P, S. aureus 39, S. epidermidis 12228, and Kl. Pneumoniae 10031 after 5-min contact time. The antimicrobial effects against Kl. pneumoniae 700603, Ps. aeruginosa 9027 and Ps. aeruginosa TA2 strains were 92.7%, 85.8% and 18.4%, respectively. The inhibition activity against C. albicans 10231 and C. albicans 2091 was 1.6% and 82.4%, respectively; while the clinical strain of C. albicans was inhibited by 92.2%. The polymer composite loaded with 5 wt.%-Triclosan displayed a stability over the period that illustrates the possibility of washing the composite surface.

Margin Integrity of Bulk-Fill Composite Restorations in Primary Teeth

This in vitro study examined the margin integrity of sculptable and flowable bulk-fill resin composites in Class II cavities of primary molars. Standardized Class II cavities were prepared in human primary molars and restored with the following resin composite materials after application of a universal adhesive: a sculptable bulk-fill composite (Tetric EvoCeram Bulk Fill (TEC) or Admira Fusion x-tra (AFX)), a flowable bulk-fill composite (Venus Bulk Fill (VBF) or SDR), or a conventional composite (Filtek Supreme XTE (FS)). The bulk-fill materials were applied in 4 mm layers, while the conventional composite was applied in either 2 mm (FS2, positive control) or 4 mm layers (FS4, negative control). The specimens were exposed to thermo-mechanical loading (TML) in a computer-controlled masticator. A quantitative margin analysis was performed both before and after TML using scanning electron microscopy, and the percentage of continuous margins (margin integrity) was statistically analyzed (α = 0.05). All composites showed a significant decline in margin integrity after TML. AFX exhibited the significantly highest margin integrity of all materials after TML (97.5 ± 2.3%), followed by FS2 (79.2 ± 10.8%), TEC (73.0 ± 9.1%), and FS4 (71.3 ± 14.6%). SDR (43.6 ± 22.3%) and VBF (25.0 ± 8.5%) revealed the lowest margin integrity. In conclusion, the tested sculptable bulk-fill materials show similar or better margin integrity in primary molars than the conventional resin composite placed in 2 mm increments.

A New Customized Bioactive Glass Filler to Functionalize Resin Composites: Acid-Neutralizing Capability, Degree of Conversion, and Apatite Precipitation

This study introduced an experimental bioactive glass (BG) with a lower Na₂O content than conventional BG 45S5 (10.5 wt% vs. 24.5 wt%), additionally containing CaF₂ (12 wt%) and a network connectivity similar to that of BG 45S5. A series of experimental composites functionalized with 5-40 wt% of the novel BG was prepared and compared to a corresponding series of experimental composites functionalized with 5-40 wt% of BG 45S5. Commercial acidneutralizing materials (alkasite, giomer, and glass ionomer) were used as references. The capabilities of the materials to neutralize hydrochloric acid (pH = 2.6) and lactic acid (pH = 4.5) were evaluated by real-time pH measurements over 1 h. The degree of conversion and precipitation of calcium phosphate were also investigated. Data were analyzed using one-way and Welch ANOVA at an overall level of significance of 0.05. The acid-neutralizing potential of the experimental BG incorporated into resin composites was generally comparable to that of BG 45S5, and better than that of a giomer and glass ionomer. Fluorine was identified in the precipitate that developed on the composites functionalized with the experimental BG, suggesting a capability of forming fluorapatite. Unlike the 45S5 composition, the experimental BG did not impair the degree of conversion of resin composites. The novel BG filler is therefore an interesting candidate for future investigations of caries-preventive resin composites, and their potential clinical applicability for restorative, preventive, and orthodontic purposes.

Light Transmittance and Polymerization of Bulk-Fill Composite Materials Doped with Bioactive Micro-Fillers

This study investigated the effect of bioactive micro-fillers on the light transmittance and polymerization of three commercially available bulk-fill resin composites. These were mixed with 20 wt% bioactive glass 45S5, Portland cement, inert dental barium glass, or nothing (controls). Composites were photo-activated and light transmittance through 4 mm thick specimens was measured in real time. Moreover, degree of conversion (DC) and Knoop hardness (KHN) were assessed. Light transmittance of all bulk-fill composites significantly decreased (p < 0.05) with addition of 20 wt% bioactive glass 45S5 but not when inert barium glass was added. For bulk-fill composites modified with Portland cement, light irradiance dropped below the detection limit at 4 mm depth. The DC at the top surface of the specimens was not affected by addition of bioactive or inert micro-fillers. The bottom-to-top ratio of both DC and KHN surpassed 80% for bulk-fill composites modified with 20 wt% bioactive or inert glass fillers but fell below 20% when the composites were modified with Portland cement. In contrast to Portland cement, the addition of 20 wt% bioactive glass maintains adequate polymerization of bulk-fill composites placed at 4 mm thickness, despite a decrease in light transmittance compared to the unmodified materials.

Genotoxic potential of dental bulk-fill resin composites

OBJECTIVE

To investigate both genotoxicity and hardening of bulk-fill composite materials applied in 4-mm layer thickness and photo-activated for different exposure times.

METHODS

Three flowable bulk-fill materials and one conventional flowable composite were filled in molds (height: 4mm) and irradiated for 20 or 30s. The top (0mm) and bottom (4mm) specimen surface were mechanically scraped, and eluates (0.01g composite in 1.5ml RPMI 1640 cell culture media) prepared for each material, surface level and irradiation time. Genotoxicity was assessed in human leukocytes using both the alkaline comet assay and cytokinesis-blocked micronucleus assay, and Knoop hardness (KHN) was measured at the top and bottom specimen surface (n=8).

RESULTS

At both irradiation times, none of the bulk-fill composites significantly affected comet assay parameters used in primary DNA damage assessment or induced significant formation of any of the scored chromatin abnormalities (number of micronuclei, nuclear buds, nucleoplasmic bridges), whether eluates were obtained from the top or bottom surface. Furthermore, no decrease in KHN from the top to the bottom surface of the bulk-fill materials was observed. On the other hand, the conventional composite irradiated for 20s showed at 4-mm depth a significant increase in the percentage of DNA that migrated in the tail and a significant increase in the number of nuclear buds, as well as a significant decrease in KHN relative to the top surface.

SIGNIFICANCE

Bulk-fill resin composites, in contrast to conventional composite, applied in 4-mm thickness and photo-activated for at least 20s do not induce relevant genotoxic effects or mechanical instability.

Influence of light-curing distance on degree of conversion and cytotoxicity of etch-and-rinse and self-etch adhesives

BACKGROUND

The degree of conversion (DC) of resin based materials depends, beside other factors, on the light-intensity applied during light curing. A lower DC might be correlated with an increased cytotoxicity of the respective materials. Therefore, aim of the present study was to investigate the influence of the distance between light-curing tip and adhesives on their cytotoxicity and degree of conversion (DC).

METHODS

For the cytotoxicity assay, a total of 98 bovine dentine samples were prepared, distributed to seven groups (G1-G7; n = 14) and treated as follows: G1: untreated; G2-G4: OptiBond FL; G5-G7: OptiBond All-In-One. Adhesives were light-cured (1200 mW/cm(2)) at 1 mm (G2;G5), 4 mm (G3;G6) or 7 mm (G4;G7) distance. Samples were stored in culture media for 24 h and extracts were added to cell cultures (dental pulp cells and gingival fibroblasts) for a further 24 h. Finally, released lactate dehydrogenase activity (LDH) was photometrically determined, as measure for the cytotoxic effects of the extracts. The cytotoxicity assay was performed three times. Additionally, the DC of the adhesives was determined by FTIR spectroscopy. DC measurements were performed five times.

RESULTS

For both cell types, no significant difference of LDH release was observed between untreated control group (G1) and treated groups G2-G7 (p > 0.05, respectively), between the groups treated with same adhesive and light-cured at different distance (p > 0.05, respectively), as well as between groups treated with different adhesives and light-cured at the same distance (p > 0.05, respectively). Within the respective adhesive, no significant difference in the DC was observed when light-cured at different distance (p > 0.05, respectively), while OptiBond FL showed significantly higher DCs compared to OptiBond All-In-One when light-cured at same distances (p < 0.05, respectively).

CONCLUSIONS

The distance between light-curing tip and adhesive surface does not significantly influence either the cytotoxicity or the DC of the tested adhesives.