Fabrication of nanowire network AAO and its application in SERS

Ultrahighly Sensitive Surface-Enhanced Raman Spectroscopy Film of Silver Nanoparticles Dispersed in Three Dimensions on a Thin Alumina Nanowire Framework

To develop highly sensitive surface-enhanced Raman spectroscopy (SERS) films, various types of aggregated Ag nanowire (NW) and nanoparticle (NP) complex structures were fabricated using anodic aluminum oxide (AAO) templates and thermal evaporation. Aggregated AgNW structures with numerous tapered nanogaps were fabricated via Ag deposition on aggregated thin alumina nanowires of different lengths. AgNP complex structures were obtained by collapsing vertically aligned thin alumina nanowires 1 μm in length and depositing AgNPs on their tops and sides using surface tension during ethanol drying after functionalization. The Raman signal enhancement factors (EFs) of the samples were evaluated by comparing the SERS signal of the thiophenol (TP) self-assembled monolayer (SAM) on the nanostructures with the Raman signal of neat TP. EFs as high as ~2.3 × 107 were obtained for the optimized aggregated AgNW structure (NW length of 1 μm) and ~3.5 × 107 for the optimized AgNP complex structure. The large EF of the AgNP complex film is attributed mainly to the AgNPs dispersed in three dimensions on the sides of the thin alumina nanowires, strongly implying some important, relevant physics yet to be discovered and also a very promising nanostructure scheme for developing ultrahighly sensitive SERS films with EF > 108.

Controlling the Multiscale Topography of Anodized Aluminum Oxide Nanowire Structures for Surface-Enhanced Raman Scattering and Perfect Absorbers

In this study, a plasmonically active substrate is developed with the aim of controlling the perfect absorption and manipulating its optical properties for application in SERS (in NIR regime) and colorimetry. Based on modified fabrication method of anodized aluminum oxide (AAO), the cost-effective self-aggregation technique is presented to fabricate unique topography of bone-fire-like funnel-shaped collapsed and vertically aligned nanowire structures. The length of the nanowire and the modification of surface topography induced by capillary force inside the nanowire are set to structural parameters, and the effect of their changes is closely studied. After deposition of 40 nm gold (Au) film on numerous AAO nanowire structures with different wire lengths and unique topography, the localized surface plasmon resonance excitation is generated, and also its application on reflection and SERS spectra have been shown quantitatively. The length of the wire and surface topography modification are identified as suitable parameters to tune the reflection/absorption (from <40 to >90%) as well as colorimetric effect. Finally, an optimized wire length of Au-coated AAO substrate in SERS sensing application with 3.92 × 10⁵ order of enhancement of rhodamine 6G (R6G) Raman signal is demonstrated.

APTES Duality and Nanopore Seed Regulation in Homogeneous and Nanoscale-Controlled Reduction of Ag Shell on SiO2 Microparticle for Quantifiable Single Particle SERS

Noble-metal nanoparticles size and packing density are critical for sensitive surface-enhanced Raman scattering (SERS) and controlled preparation of such films required to achieve reproducibility. Provided that they are made reliable, Ag shell on SiO₂ microscopic particles (Ag/SiO₂) are promising candidates for lab-on-a-bead analytical measurements of low analyte concentration in liquid specimen. Here, we selected nanoporous silica microparticles as a substrate for reduction of AgNO₃ with 3-aminopropyltriethoxysilane (APTES). In a single preparation step, homogeneous and continuous films of Ag nanoparticles are formed on SiO₂ surfaces with equimolar concentration of APTES and silver nitrate in ethanol. It is discussed that amine and silane moieties in APTES contribute first to an efficient reduction on the silica and second to capping the Ag nanoparticles. The high density and homogeneity of nanoparticle nucleation is further regulated by the nanoporosity of the silica. The Ag/SiO₂ microparticles were tested for SERS using self-assembled 4-aminothiophenol monolayers, and an enhancement factor of ca. 2 × 10⁶ is measured. Importantly, the SERS relative standard deviation is 36% when a single microparticle is considered and drops to 11% when sets of 10 microparticles are considered. As prepared, the microparticles are highly suitable for state-of-the-art quantitative lab-on-a-bead interrogation of specimens.

Fast anodization fabrication of AAO and barrier perforation process on ITO glass

Thin films of porous anodic aluminum oxide (AAO) on tin-doped indium oxide (ITO) substrates were fabricated through evaporation of a 1,000- to 2,000-nm-thick Al, followed by anodization with different durations, electrolytes, and pore widening. A faster method to obtain AAO on ITO substrates has been developed, which with 2.5 vol.% phosphoric acid at a voltage of 195 V at 269 K. It was found that the height of AAO films increased initially and then decreased with the increase of the anodizing time. Especially, the barrier layers can be removed by extending the anodizing duration, which is very useful for obtaining perforation AAO and will broaden the application of AAO on ITO substrates.