'Cold' crystallization in nanostructurized 80GeSe2-20Ga2Se3 glass

Water-Vapor Sorption Processes in Nanoporous MgO-Al2O3 Ceramics: the PAL Spectroscopy Study

The water-vapor sorption processes in nanoporous MgO-Al2O3 ceramics are studied with positron annihilation lifetime (PAL) spectroscopy employing positron trapping and positronium (Ps)-decaying modes. It is demonstrated that the longest-lived components in the four-term reconstructed PAL spectra with characteristic lifetimes near 2 and 60-70 ns can be, respectively, attributed to ortho-positronium (o-Ps) traps in nanopores with 0.3- and 1.5-1.8-nm radii. The first o-Ps decaying process includes "pick-off" annihilation in the "bubbles" of liquid water, while the second is based on o-Ps interaction with physisorbed water molecules at the walls of the pores. In addition, the water vapor modifies structural defects located at the grain boundaries in a vicinity of pores, this process being accompanied by void fragmentation during water adsorption and agglomeration during water desorption after drying.

Optical and Vibrational Spectra of CsCl-Enriched GeS2-Ga2S3 Glasses

Optical and FTIR spectroscopy was employed to study the properties of 80GeS2-20Ga2S3-CsCl chalcohalide glasses with CsCl additives in a temperature range of 77-293 K. It is shown that CsCl content results in the shift of fundamental absorption edge in the visible region. Vibrational bands in FTIR spectra of (80GeS2-20Ga2S3)100 - х (СsCl) x (x = 5, 10, and 15) are identified near 2500 cm(-1), 3700 cm(-1),, around 1580 cm(-1), and a feature at 1100 cm(-1). Low energy shifts of vibrational frequencies in glasses with a higher amount of CsCl can be caused by possible thermal expansion of the lattice and nanovoid agglomeration formed by CsCl additives in the inner structure of the Ge-Ga-S glass.