Nanotribological and Nanomechanical Properties Changes of Tooth After Bleaching and Remineralization in Wet Environment

Effect of highly concentrated bleaching gels on enamel microhardness and superficial morphology, and the recovery action of four remineralizing agents

BACKGROUND

Dental bleaching is a common clinical practice. The aim of this study is to investigate the effect of 35% hydrogen peroxide (HP) bleaching gel on the morphology and microhardness of enamel, and to analyze the effect of four remineralizing agents.

METHODS

One hundred blocks were prepared. The enamel surfaces were bleached with 35% HP in one session. The specimens were divided into four remineralization treatment groups (n = 25). G1: Tooth Mousse, G2: Remin-Pro, G3: Colgate Pro-Relif, G4: Mirafluor. The remineralizing protocol was applied 3 min per day for one week. Vickers microhardness (HV) measurements and SEM observations were performed at baseline, after bleaching, and after remineralizing treatment in all groups. Statistical analyses were performed using the paired t-test and ANOVA.

RESULTS

After bleaching, SEM showed an increase of irregularities on the surface of the samples. Enamel microhardness decreased a mean of 47.7 HV, equivalent to a mean decrease of 18.3% (p < 0.05). After remineralization, the HV increased in all groups between 16 and 33% (p < 0.01), recovering the initial microhardness of enamel samples. SEM images revealed a higher quantity of superficial mineral deposits in groups 1 and 2 compared to the rest of the groups.

CONCLUSIONS

The application of remineralizing products generates a significant increase in enamel microhardness. Tooth Mousse-treated samples showed a greater microhardness recovery, followed by Remin Pro. The superficial morphology of the samples reflects the results obtained in the HV tests.

Effect of Vital Bleaching on Micromorphology of Enamel Surface: an in Vitro Study

OBJECTIVES

The aims of this in vitro study was to investigate the effects of bleaching agents commonly used in micromorphology of the enamel surface and to assess the effect of concentration and of adding fluoride in the bleaching agents.

METHODS

Sixty freshly extracted intact teeth were stored in distilled water. One half of each tooth was served as control, the other part was treated with bleaching agent. Samples were randomly divided into six groups of ten, according to the bleaching agents: G1- at-home-CP10; G2- at-home-CP16; G3- at-home-CP22; G4- in-office-CP35; G5- in-office-HP40 with fluoride; G6- in-office-HP40 without fluoride. Enamel specimens for each group were then submitted to a quantitative scanning electron microscopy. Number of pores and their diameter were measured to assess porosity of enamel surface.

RESULTS

SEM analysis revealed enamel surface porosity after bleaching. Significant increase in number and major diameter of pores in bleached samples (p<0.001) were observed. The comparison between samples treated with 10% PC and samples treated with 22% PC showed significant increase in number of pores (p=0.006) and major diameter (p=0.001) from samples treated with 22% PC. Statistical analyses showed significant increase in the number of pores (p=0.006) from samples treated with 40% HP without fluoride compared to samples treated with 40% HP containing fluoride.

CONCLUSIONS

Bleaching products with low concentration cause less porosity at surface of the enamel compared to concentrated products. Adding fluoride in the bleaching agent appears to reduce porosity of enamel surface.