Evaluation of compressive strength, surface microhardness, solubility and antimicrobial effect of glass ionomer dental cement reinforced with silver doped carbon nanotube fillers

Enhancing Mechanical and Biological Properties of Zinc Phosphate Dental Cement with Akermanite and Hardystonite Nanoparticles: A Synthesis and Characterization Study

This study investigates the potential of incorporating akermanite and hardystonite nanoparticles (NPs) into commercially available zinc phosphate cement. Akermanite and hardystonite NPs were synthesized through a mechanical route and characterized using X-ray diffraction (XRD), fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The NPs were then added to the cement at a concentration of 5 wt%, and the physical and biological properties of the resulting composite were evaluated. The results showed that the incorporation of NPs led to a significant reduction in porosity (from 12.4% to 5.6%) and a notable improvement in compressive strength (from 90 to 120 MPa) compared to the control group. MTT assay revealed that the cement containing NPs exhibited no significant toxicity and even promoted cell growth and proliferation. Specifically, cell viability increased by 15%, and cell proliferation rate increased by 20% compared to the control group. These findings suggest that the designed cement has suitable mechanical and biological properties, making it a promising material for dental and orthopedic applications.

Effect of E-glass fibers addition on compressive strength, flexural strength, hardness, and solubility of glass ionomer based cement

BACKGROUND

In dentistry, glass-ionomer cements (GICs) are extensively used for a range of applications. The unique properties of GIC include fluoride ion release and recharge, chemical bonding to the tooth's hard tissues, biocompatibility, a thermal expansion coefficient like that of enamel and dentin, and acceptable aesthetics. Their high solubility and poor mechanical qualities are among their limitations. E-glass fibers are generally utilized to reinforce the polymer matrix and are identified by their higher silica content.

OBJECTIVES

The purpose of the study was to assess the impact of adding (10 wt% and 20 wt%) silane-treated E-glass fibers to traditional GIC on its mechanical properties (compressive strength, flexural strength, and surface hardness) and solubility.

METHODS

The characterization of the E-glass fiber fillers was achieved by XRF, SEM, and PSD. The specimens were prepared by adding the E-glass fiber fillers to the traditional GIC at 10% and 20% by weight, forming two innovative groups, and compared with the unmodified GIC (control group). The physical properties (film thickness and initial setting time) were examined to confirm operability after mixing. The evaluation of the reinforced GIC was performed by assessing the compressive strength, flexural strength, hardness, and solubility (n = 10 specimens per test). A one-way ANOVA and Tukey tests were performed for statistical analysis (p ≤ 0.05).

RESULTS

The traditional GIC showed the least compressive strength, flexural strength, hardness, and highest solubility. While the GIC reinforced with 20 wt% E-glass fibers showed the highest compressive strength, flexural strength, hardness, and least solubility. Meanwhile, GIC reinforced with 10 wt% showed intermediate results (P ≤ 0.05).

CONCLUSION

Using 20 wt% E-glass fiber as a filler with the traditional GIC provides a strengthening effect and reduced solubility.

Clinical Performance of Glass Ionomer Cement in Load-Bearing Restorations: A Systematic Review

Glass ionomer cement (GIC) is a self-adhesive dental restorative material composed of a polyacrylic acid liquid and fluoro-aluminosilicate glass powder. It is commonly used for cementation during dental restoration. This study aimed to systematically review the existing literature regarding the clinical performance of GIC in load-bearing dental restorations. A comprehensive literature search was conducted in EBSCO, PubMed, Embrace, and Cochrane databases. Only randomized controlled trials (RCTs) were included in the search, and a broad search technique was used, where inclusion and exclusion criteria were applied. After a thorough evaluation, 12 RCTs were extensively reviewed, and whether GIC is suitable for load-bearing restorations was determined. Significant variations in staining surface or margin, color match, translucency, esthetic anatomical form, retention, material fracture, marginal adaptation, surface luster, occlusal contour, wear, and approximal anatomical form indicated the unsuitability of GIC. By contrast, significance differences in patient view and periodontal response indicated that GIC is suitable. No significant differences in postoperative sensitivity, recurrence of caries, or tooth integrity were observed. Nevertheless, the results of the review demonstrated that the clinical performance of GIC is comparable to that of traditional restorative materials with regard to the parameters analyzed. GIC is a suitable restorative material for load-bearing restorations regarding surface margin, esthetic anatomical form, material retention and fracture, marginal adaptation, occlusal contour, wear, and approximal anatomical form. It reduces other parameters, such as postoperative sensitivity, recurrence of caries, and tooth integrity.

Evaluation of flexural strength, impact strength, and surface microhardness of self-cured acrylic resin reinforced with silver-doped carbon nanotubes

BACKGROUND

Poly-methyl methacrylate (PMMA) is a type of polymer mostly used to make denture bases. Self-cured acrylic resin (PMMA) can be used to repair a fractured acrylic denture base; however, even after repair, this area remains vulnerable. Carbon nanotubes (CNTs) could be used as a filler for polymer reinforcement. Furthermore, silver nanoparticles are efficient agents for the prevention of dental biofilm and improving their mechanical properties. The doping of CNTs with silver nanoparticles may lead to a synergistic interaction that is predicted to enhance the mechanical characteristics of the fillers.

OBJECTIVES

The aim of the study was to assess the influnce of manual incorporation of 0.5% weight percent (%wt.) of silver doped carbon nanotubes (Ag-doped CNTs) into commercial self-cured PMMA on its flexural strength, impact strength, and surface microhardness.

METHODS

In this investigation, a total of 60 specimens comprised of acrylic resin were employed. They are divided into two main groups: (a) the control group, which was made by using liquid monomer and commercial self-cured PMMA powder; and (b) the modified group, prepared by hand mixing the purchased silver-doped CNTs powder (0.5% wt.) to self-cured PMMA powder (99.5%wt.), and then the blended powder was incorporated into the liquid monomer. Flexural strength, flexural modulus, impact strength, and surface microhardness were evaluated. Independent sample t-tests were used to statistically analyze the data and compare the mean values of flexural strength, flexural modulus, impact strength, and surface microhardness (p-value ≤ 0.05).

RESULTS

The flexural strength of the modified groups with Ag-doped CNTs (132.4 MPa) was significantly greater than that of the unmodified (control) groups (63.2 MPa). Moreover, the flexural modulus of the modified groups with Ag-doped CNTs (3.067 GPa) was significantly greater than that of the control groups (1.47 GPa). Furthermore, the impact strength of the modified groups with Ag-doped CNTs (11.2 kJ/mm2) was significantly greater than that of the control groups (2.3 kJ/mm2). Furthermore, the microhardness of the modified groups with Ag-doped CNTs (29.7 VHN) was significantly greater than that of the control groups (16.4 VHN), (p-value = 0.0001).

CONCLUSION

The incorporation of 0.5% wt. silver doped CNTs fillers to the self-cured acrylic resin enhanced its flexural strength, flexural modulus, impact strength, and surface microhardness.

Physicochemical properties of AH plus bioceramic sealer, Bio-C Sealer, and ADseal root canal sealer

BACKGROUND

The aim of this study was to evaluate the physicochemical properties of two newly introduced premixed calcium silicate-based root canal sealers (AH Plus Bioceramic Sealer and Bio-C Sealer) compared to a resin-based root canal sealer (ADseal root canal sealer).

METHODS

Solubility, pH analysis, calcium ion release, and film thickness of each sealer were evaluated following ISO guidelines. The data were examined using the two-way ANOVA test. Furthermore, X-ray diffraction (XRD) examination was performed to investigate the crystalline phase of each type of sealer. X-ray fluorescence (XRF) analysis was done for the chemical elemental analysis of each sealer.

RESULTS

The least film thickness, highest alkalinity, and highest calcium ion release were all displayed by AH Plus Bioceramic Sealer. High solubility, high alkalinity, intermediate calcium ion release, and intermediate film thickness were all displayed by Bio-C Sealer. While ADseal root canal sealer displayed the greatest film thickness, least solubility, alkalinity, and calcium ion release.

CONCLUSIONS

Both AH Plus Bioceramic Sealer and Bio-C Sealer represented adequate properties to be considered a good sealer that could be used as a potential alternative to resin-based root canal sealers.