Osseointegration of TI6Al4V dental implants modified by thermal oxidation in osteoporotic rabbits

Surface Properties and In Vitro Corrosion Studies of Blasted and Thermally Treated Ti6Al4V Alloy for Bioimplant Applications

The biomedical Ti6Al4V alloy was thermally treated under sandblasting and mirror finish surface preparation conditions. The surface morphology, structure, roughness, wettability, and energy were characterized. Microhardness and in vitro corrosion studies were carried out. X-ray diffraction results showed a formation of rutile TiO₂ phase for thermally treated samples under different pretreated conditions. The thermally oxidized samples exhibited an increase in microhardness compared to the untreated mirror finish and sandblasted samples by 22 and 33%, respectively. The wettability study revealed enhanced hydrophilicity of blasted and thermally treated samples. The surface energy of the thermal treatment samples increased by 26 and 32.6% for mirror surface and blasted preconditions, respectively. The acquired in vitro corrosion results using potentiodynamic polarization measurement and electrochemical impedance spectroscopy confirmed the surface protective performance against corrosion in Hank's medium. The enhanced surface characteristics and corrosion protection of treated Ti6Al4V alloy give it potential for bio-implant applications.

Assessment of dental implant stability using resonance frequency analysis and quantitative ultrasound methods

Purpose Quantitative ultrasound (QUS) and resonance frequency analyses (RFA) are promising methods to assess the stability of dental implants. The aim of this in vivo preclinical study is to compare the results obtained with these two techniques with the bone-implant contact (BIC) ratio, which is the gold standard to assess dental implant stability.Methods Twenty-two identical dental implants were inserted in the tibia and femur of 12 rabbits, which were sacrificed after different healing durations (0, 4, 8 and 13 weeks). For each implant, the ultrasonic indicator (UI) and the implant stability quotient (ISQ) were retrieved just before the animal sacrifice using the QUS and RFA techniques, respectively. Histomorphometric analyses were carried out to estimate the bone-implant contact ratio.Results UI values were found to be better correlated to BIC values (R²=0.47) compared to ISQ values (R²=0.39 for measurements in one direction and R²=0.18 for the other direction), which were shown to be dependent on the direction of measurements. Errors realized on the UI were around 3.3 times lower to the ones realized on the ISQ.Conclusions QUS provide a better estimation of dental implant stability compared to RFA. This study paves the way for the future clinical development of a medical device aiming at assessing dental implant stability in a patient-specific manner. Clinical studies should confirm these results in the future.

Titanium Alloys for Dental Implants: A Review

The topic of titanium alloys for dental implants has been reviewed. The basis of the review was a search using PubMed, with the large number of references identified being reduced to a manageable number by concentrating on more recent articles and reports of biocompatibility and of implant durability. Implants made mainly from titanium have been used for the fabrication of dental implants since around 1981. The main alloys are so-called commercially pure titanium (cpTi) and Ti-6Al-4V, both of which give clinical success rates of up to 99% at 10 years. Both alloys are biocompatible in contact with bone and the gingival tissues, and are capable of undergoing osseointegration. Investigations of novel titanium alloys developed for orthopaedics show that they offer few advantages as dental implants. The main findings of this review are that the alloys cpTi and Ti-6Al-4V are highly satisfactory materials, and that there is little scope for improvement as far as dentistry is concerned. The conclusion is that these materials will continue to be used for dental implants well into the foreseeable future.

Influence of the Thermal Treatment to Address a Better Osseointegration of Ti6Al4V Dental Implants: Histological and Histomorphometrical Study in a Rabbit Model

Background

Pure titanium continues to be the first choice for dental implants and represents the gold standard for their biocompatibility and physical and mechanical characteristics, while the titanium alloy (Ti6Al4V) has good mechanical properties. The surface structure of the titanium oxide layer formation on the surface influences and improves the bone response around dental implants.

Purpose

The purpose of this study is to evaluate the influence of a thermal treatment of Ti6Al4V implant surfaces and the bone healing response in a rabbit model.

Methods

Altogether sixteen implants with same design were inserted into the distal femoral metaphysis. A screw (13 mm long, 4 mm in diameter) was inserted in an implant bed. Each rabbit received two implants, one in the left femur and one in the right femur. The samples were histologically and histomorphometrically evaluated at 8 weeks.

Results

A statistically significant difference (p = 0.000034) was present histologically in the percentages of bone-implant contact (BIC) between the test group (BIC = 69.25±4.49%.) and control group (BIC = 56.25 ± 4.8%) by one-way analysis of variance (ANOVA). Significance was set at p ≤ 0.05.

Conclusions

The outcome of the present study indicates a novel approach to improving bone healing around titanium implants.

Thermal oxidation and hydrofluoric acid treatment on the sandblasted implant surface: A histologic histomorphometric and biomechanical study

OBJECTIVES

This study aimed to analyze and compare the topographical, chemical, and osseointegration characteristics of a sandblasted acid-etched surface (SLA group), a sandblasted thermally oxidized surface (SO group), and a surface chemically modified by hydrofluoric (HF) acid (SOF group).

MATERIALS AND METHODS

Following the preparation and characterization of the relevant surfaces, 90 implants (30 for each group) were placed on the pelvic bone of six sheep. Resonance frequency analysis (RFA), insertion (ITV), removal torque value (RTV), and histomorphometric analyses (BIC%) were performed after three and 8 weeks of healing. The results were analyzed by nonparametric tests (p < 0.05).

RESULTS

The roughness value (Ra) in the SOF group was significantly lower than the SLA and the SO group (p = 0.136, p < 0.001, respectively). This resulted in a substantially inferior ITV 14.83 N/cm (SD: 4.04) than those achieved in the SLA and SO groups (19.50 (SD: 6.07) and 20.17 N/cm (SD: 8.95), respectively; p = 0.001). A statistically significant change in the RFA from the baseline (47.36 ISQ, SD: 6.93) to the 3rd week (62.56 ISQ, SD: 5.29) was observed in the SOF group only (p = 0.008). The highest postplacement RFA and RTV values were measured from the SLA group (61.11 ISQ, SD: 7.51 and 78.22 N/cm, SD: 28.73). The early-term (3rd week) BIC% was highest in the SO group (39.93%, SD: 16.14). After 8 weeks, the differences in BIC% values were statistically not significant.

CONCLUSIONS

Adjunct HF acid application on the thermally oxidized surface did not provide an additional benefit compared to the sandblasted and acid-etched surface (SLA group).