Influence of an acrylic polymer blend on the physical stability of film-coated theophylline pellets

Film-Forming Systems for the Delivery of DNDI-0690 to Treat Cutaneous Leishmaniasis

In cutaneous leishmaniasis (CL), parasites reside in the dermis, creating an opportunity for local drug administration potentially reducing adverse effects and improving treatment adherence compared to current therapies. Polymeric film-forming systems (FFSs) are directly applied to the skin and form a thin film as the solvent evaporates. In contrast to conventional topical dosage forms, FFSs strongly adhere to the skin, favouring sustained drug delivery to the affected site, reducing the need for frequent applications, and enhancing patient compliance. This study reports the first investigation of the use of film-forming systems for the delivery of DNDI-0690, a nitroimidazole compound with potent activity against CL-causing Leishmania species. A total of seven polymers with or without plasticiser were evaluated for drying time, stickiness, film-flexibility, and cosmetic attributes; three FFSs yielded a positive evaluation for all test parameters. The impact of each of these FFSs on the permeation of the model skin permeant hydrocortisone (hydrocortisone, 1% (w/v) across the Strat-M membrane was evaluated, and the formulations resulting in the highest and lowest permeation flux (Klucel LF with triethyl citrate and Eudragit RS with dibutyl sebacate, respectively) were selected as the FFS vehicle for DNDI-0690. The release and skin distribution of the drug upon application to Leishmania-infected and uninfected BALB/c mouse skin were examined using Franz diffusion cells followed by an evaluation of the efficacy of both DNDI-0690 FFSs (1% (w/v)) in an experimental CL model. Whereas the Eudragit film resulted in a higher permeation of DNDI-0690, the Klucel film was able to deposit four times more drug into the skin, where the parasite resides. Of the FFSs formulations, only the Eudragit system resulted in a reduced parasite load, but not reduced lesion size, when compared to the vehicle only control. Whereas drug delivery into the skin was successfully modulated using different FFS systems, the FFS systems selected were not effective for the topical application of DNDI-0690. The convenience and aesthetic of FFS systems alongside their ability to modulate drug delivery to and into the skin merit further investigation using other promising antileishmanial drugs.

In-Depth Study into Polymeric Materials in Low-Density Gastroretentive Formulations

The extensive use of oral dosage forms for the treatment of diseases may be linked to deficient pharmacokinetic properties. In some cases the drug is barely soluble; in others, the rapid transit of the formulation through the gastrointestinal tract (GIT) makes it difficult to achieve therapeutic levels in the organism; moreover, some drugs must act locally due to a gastric pathology, but the time they remain in the stomach is short. The use of formulations capable of improving all these parameters, as well as increasing the resident time in the stomach, has been the target of numerous research works, with low-density systems being the most promising and widely explored, however, there is further scope to improve these systems. There are a vast variety of polymeric materials used in low-density gastroretentive systems and a number of methods to improve the bioavailability of the drugs. This works aims to expedite the development of breakthrough approaches by providing an in-depth understanding of the polymeric materials currently used, both natural and synthetic, their properties, advantages, and drawbacks.

Controlled Release Film Forming Systems in Drug Delivery: The Potential for Efficient Drug Delivery

Despite many available approaches for transdermal drug delivery, patient compliance and drug targeting at the desired concentration are still concerns for effective therapies. Precise and efficient film-forming systems provide great potential for controlling drug delivery through the skin with the combined advantages of films and hydrogels. The associated disadvantages of both systems (films and hydrogels) will be overcome in film-forming systems. Different strategies have been designed to control drug release through the skin, including changes to film-forming polymers, plasticizers, additives or even model drugs in formulations. In the current review, we aim to discuss the recent advances in film-forming systems to provide the principles and review the methods of these systems as applied to controlled drug release. Advances in the design of film-forming systems open a new generation of these systems.

Preparation and Characterization of a Novel Aqueous Dispersion for Enteric Coating of Pantoprazole Sodium Pellets

The purpose of this work was to investigate a novel aqueous dispersion (Eudragit® L100-55) f or e nteric c oating o f drugs. Three different casting solutions, Eudragit® L100-55 aqueous dispersion, Eudragit® L 100-55 o rganic s olution, and Eudragit® L30D-55 aqueous dispersion, were used to prepare free films by the casting method. Drug-loaded pellets, prepared by the extrusion-spheronization method, were coated with one of these three coating solutions using the fluidized-bed spray coating technology. Properties of the free films were thoroughly investigated. Films formed by Eudragit® L100-55 aqueous dispersions showed similar properties to those formed by Eudragit® L100-55 organic solution regarding thermodynamic properties, moisture permeability, solubility and acid tolerance ability. Furthermore, the performance of the novel film was better than that formed by Eudragit® L30D-55 aqueous dispersion. Among the three enteric coating solutions, Eudragit® L100- 55 aqueous dispersion will be a promising aqueous dispersion for enteric coating and can be used in the development of enteric-coated preparations.

Novel extraction and application of okra gum as a film coating agent using theophylline as a model drug

The purpose of this study was to investigate the effect of extraction and application of okra gum as an aqueous film coating agent. Powdered okra pods dispersed in demineralized water was heated at 80 ± 2^oC for 30 minutes in the presence of sodium chloride. The filtrate was successively centrifuged at 4000 rpm for 30, 60, or 120 minutes and freeze dried. The samples were used as film former at different concentrations in aqueous film coating operations. Near infrared (nIR) absorption spectra, photomicrographs, and some physicochemical properties of the coated tablets were evaluated. The okra gum samples had different nIR spectra and possessed good processing and application quality due to relatively low viscosity. A six-fold concentration of this gum from the novel extraction yielded glossy theophylline tablets within a short time. A t (18) = 2.895, P < 0.005, t critical = 1.734 were obtained for the independent analysis of the hardness of core and coated theophylline tablets. A 3.0% concentration of the okra samples at a flow rate of 3 ml/min for 100 minutes showed that F = 3.798, DF = 29, P < 0.035, F critical = 3.354 in tablet hardness among samples and F = 15.632, DF = 29, P < 0.0001, F critical = 2.152 were obtained on film thickness among tablet samples during the coating and drying operation. Novel extraction process enhanced the film coating potential of okra gum by delivering more solids on the substrate at a shorter time with improved operation efficiency.

Comparison of physicomechanical properties of films prepared from organic solutions and aqueous dispersion of Eudragit RL

BACKGROUND AND THE PURPOSE OF THE STUDY

Mechanical properties of films prepared from aqueous dispersion and organic solutions of Eudragit RL were assessed and the effects of plasticizer type, concentration and curing were examined.

METHODS

Films were prepared from aqueous dispersion and solutions of Eudragit RL (isopropy alcohol-water 9:1) containing 0, 10 or 20% (based on polymer weight) of PEG 400 or Triethyl Citrate (TEC) as plasticizer using casting method. Samples of films were stored in oven at 60°C for 24 hrs (Cured). The stress-strain curve was obtained for each film using material testing machine and tensile strength, elastic modulus, %elongation and work of failure were calculated.

RESULTS AND MAJOR CONCLUSION

The films with no plasticizer showed different mechanical properties depending on the vehicle used. Addition of 10% or 20% of plasticizer decreased the tensile strength and elastic modulus and increased %elongation and work of failure for all films. The effect of PEG 400 on mechanical properties of Eudragit RL films was more pronounced. The differences in mechanical properties of the films due to vehicle decreased with addition of plasticizer and increase in its concentration. Curing process weakened the mechanical properties of the films with no plasticizer and for films with 10% plasticizer no considerable difference in mechanical properties was observed before and after curing. For those with 20% plasticizer only films prepared from aqueous dispersion showed remarkable difference in mechanical properties before and after curing. Results of this study suggest that the mechanical properties of the Eudragit RL films were affected by the vehicle, type of plasticizer and its concentration in the coating liquid.