Bivalves rapidly repair shells damaged by fatigue and bolster strength

Direct control of shell regeneration by the mantle tissue in the pearl oyster Pinctada fucata

Molluscs rapidly repair the damaged shells to prevent further injury, which is vital for their survival after physical or biological aggression. However, it remains unclear how this process is precisely controlled. In this study, we applied scanning electronic microscopy and histochemical analysis to examine the detailed shell regeneration process in the pearl oyster Pinctada fucata. It was found that the shell damage caused the mantle tissue to retract, which resulted in relocation of the partitioned mantle zones with respect to their correspondingly secreting shell layers. As a result, the relocated mantle tissue dramatically altered the shell morphology by initiating de novo precipitation of prismatic layers on the former nacreous layers, leading to the formation of sandwich-like "prism-nacre-prism-nacre" structure. Real-time PCR revealed the up-regulation of the shell matrix protein genes, which was confirmed by the thermal gravimetric analysis of the newly formed shell. The increased matrix secretion might have led to the change of CaCO₃ precipitation dynamics which altered the mineral morphology and promoted shell formation. Taken together, our study revealed the close relationship between the physiological activities of the mantle tissue and the morphological change of the regenerated shells.

Bivalves maintain repair when faced with chronically repeated mechanical stress

Even though mollusks' capacity to repair shell damage is usually studied in response to a single event, their shells have to defend them against predatory and environmental threats throughout their potentially multi-decadal life. We measured whether and how mollusks respond to chronic mechanical stress. Once a week for 7 months, we compressed whole live California mussels (Mytilus californianus) for 15 cycles at ∼55% of their predicted one-time breaking force, a treatment known to cause fatigue damage in shells. We found mussels repaired their shells. Shells of experimentally stressed mussels were just as strong at the end of the experiment as those of control mussels that had not been experimentally loaded, and they were more heavily patched internally. Additionally, stressed shells differed in morphology; they were heavier and thicker at the end of the experiment than control shells but they had increased less in width, resulting in a flatter, less domed shape. Finally, the chronic mechanical stress and repair came at a cost, with stressed mussels having higher mortality and less soft tissue than the control group. Although associated with significant cost, mussels' ability to maintain repair in response to ongoing mechanical stress may be vital to their survival in harsh and predator-filled environments.

Mussels Repair Shell Damage despite Limitations Imposed by Ocean Acidification

Bivalves frequently withstand shell damage that must be quickly repaired to ensure survival. While the processes that underlie larval shell development have been extensively studied within the context of ocean acidification (OA), it remains unclear whether shell repair is impacted by elevated pCO2. To better understand the stereotypical shell repair process, we monitored mussels (Mytilus edulis) with sublethal shell damage that breached the mantle cavity within both field and laboratory conditions to characterize the deposition rate, composition, and integrity of repaired shell. Results were then compared with a laboratory experiment wherein mussels (Mytilus trossulus) repaired shell damage in one of seven pCO2 treatments (400–2500 µatm). Shell repair proceeded through distinct stages; an organic membrane first covered the damaged area (days 1–15), followed by the deposition of calcite crystals (days 22–43) and aragonite tablets (days 51–69). OA did not impact the ability of mussels to close drill holes, nor the microstructure, composition, or integrity of end-point repaired shell after 10 weeks, as measured by µCT and SEM imaging, energy-dispersive X-ray (EDX) analysis, and mechanical testing. However, significant interactions between pCO2, the length of exposure to treatment conditions, the strength and inorganic content of shell, and the physiological condition of mussels within OA treatments were observed. These results suggest that while OA does not prevent adult mussels from repairing or mineralizing shell, both OA and shell damage may elicit stress responses that impose energetic constraints on mussel physiology.