Effect of stem preheating on the fatigue behaviour of bone cement around hip prostheses

An experimental study on the impact of prosthesis temperature on the biomechanical properties of bone cement fixation

PURPOSE

To investigate the effect of the femoral component and tibial plateau component temperature on the strength of cement fixation during total knee arthroplasty (TKA).

METHODS

Femoral prosthesis, tibial plateau prosthesis, and polypropylene mold base were used to simulate TKA for bone cement fixation. Pre-cooling or pre-warming of femoral and tibial plateau components at different temperatures (4 °C, 15 °C, 25 °C, 37 °C, 45 °C), followed by mixing and stirring of bone cement at laboratory room temperature (22 °C), were performed during research. The prosthesis and the base adhered together, and the bone cement was solidified for 24 h at a constant temperature of 37 °C to verify the hardness of the bone cement with a push-out test.

RESULTS

The push-out force of the femoral prosthesis after fixation was higher than that of the tibial plateau prosthesis, and with the increase of the prosthesis temperature, the push-out force after fixation of the bone cement also increased linearly and the porosity of the prosthetic cement in the tibia and femur decreased as the temperature increased.

CONCLUSION

Without changing the mixing temperature and solidification temperature, the fixation strength of the femoral prosthesis is higher than that of the tibial plateau prosthesis. Properly increasing the temperature of the prosthesis can increase the push-out force of the fixation strength.

METHODS FOR THE CHARACTERIZATION OF THE LONG-TERM MECHANICAL PERFORMANCE OF CEMENTS FOR VERTEBROPLASTY AND KYPHOPLASTY: CRITICAL REVIEW AND SUGGESTIONS FOR TEST METHODS

There is a growing interest towards bone cements for use in vertebroplasty and kyphoplasty, as such spine procedures are becoming more and more common. Such cements feature different compositions, including both traditional acrylic cements and resorbable and bioactive materials. Due to the different compositions and intended use, the mechanical requirements of cements for spinal applications differ from those of traditional cements used in joint replacement. Because of the great clinical implications, it is very important to assess their long-term mechanical competence in terms of fatigue strength and creep. This paper aims at offering a critical overview of the methods currently adopted for such mechanical tests. The existing international standards and guidelines and the literature were searched for publications relevant to fatigue and creep of cements for vertebroplasty and kyphoplasty. While standard methods are available for traditional bone cements in general, no standard indicates specific methods or acceptance criteria for fatigue and creep of cements for vertebroplasty and kyphoplasty. Similarly, a large number of papers were published on cements for joint replacements, but only few cover fatigue and creep of cements for vertebroplasty and kyphoplasty. Furthermore, the literature was analyzed to provide some indications of tests parameters and acceptance criteria (number of cycles, duration in time, stress levels, acceptable amount of creep) for possible tests specifically relevant to cements for spinal applications.

Effects of Cemented Hip Stem Pre-heating on Stem Push-out Strength

OBJECTIVE

To determine the effect on ultimate push-out load and cement-stem surface shear strength of thermally manipulating the cobalt-chromium-molybdenum (CoCrMo) alloy stems of bone cement-stem constructs.

METHODS

Satin-finished CoCrMo alloy stems were allocated to the following three groups with the predetermined temperatures: T24, ambient (24 °C); T37, body (37 °C); and T44, pre-heated stem (>44 °C). They were then inserted into hand-mixed high viscosity bone cement. Ultimate push-out load to failure was assessed with a servo hydraulic testing machine and the surface shear strength calculated. Data were compared among groups using the Kruskal-Wallis with Dunn's test. A P value of less than 0.05 was considered statistically significant.

RESULTS

According to Kruskal-Wallis analysis, ultimate push-out load and surface shear strength differed significantly between the groups (P = 0.001). The T37 and T44 groups had higher ultimate push-out loads and surface shear strengths than the T24 group (P = 0.04 and 0.001, respectively). However, there was no statistically significant difference in these two variables between the T37 and T44 groups (P = 0.08).

CONCLUSIONS

Pre-heating CoCrMo alloy stems enhance the ultimate push-out load and surface shear strength in vitro. The suggested temperature is 37 °C. This technique is recommended for hip arthroplasty procedures.

The effect of vacuum mixing and pre-heating the femoral component on the mechanical properties of the cement mantle

We investigated the effect of pre-heating a femoral component on the porosity and strength of bone cement, with or without vacuum mixing used for total hip replacement. Cement mantles were moulded in a manner simulating clinical practice for cemented hip replacement. During polymerisation, the temperature was monitored. Specimens of cement extracted from the mantles underwent bending or fatigue tests, and were examined for porosity. Pre-heating the stem alone significantly increased the mean temperature values measured within the mantle (+14.2 degrees C) (p < 0.001) and reduced the mean curing time (-1.5 min) (p < 0.001). The addition of vacuum mixing modulated the mean rise in the temperature of polymerisation to 11 degrees C and reduced the mean duration of the process by one minute and 50 seconds (p = 0.01 and p < 0.001, respectively). In all cases, the maximum temperature values measured in the mould simulating the femur were < 50 degrees C. The mixing technique and pre-heating the stem slightly increased the static mechanical strength of bone cement. However, the fatigue life of the cement was improved by both vacuum mixing and pre-heating the stem, but was most marked (+ 280 degrees C) when these methods were combined. Pre-heating the stem appears to be an effective way of improving the quality of the cement mantle, which might enhance the long-term performance of bone cement, especially when combined with vacuum mixing.