Preparation of Antifog Hard Coatings Based on Carboxy-Functionalized Polyhedral Oligomeric Silsesquioxane Cross-Linked with Oligo(ethylene glycol)s

In this study, we prepared antifog hard coatings by heating a mixture of carboxy-functionalized polyhedral oligomeric silsesquioxane (POSS-C) and oligo(ethylene glycol)s (OEGs, HO(CH2CH2O) n H, n = 1-6) in N,N-dimethylformamide, applying the mixture onto a glass substrate, and subsequently removing the solvent via heating. In addition, we evaluated the water resistance, hardness, and antifogging performance of the coatings. In particular, the coating produced at a 2:1 functional group ratio of POSS-C to tetraethylene glycol (OEG, n = 4) coating exhibited high surface hardness (6H), as determined using pencil scratch testing. The coating remained clear after exposure to the vapor of warm water at 40 °C at a height of 2 cm for 10 s, demonstrating its antifogging property. Furthermore, no dissolution or cracking was observed when the POSS-C/OEG coating (n = 4, COOH/OH = 2:1) was immersed in water at room temperature for 1 h, confirming its water resistance. The Fourier transform infrared/attenuated total reflectance results showed the formation of ester bonds, indicating the construction of a network structure that enhanced the water resistance and hardness of the coating.

Ionic Liquids Containing Silsesquioxane and Cyclic Siloxane Frameworks

This paper describes the author's recent work on the preparation and properties of thermally stable ionic liquids (ILs) containing siloxane frameworks. Quaternary ammonium and imidazolium salt-type ILs containing random oligosilsesquioxane frameworks were successfully prepared via the hydrolytic condensation of the corresponding organotrialkoxysilanes by using an aqueous superacid bis(trifluoromethanesulfonyl)imide (HNTf2 ) solution as a catalyst and solvent. Imidazolium salt-type ILs containing polyhedral oligomeric silsesquioxane (POSS) frameworks were also prepared through a reaction similar to that described above by using a water/methanol mixed solution of HNTf2 . In addition, amorphous POSSs with two types of ionic groups randomly distributed in the side chain were prepared. These POSSs were ILs exhibiting fluidity at relatively low temperatures. Furthermore, imidazolium and ammonium salt-type ILs containing cyclic oligosiloxane frameworks were prepared through a reaction similar to that of the corresponding organodialkoxysilanes. The thermal decomposition temperatures of the above ILs containing siloxane frameworks were higher than those of general ILs.