Fabrication aspects of PLA-CaP/PLGA-CaP composites for orthopedic applications: a review

For several decades, composites made of polylactic acid-calcium phosphates (PLA-CaP) and polylactic acid-co-glycolic acid-calcium phosphates (PLGA-CaP) have seen widespread uses in orthopedic applications. This paper reviews the fabrication aspects of these composites, following the ubiquitous materials science approach by studying "processing-structure-property" correlations. Various fabrication processes such as microencapsulation, phase separation, electrospinning, supercritical gas foaming, etc., are reviewed, with specific examples of their applications in fabricating these composites. The effect of the incorporation of CaP materials on the mechanical and biological performance of PLA/PLGA is addressed. In addition, this paper describes the state of the art on challenges and innovations concerning CaP dispersion, incorporation of biomolecules/stem cells and long-term degradation of the composites.

Influence of the charge relay effect on the silanol condensation reaction as a model for silica biomineralization

The catalytic effect of various sequential peptides for silica biomineralization has been studied. In peptide sequence design, lysine (K) and histidine (H) were selected as the standard amino acids and aspartic acid (D) was selected to promote the charge relay effects, such as in the enzyme active site. Therefore, homopolypeptides (K(10) and H(10)), block polypeptides (K(5)D(5) and H(5)D(5)), and alternate polypeptides [(KD)(5) and (HD)(5)] were designed, and the dehydration reaction ability of trimethylethoxysilane was investigated as a quantitative model of silica mineralization. The catalytic activity per basic residue of alternate polypeptide was the highest because of the charge relay effects at the surface of the peptide. In silica mineralization using tetraethoxysilane, spherical silica particles were obtained, and their size is related to the catalytic activities of the peptides in the model systems. From these results, the effect of the functional group combination by the peptide sequence design enables the control of the efficiency of mineralization and preparation of specific inorganic materials.

Hydroxyapatite nanoparticles as particulate emulsifier: fabrication of hydroxyapatite-coated biodegradable microspheres

Hydroxyapatite (HAp) nanoparticle-coated micrometer-sized poly(l-lactic acid) (PLLA) microspheres were fabricated via a "Pickering-type" emulsion route in the absence of any molecular surfactants. Stable oil-in-water emulsions were prepared using 40 nm HAp nanoparticles as a particulate emulsifier and a dichloromethane (CH(2)Cl(2)) solution of PLLA as an oil phase. It was clarified that the interaction between carbonyl/carboxylic acid groups of PLLA and the HAp nanoparticles at the CH(2)Cl(2)-water interface played a crucial role to prepare the stable Pickering-type emulsion. The HAp nanoparticle-coated PLLA microspheres were fabricated by the evaporation of CH(2)Cl(2) from the emulsion and characterized in terms of size, particle size distribution, and morphology using scanning/transmission electron microscopes. Scanning electron microscopy study and ultrathin cross section observation using transmission electron microscopy confirmed adsorption of the HAp nanoparticles only at the surface of the PLLA microspheres. Cell-adhesion experiments suggested the HAp nanoparticles on the surface of the PLLA microspheres promoted the cell adhesion and spreading.

Preparation of Porous Poly(Lactic Acid)/Hydroxyapatite Microspheres Intended for Injectable Bone Substitutes

Porous biodegradable microspheres were successfully obtained by an improvement single step and surfactant-free emulsion solvent evaporation method. The organic phase composed of PLA and dichloromethane was stirred in aqueous phase including Ca2+ ions to yield oil in water emulsion. During emulsification, stirring rate was increased so as to produce the W/O/W emulsion that results in microspheres with internal pores. The interface of internal water/oil was stable in W/O/W emulsion, which was explained that the bond between Ca2+ ions and carboxyl group of poly(lactic acid) would be stabilized the internal water/oil interface. Adding PO4 3- aqueous solution prompted to precipitate low crystallized hydroxyapatite on the external oil/water interface, and the precipitated hydroxyapatite would stabilizied microspheres formation. The resulting microspheres were approximately 100-500 µm with internal spherical pores of 10-200 µm in diameter. The porous biodegradable microspheres were expected to be utilized as injectable bone substitutes that allow bone ingrowth and bone regeneration.