Sr-doped nanowire modification of Ca-Si-based coatings for improved osteogenic activities and reduced inflammatory reactions

Biomedical coatings for orthopedic implants should facilitate osseointegration and mitigate implant-induced inflammatory reactions. In our study, Ca-Si coatings with Sr-containing nanowire-like structures (NW-Sr-CS) were achieved via hydrothermal treatment. In order to identify the effect of nanowire-like topography and Sr dopant on the biological properties of Ca-Si-based coatings, the original Ca-Si coating, Ca-Si coatings modified with nanoplate (NP-CS) and similar nanowire-like structure (NW-CS) were fabricated as the control. Surface morphology, phase composition, surface area, zeta potential and ion release of these coatings were characterized. The in vitro osteogenic activities and immunomodulatory properties were evaluated with bone marrow stromal cells (BMSCs) and RAW 264.7 cells, a mouse macrophage cell line. Compared with the CS and NP-CS coatings, the NW-CS coating possessed a larger surface area and pore volume, beneficial protein adsorption, up-regulated the expression levels of integrin β1, Vinculin and focal adhesion kinase and promoted cell spreading. Furthermore, the NW-CS coating significantly enhanced the osteogenic differentiation and mineralization as indicated by the up-regulation of ALP activity, mineralized nodule formation and osteoblastogenesis-related gene expression. With the introduction of Sr, the NW-Sr-CS coatings exerted a greater effect on the BMSC proliferation rate, calcium sensitive receptor gene expression as well as PKC and ERK1/2 phosphorylation. In addition, the Sr-doped coatings significantly up-regulated the ratio of OPG/RANKL in the BMSCs. The NW-Sr-CS coatings could modulate the polarization of macrophages towards the wound-healing M2 phenotype, reduce the mRNA expression levels of pro-inflammatory cytokines (TNF-α, IL-1β, IL-6) and enhance anti-inflammatory cytokines (IL-1ra, IL-10). The Sr-doped nanowire modification may be a valuable approach to enhance osteogenic activities and reduce inflammatory reactions.

Facile synthesis of calcium silicate hydrate using sodium dodecyl sulfate as a surfactant assisted by ultrasonic irradiation

Calcium silicate hydrate (CSH) consisting of nanosheets has been successfully synthesized assisted by a tip ultrasonic irradiation (UI) method using calcium nitrate (Ca(NO3)·4H2O), sodium silicate (Na2SiO3·9H2O) and sodium dodecyl sulfate (SDS) in water. Systematic studies found that reaction time of ultrasonic irradiation and concentrations of surfactant (SDS) in the system were important factors to control the crystallite size and morphologies. The products were characterized by X-ray power diffraction (XRD), field emission scanning electron microscopy (FESEM) and Fourier transform infrared spectrometry (FTIR). The size-strain plot (SSP) method was used to study the individual contributions of crystallite sizes and lattice strain on the peak broadening of the CSH. These characterization techniques revealed the successful formation of a crystalline phase with an average crystallite size of about 13 nm and nanosheet morphology at a reaction time of 10 min UI with 0.2 g SDS in solvent which were found to be optimum time and concentrations of SDS for the synthesis of CSH powders.

Fabrication of fibrous poly(butylene succinate)/wollastonite/apatite composite scaffolds by electrospinning and biomimetic process

In this paper, a novel kind of Poly(butylene succinate) (PBSU) /wollastonite/apatite composite scaffold was fabricated via electrospinning and biomimetic process. Pure PBSU scaffold and composite scaffolds with 12.5 wt% and 25 wt% wollastonite were firstly fabricated by electrospinning. SEM micrographs showed that all the electrospun scaffolds had homogeneous fibrous structures with interconnected pores and randomly oriented ultrafine fibers. The composite scaffolds were then surface modified using a biomimetic process. SEM and XRD results showed that apatite could deposit on the surfaces of the composite fibers after incubation in SBF and a novel fibrous structure with microspheres composed of worm-like apatite on composite fibers was formed. Incubation time and wollastonite content were found to influence the morphology of the scaffolds during the biomimetic process obviously. Both the amount and the size of the microspheres on the composite scaffolds increased with increased incubation time. After a certain incubation time, microspheres formed on the composite fibers with less wollastonite had a relatively larger size. Therefore, the microstructure of the composite scaffolds could be adjusted by controlling the wollastonite content and the incubation time. All of these results suggest that it is an effective approach to fabricate PBSU/wollastonite/apatite fibrous composite scaffolds with different material content and controllable microstructure for bone tissue engineering.