Adhesion of fluid infused silicone elastomer to glass

Elastomers swollen with non-polar fluids show potential as anti-adhesive materials. We study the effect of oil fraction and contact time on the adhesion between swollen spherical probes of PDMS (polydimethylsiloxane) and flat glass surfaces. The PDMS probes are swollen with pre-determined amount of 10 cSt silicone oil to span the range where the PDMS is fluid free (via solvent extraction) up to the limit where it is oil saturated. Probe tack measurements show that adhesion decreases rapidly with an increase in oil fraction. The decrease in adhesion is attributed to excess oil present at the PDMS-air interface. Contact angle measurements and optical microscopy images support this observation. Adhesion also increases with contact time for a given oil fraction. The increase in adhesion with contact time can be interpreted through different competing mechanisms that depend on the oil fraction where the dominant mechanism changes from extracted to fully swollen PDMS. For partially swollen PDMS, we observe that adhesion initially increases because of viscoelastic relaxation and at long times increases because of contact aging. In contrast, adhesion between fully swollen PDMS and glass barely increases over time and is mainly due to capillary forces. While the relaxation of PDMS in contact is well-described by a visco-poroelastic model, we do not see evidence that poroelastic relaxation of the PDMS contributes to an increase of adhesion with glass whether it is partially or fully swollen.

Nanoparticles can modulate network topological defects during multimodal elastomer formation

We experimentally show that nanoparticles (NPs) can significantly regulate the network topological defects during a molecularly controlled elastomeric synthesis. Using positron annihilation lifetime spectroscopy, we demonstrate this on well-defined model systems of poly(dimethyl siloxane) elastomers and layered silicate nanoparticles (NPs). The evolutions of topological defects in elastomeric networks prepared from unimodal, bimodal, and NP dispersed bimodal elastomers are sequentially investigated. The extent of NP induced defect regulation is identified by varying the particle concentration from moderately low to an approximate upper limit. The fraction of free volume hole defects present between packed chains in the network generated by molecular control is significantly reduced. The fraction of smaller interstitial cavities near the cross-link sites shows a moderate increase at the lowest NP concentration. However, this fraction decreases at a high NP concentration and is nearly the same as that of bimodal networks that are devoid of NP infusion. Despite the variations in their fractions with NP infusion, the sizes of both these types of defects that remain in the network are minimally affected. The collective topological defects arising from chain induced heterogeneity also show a qualitative reduction upon NP infusion.