Preparation and Neutronic Studies of Tungsten Carbide Composite

Efficient Synthesis of WB5-x-WB2 Powders with Selectivity for WB5-x Content

We proposed an efficient method toward the synthesis of higher tungsten boride WB_5-x in the vacuumless direct current atmospheric arc discharge plasma. The crystal structure of the synthesized samples of boron-rich tungsten boride was determined using computational techniques, showing a two-phase system. The ab initio calculations of the energies of various structures with similar X-ray diffraction (XRD) patterns allowed us to determine the composition of the formed higher tungsten boride. We determined the optimal parameters of synthesis to obtain samples with 61.5% WB_5-x by volume. The transmission electron microscopy measurements showed that 90% of the particles have sizes of up to 100 nm, whereas the rest of them may have sizes from 125 to 225 nm. Our study shows the possibility of using the proposed vacuumless method as an efficient and inexpensive way to synthesize superhard WB_5-x without employing resource-consuming vacuum techniques.

A novel WC–W2C composite synthesis by arc plasma melt cast technique: microstructural and mechanical studies

WC–W2C composites of three different compositions have been synthesized from mixture of WC + W (0, 5 and 16 wt% W) by thermal arc plasma melt-cast technique. Various grown phases observed in the composites consisting of major phases of WC and W2C and minor phases of unbound C (graphite) and tungsten (W) were confirmed by X-ray diffraction, selected area electron diffraction, X-ray photoelectron spectroscopy and Fourier transform infrared studies. Transmission electron microscopy and field emission scanning electron microscopy show polycrystalline nature of composites. Energy dispersive spectroscopy (of X-ray) infers the absence of any impurity in the composite. Almost porous free nature of composites were observed from X-ray micro computed tomography and BET analysis studies. WC–W2C composite (16 wt% W) shows 25% and 21% higher micro hardness (2535 VHN) and Young’s modulus (625 GPa) values than that of pure melt cast WC sample.