Fabrication of a mesoporous silica film based optical waveguide sensor for detection of small molecules

Theoretical optimization of a frequency-domain- based color polarization interference sensor via coupling with a Gaussian beam

In this paper, a Gaussian-beam-coupled color polarization interference (CCPI) sensor with an adjustable digital Gaussian filter was proposed theoretically in the frequency domain. The coupling principle of a traditional color polarization interference (CPI) sensor and a Gaussian beam was investigated, and sensitivity optimization was then implemented. The formation of a doublet is related to the shape of a CPI curve, expected wavelength, and FWHM of the Gaussian beam. Based on the calculated results, the angle between the two polarizers and the obliquity of the wave plate are the two most significant adjusting parameters. The sensitivity of a CCPI sensor is approximately twofold higher than that of a traditional CPI sensor. The sensing range is also related to the FWHM of the Gaussian beam and a larger FWHM usually means a wider sensing range. We also found that the sensitivity would reach a maximum when the incident angle is near the total internal reflection angle. Besides, a longer incident wavelength usually corresponds to a higher sensitivity and the sensitivity could reach as high as 9270 nm/refractive index unit when the resonance wavelength is 977.40 nm.

Stability of mesoporous silica using ricinoleic methyl ester as a template with the addition of HCl and application of Cd2+ adsorption optimized by Box-Behnken design

Mesoporous silica is restricted to organic solvents or other acidic media. The application of mesoporous silica depends on the medium's chemical stability and mechanical properties. It is necessary to stabilize the mesoporous silica material under acidic conditions. The results of the nitrogen adsorption characterization show that MS-50 has a large surface area and porosity, resulting in good mesoporous silica. Using variance analysis (ANOVA) to compare the collected data, the best conditions were found at a pH of 6.32, a Cd²⁺ concentration of 25.30 ppm, an adsorbent dose of 0.06 g, and a time of 70.44 min. The Cd²⁺ adsorption experiment data best fit the Langmuir isotherm model with the maximum amount of Cd²⁺ that MS-50 could absorb being 103.10 mg g^-1.

SBA-15 with Crystalline Walls Produced via Thermal Treatment with the Alkali and Alkali Earth Metal Ions

Crystalline walled SBA-15 with large pore size were prepared using alkali and alkali earth metal ions (Na⁺, Li⁺, K⁺ and Ca²⁺). For this work, the ratios of alkali metal ions (Si/metal ion) ranged from 2.1 to 80, while the temperatures tested ranged from 500 to 700 °C. The SBA-15 prepared with Si/Na⁺ ratios ranging from 2.1 to 40 at 700 °C exhibited both cristobalite and quartz SiO₂ structures in pore walls. When the Na⁺ amount increased (i.e., Si/Na increased from 80 to 40), the pore size was increased remarkably but the surface area and pore volume of the metal ion-based SBA-15 were decreased. When the SBA-15 prepared with Li⁺, K⁺ and Ca²⁺ ions (Si/metal ion = 40) was thermally treated at 700 °C, the crystalline SiO₂ of quartz structure with large pore diameter (i.e., 802.5 Å) was observed for Ca⁺² ion-based SBA-15, while no crystalline SiO₂ structures were observed in pore walls for both the K⁺ and Li⁺ ions treated SBA-15. The crystalline SiO₂ structures may be formed by the rearrangement of silica matrix when alkali or alkali earth metal ions are inserted into silica matrix at elevated temperature.