Photo-polymerization differences by using nanosecond and picosecond laser pulses

Thermal control of SZ2080 photopolymerization in four-beam interference lithography

Photopolymerization by four-beam interference lithography on a preheated SZ2080 sample was explored at different initial temperatures of the sample: 20 °C, 50 °C, 75 °C, 100 °C, 125 °C, and 150 °C, and at exposure times ranging from 0.5 s to 5 s. The average laser power selected was ∼100 mW for the 300 ps duration pulses at a 1 kHz repetition rate. The experimental results demonstrate that the higher initial temperature of the sample positively influences the crosslinking of the patterns. These findings will improve polymerization protocols for multi-beam interference lithography.

Polymers for Regenerative Medicine Structures Made via Multiphoton 3D Lithography

Multiphoton 3D lithography is becoming a tool of choice in a wide variety of fields. Regenerative medicine is one of them. Its true 3D structuring capabilities beyond diffraction can be exploited to produce structures with diverse functionality. Furthermore, these objects can be produced from unique materials allowing expanded performance. Here, we review current trends in this research area. We pay particular attention to the interplay between the technology and materials used. Thus, we extensively discuss undergoing light-matter interactions and peculiarities of setups needed to induce it. Then, we continue with the most popular resins, photoinitiators, and general material functionalization, with emphasis on their potential usage in regenerative medicine. Furthermore, we provide extensive discussion of current advances in the field as well as prospects showing how the correct choice of the polymer can play a vital role in the structure’s functionality. Overall, this review highlights the interplay between the structure’s architecture and material choice when trying to achieve the maximum result in the field of regenerative medicine.

Fabrication of high-aspect-ratio structures using Bessel-beam-activated photopolymerization

Microfabrication based on photopolymerization is typically achieved by scanning a focal spot within the material point by point, which significantly limits fabrication speed. In this paper, we explore a method for rapid fabrication of high-aspect-ratio microstructures based on photopolymerization using a femtosecond laser beam that is converted into a Bessel beam by an axicon. With stationary exposure, a polymer fiber measured at 200 μm in length and 400 nm in width (500∶1 aspect ratio) was fabricated within 50 ms of exposure time. The exposure conditions can be adjusted to produce fibers with variable widths. A phenomenological polymerization-threshold model is adapted for Bessel-beam exposure. The revised model is applied to analyze the structure width and estimate the order of multi-photon absorption. Examination of the cross section of the fibers shows that they are nearly monolithic, suggesting that active species diffuse during photopolymerization. By scanning the Bessel beam in the plane transverse to the direction of beam propagation, mesh structures are fabricated with a single-pass scan, showing the potential of this method for rapid fabrication of large-scale high-aspect-ratio microstructures for applications in photonics, micro-machines, and tissue engineering.