Shape-dependent infrared reflectance properties of CNT forest metamaterial arrays

Solvothermal synthesis of hair-like carbon nanotubes onto sub-micron-sized spherical metal oxide catalyst cores

Long- and uniform-length, and high-density hair-like carbon nanotubes (CNTs) were produced by CNT growth on sub-micron-sized spherical catalyst supports. The nanosized catalysts (FeO _x , CoO _x , and NiO _x ) that were supported in/on the sub-micron-sized spherical metal oxides (TiO₂, ZrO₂, SnO₂, and CeO₂) were prepared via one-step solvothermal and/or two-step impregnation methods. The nanosized catalysts supported in/on the spherical metal oxide supports were converted into CNT conjugates with the CNT-hair morphology via a chemical thermal vapor deposition technique using ethyne gas as a carbon source; the CNTs grew on the central spherical metal oxide core under the base growth process conditions. Among the many types of candidate spherical catalyst materials, the combination of FeO _x as a catalyst for CNT growth and ZrO₂ as a support led to the best growth of CNT-hair under the reaction conditions, which included a temperature of 730 °C, pressure of 65 Pa, a 10 sccm ethyne gas flow, and a reaction time of 10 s. The CNTs consisted of five-to-eight-layered multi-wall structures with lengths of approximately 3 μm. The CNT-hair that was obtained using the solvothermally embedded catalyst showed higher crystallinity and was dense, thick, and straight, while the corresponding CNT-hair obtained using the impregnated catalyst was slightly sparse, thin, and curly. A unique layer structure constructed using large quantities of uniform CNT-hair, including multiple CNT yarns similar to fuzzy balls or cotton candies, was assembled. The CNT-hair conjugate, specifically constructed in a layer structure with core FeO _x /ZrO₂ catalysts and tangled CNT yarns, had an appearance similar to frog eggs. Therefore, we successfully prepared suitable catalysts for CNT-hair production and fabricated a layer structure consisting of large numbers of CNT-hair conjugates. The unique structures are expected as a new metamaterial with intriguing physical properties, including isotropic absorption of polarized light and electromagnetic waves.

Fabrication of Self-Assembling Carbon Nanotube Forest Fishnet Metamaterials

The investigation of the preparation of polystyrene (PS) nanosphere monolayers for the fabrication of carbon nanotube (CNT) forest fishnet metamaterial structures is studied in this paper, as a cheap alternative for top-down patterning methods. The precise control of dry etching conditions resulted in a highly controlled diameter of PS nanobeads, which were then used as a shadow mask for CNT fishnet preparation. The change of the size of the holes from 370 nm to 665 nm resulted in a gradual change of the CNT morphology from multi-walled to single-walled CNTs. The ultraviolet-visible (UV-Vis) reflectance spectra showed that the variation of the hole diameter resulted in the nonlinear light absorption in CNT fishnets that caused the change of the resonance frequency. The change of the fishnet wire width (inductance) and the hole size (capacitance) resulted in the blueshift of the broadband resonance frequency peak. The presented work has a significant potential to allow for the large-scale fabrication of CNT-based fishnet metamaterial structures for applications in energy harvesting, energy storage, solar cells, or optoelectronic devices, such as neuromorphic networks.

A Study of Terahertz-Wave Cylindrical Super-Oscillatory Lens for Industrial Applications

This paper describes the design and development of a cylindrical super-oscillatory lens (CSOL) for applications in the sub-terahertz frequency range, which are especially ideal for industrial inspection of films using terahertz (THz) and millimeter waves. Product inspections require high resolution (same as inspection with visible light), long working distance, and long depth of focus (DOF). However, these are difficult to achieve using conventional THz components due to diffraction limits. Here, we present a numerical approach in designing a 100 mm × 100 mm CSOL with optimum properties and performance for 0.1 THz (wavelength λ = 3 mm). Simulations show that, at a focal length of 70 mm (23.3λ), the focused beam by the optimized CSOL is a thin line with a width of 2.5 mm (0.84λ), which is 0.79 times the diffraction limit. The DOF of 10 mm (3.3λ) is longer than that of conventional lenses. The results also indicate that the generation of thin line-shaped focal beam is dominantly influenced by the outer part of the lens.

Subdiffraction focusing with a long focal length using a terahertz-wave super-oscillatory lens

This Letter describes a super-oscillatory lens (SOL), with concentric ring-type metallic slits photolithographically fabricated on a glass substrate, that can function at subterahertz frequencies. The SOL has been investigated both experimentally and theoretically and demonstrates a spatial resolution of 1.5 mm (0.5λ), which is 0.45 times the diffraction limit, with a focal length of 75 mm (25λ) at 100 GHz (λ=3mm). Furthermore, the depth of focus of the lens was measured to be 47 mm, which is 10.8 times larger than that of a conventional lens. This type of SOL, with subdiffraction focusing, is thus highly effective for use in industrial inspections with millimeter and terahertz waves.

Facile fabrication of urchin-like carbon nanotube-modified Cu0.48Ni0.16Co2.36O4/CuO with high optical-infrared-microwave attenuation

Developing high-performance absorbers with a broad absorption band is a considerable challenge. Herein, carbon nanotube-modified Cu_0.48Ni_0.16Co_2.36O₄/CuO (C-CuNiCoO) composites were prepared using the one-pot hydrothermal method. The composites show good light scattering ability and longer light path due to their urchin-like structures, and lead to perfect absorption above 90% in optical ranges. Moreover, in the infrared ranges, the composites exhibited a high average mass extinction coefficient of 2.52 m^2.g^-1. The unique carbon modification favored the balance between impedance and strong loss capacity. Consequently, C-CuNiCoO achieved excellent absorption performance with a reflection loss up to -40.5 dB at 17.1 GHz. This study opens a new pathway for designing and synthesizing wideband absorption materials.

Mid-infrared, long-wave infrared, and terahertz photonics: introduction

This feature issue presents recent progress in long-wavelength photonics, focusing on wavelengths that span the mid-infrared (3-50 µm), the long-wavelength infrared (30-60 µm), and the terahertz (60-300 µm) portions of the electromagnetic spectrum. The papers in this feature issue report recent progress in the generation, manipulation, detection, and use of light across this long-wave region of the "photonics spectrum," including novel sources and cutting edge advances in detectors, long-wavelength non-linear processes, optical metamaterials and metasurfaces, and molecular spectroscopy. The range of topics covered in this feature issue provide an excellent insight into the expanding interest in long-wavelength photonics, which could open new possibilities for basic research and applications in industries that span health, environmental, and security.