Fluorine-doped SiO2 glasses for F2 excimer laser optics: fluorine content and color-center formation

Paramagnetic Point Defect in Fluorine-Doped Silica Glass: The E^{'}(F) Center

Fluorine-doped silica is a key material used in all low-loss and/or radiation-resistant optical fibers. Surprisingly, no fluorine-related radiation-induced point defects have been identified. By using electron paramagnetic resonance, we report the first observation of F-related defects in silica. Their fingerprint is a doublet with 10.5 mT splitting due to hyperfine coupling (hfc) to ^{19}F nuclear spins. An additional 44.4 mT hfc to the ^{29}Si nucleus indicates that this defect belongs to the "E^{'} center" family and has a structure of a fluorine-modified Si dangling bond: 3-coordinated Si atoms with an unpaired electron in an sp^{3} orbital, bonded to a glass network by 2 bridging oxygen atoms and to a F atom.

Improved radiation resistance of an Er-doped silica fiber by a preform pretreatment method

We report a novel pretreatment method to improve the radiation resistance of Er-doped fiber (EDF). The processing object of this method is EDF preform, and the pretreatment processing involves three steps: deuterium loading, pre-irradiation, and thermal annealing. The effects of pretreatment conditions on the optical loss, gain performance, and radiation resistance of EDF were systematically studied. The relevant mechanisms were revealed using Fourier transform infrared (FTIR), radiation-induced absorption (RIA), and electron paramagnetic resonance (EPR) spectroscopies. The results show that the pretreatment can not only greatly reduce the hydroxyl content of the EDF core, but it can also effectively improve the radiation resistance of EDF. The online test results show that the gain of the commercial, pristine, and pretreated EDFs were reduced by 19.0, 4.2, and 1.3 dB, respectively, corresponding to a decrease of 68.1, 16.2, and 4.7% after 98 krad X-rays irradiation. The high vacuum experiments show that the pretreatment method can maintain long-term stable high radiation resistance. This work provides a reference for the development of high-performance radiation resistant EDFs for use in the lower, middle, and geosynchronous earth orbit.

1064 nm laser-induced defects in pure SiO₂ fibers

We investigate evidence of the formation of nonbridging oxygen hole centers in pure silica photonic crystal fibers from 5 ps 1064 nm pulses. The formation of the defects is attributed to the breaking of stressed silicon-oxygen bonds in the glass matrix through a many-photon process. We compare the photodarkening induced by the 1064 nm pump with photodarkening induced by short wavelength light in a 1064 nm pumped supercontinuum extending to 400 nm. It is shown that the higher peak power at the pump wavelength makes it a more significant cause of photodarkening when compared to the shorter wavelength light generated in the fiber.

Physical disorder and optical properties in the vacuum ultraviolet region of amorphous SiO(2)

The optical absorption of point-defect-free SiO(2) glass in the vacuum ultraviolet region is primarily controlled by the concentrations of three- and four-membered ring structures composed of heavily strained Si-O-Si bonds. The main channel of color center formation by F(2) excimer laser (7.9 eV) irradiation is not Frenkel-defect generation of oxygen via two-photon absorption processes but a pair generation of E' and nonbridging oxygen hole centers by the one-photon excitation of these strained bonds with 7.9 eV photons.

Fabrication of strong long-period gratings in hydrogen-free fibers with 157-nm F2-laser radiation

Long-period gratings were fabricated in standard telecommunication fiber (Corning SMF-28) by use of what is believed to be record short-wavelength light from a 157-nm F(2) laser. Strong loss peaks were formed without the need for enhancement techniques such as hydrogen loading. The magnitude of the attenuation peak was sensitive to the single-pulse laser fluence, decreasing with increasing pulse fluence as a result of nonuniform 157-nm laser interaction with both the fiber cladding and core. The long-period fiber gratings have good wavelength stability (Dlambda~7 nm) under thermal annealing at 150 degrees C.