Evaluation of tissue-engineered bone constructs using rabbit fetal osteoblasts on acellular bovine cancellous bone matrix

Different grinding speeds affect induced regeneration capacity of human treated dentin matrix

Human-treated dentin matrix (hTDM) is a biomaterial scaffold, which can induce implant cells to differentiate into odontoblasts and then form neo-dentin. However, hTDM with long storage or prepared by high-speed handpiece would not to form neo-dentin. In this research, we developed two fresh hTDM with different grinding speeds, which were low-speed hTDM (LTDM) with maximum speed of 500 rpm and high-speed hTDM (HTDM) with a speed of 3,80,000 rpm. Here, we aim to understand whether there were induced regeneration capacity differences between LTDM and HTDM. Scanning electron microscope showed that DFCs grew well on both materials, but the morphology of DFCs and the extracellular matrix was different. Especially, the secreted extracellular matrixes on the inner surface of LTDM were regular morphology and ordered arrangement around the dentin tubules. The transcription-quantitative polymerase chain reaction (qRT-PCR), western blot and immunofluorescence assay showed that the dentin markers DSPP and DMP-1 were about 2× greater in DFCs induced by LTDM than by HTDM, and osteogenic marker BSP was about 2× greater in DFCs induced by HTDM than by LTDM. Histological examinations of the harvested grafts observed the formation of neo-tissue were different, and there were neo-dentin formed on the inner surface of LTDM and neo-cementum formed on the outer surface of HTDM. In summary, it found that the induction abilities of LTDM and HTDM are different, and the dentin matrix is directional. This study lays a necessary foundation for searching the key factors of dentin regeneration in future.

Skeletal microenvironment system utilising bovine bone scaffold co-cultured with human osteoblasts and osteoclast-like cells

A three-dimensional ex vivo bone cell culture system mimicking the skeletal system is useful for bone tissue engineering and as drug discovery platforms. The present study aimed to establish a three-dimensional skeletal culture system using native bovine bone scaffolds and human bone cells. Bovine bone scaffolds were cultured with human foetal osteoblasts 1.19 and human peripheral blood mononuclear cells for 21 days under standard culture conditions. The following groups were established: Decalcified unseeded bone scaffold (DUBS) as baseline control, decalcified seeded bone scaffold (DSBS) to mimic osteoporosis condition and undecalcified seeded bone scaffold to mimic normal condition. The scaffold's porosity and cell attachment on the scaffolds were determined using scanning electron microscopy. Histological evaluation was used to examine changes in trabecular bone structure. Dual-energy X-ray absorptiometry analysis was performed to determine the bone mineral density (BMD) and bone mineral content (BMC) of the scaffolds. A compression test was performed to examine the total biomechanical strength of the scaffolds. The trabecular thickness and number increased, while the trabecular separationwas reduced slightly in DSBS than in DUBS (P>0.05). The BMD and BMC increased significantly (P<0.05), while the compressive strength only increased slightly in DSBS than in DUBS (P>0.05). In conclusion, the ex vivo skeletal microenvironment comprising native bovine bone scaffolds seeded with bone cells is structurally, functionally and mechanically comparable with natural bone. This system may be used as a platform to understand bone physiology and screen for potential drug candidates.

Repair of Bone Defects With Endothelial Progenitor Cells and Bone Marrow-Derived Mesenchymal Stem Cells With Tissue-Engineered Bone in Rabbits

PURPOSE

This study aimed to investigate the repair of bone defects in rabbits with tissue-engineered bones using cocultured endothelial progenitor cells (EPCs) and bone marrow mesenchymal stem cells (BMSCs) as seeding cells.

METHODS

Endothelial progenitor cells and BMSCs were isolated and purified from the peripheral blood and bone marrow, respectively, of New Zealand rabbits. The third passage of BMSCs was cultured alone or with EPCs. Cells were characterized using specific markers and then seeded on partially deproteinized biologic bones from pigs as a scaffold. The engineered bones were used to repair bone defects in rabbits. Hematoxylin and eosin and Masson staining were performed to examine vascularization and osteogenesis in the engineered bone.

RESULTS

The cocultured EPCs and BMSCs grew well on the surface of the scaffold. Compared with monocultured BMSCs, cocultured EPCs and BMSCs promoted the formation of blood vessels and bone on the scaffold, in addition to accelerating the repair of bone defects. The collagen content was significantly increased in the scaffold with cocultured EPCs and BMSCs, compared with the scaffold seeded with mono-cultured BMSCs.

CONCLUSIONS

Tissue-engineered bones seeded with cocultured EPCs and BMSCs may be used effectively for the repair of bone defects.