Improving the Ablation Properties of Liquid Silicone Rubber Composites by Incorporating Hexaphenoxycyclotriphosphonitrile

The ablative properties of epoxy-modified vinyl silicone rubber (EMVSR) composites containing hexaphenoxycyclotriphosphonitrile (HPCTP) have been systematically studied. The strength of the ablation char layer was greatly enhanced with the addition of HPCTP, which induced the formation of a more complete, denser, and thicker char during oxyacetylene ablation tests. Moreover, the HPCTP-containing EMVSR composites demonstrated lower thermal conductivity and pyrolysis rate when compared with those without HPTCP. At the same time, the thermal insulation properties of HPCTP-filled composites were improved under low heat flow ablation scenarios. The reduction of graphitic carbon content, the formation of phosphate-like crystals as well as the increase of SiC content contributed to strengthening the char layer, which was critical for improving the ablation properties. The optimum char layer strength and thermal insulation properties were achieved when the content of HPCTP was 15 phr, whereas an optimum ablation resistance was achieved at 25 phr HPCTP. This suggests that HPCTP-modified EMVSR composites can be used for thermal protection purposes, especially in the fields of aerospace and aeronautics.

Preparation Optimization of CFRP and EPDM Composite by the Co-Curing Method

As the requirements of aerospace technology become more rigorous, the performance of solid rocket motor (SRM) cases needs to be further optimized. In the present study, a co-curing technique was used to fabricate carbon fiber reinforced polymer (CFRP)/ethylene-propylene-diene monomer (EPDM) composites whereby the properties of CFRP/EPDM composites were adjusted by varying the temperature, heating time and type of vulcanizing agent to obtain the optimum manufacturing process. The results of crosslink density (3.459 × 10^-4 mol/cm³) tested by nuclear magnetic resonance (NMR), a 90° peel strength test (2.342 N/mm), and an interlaminar shear test (ILSS = 82.08 MPa) demonstrated that the optimum mechanical properties of composites were obtained under the temperature 160 °C heated for 20 min with the curing agent DCP/S. The interfacial phase and bonding mechanism of composites were investigated by scanning electron microscopy (SEM). Thermogravimetric analysis (TGA) further indicated that EPDM/DCP/S had favorable thermal stability. This will provide valuable recommendations for the optimization of the SRM shell preparation process.

A critical review of fibrous polyurethane-based vascular tissue engineering scaffolds

Certain polymeric materials such as polyurethanes (PUs) are the most prevalent class of used biomaterials in regenerative medicine and have been widely explored as vascular substitutes in several animal models. It is thought that PU-based biomaterials possess suitable hemo-compatibility with comparable performance related to the normal blood vessels. Despite these advantages, the possibility of thrombus formation and restenosis limits their application as artificial functional vessels. In this regard, various surface modification approaches have been developed to enhance both hemo-compatibility and prolong patency. While critically reviewing the recent advances in vascular tissue engineering, mainly PU grafts, this paper summarizes the application of preferred cell sources to vascular regeneration, physicochemical properties, and some possible degradation mechanisms of PU to provide a more extensive perspective for future research.