Crystalline titanium-dioxide nanofinish impregnated on electrospun stereocomplex poly (lactic acid) as non-woven nanotextile with superhydrophilic, anti-shrinkage, dark dyeing and waste dye removal ability for sustainable application

An environmentally friendly non-woven nanotextile has been prepared using enantiomeric pairs of poly (lactic acid) PLA by electrospinning technique. Solution blending of synthesized high molecular weight (⁓10⁵ Da) poly (L-lactic acid) PLLA and poly (D-lactic acid), PDLA for prolonged time stirring produce solely stereocrystallites (sc). The high crosslinking effect of sc-PLA has played an important role, with multifunctional behaviour on the addition of anatase-TiO₂ (a-TiO₂) in three different ways (Case-I-III). The high crystallinity of a-TiO₂ (~7.14 nm), has been confirmed from XRD and TEM studies as 98 %. The nanofinish as studied in (Case -III) by dipping and drying has decreased the water contact angle for the electrospun sc-PLA nanotextile from highly hydrophobic (132°) to superhydrophilicity after 8 min. An easy demonstration of high temperature treated nanofabric (at 100 °C) has proven to obtain an anti-shrinkage sc-PLA nanofabric. Even, the presence of a-TiO₂ has improved the colour strength ability of sc-PLA as a dark dyed nanofabric. The loading of as-synthesized a-TiO₂ nanoparticle has enhanced adsorbent dosages for 5T_dipscPLA up to 1.44 mg/g of MB dosage, at contact time (8 h), and 68 % methylene blue (MB) removal efficiency under UV irradiation. Thereby, this a-TiO₂ impregnated sc-PLA nanofabric tends to dye removal.

Mechanical properties and heat resistance of stereocomplex polylactide/copolyester blend films prepared by in situ melt blending followed with compression molding

This work focuses on the process to obtain high heat-resistant stereocomplex polylactide (scPLA)/copolyester blend films by in situ melt blending of high molecular-weight poly(L-lactide) (PLLA), low molecular-weight poly(D-lactide) (PDLA) and copolyester followed with compression molding. A copolyester of poly(ε-caprolactone-co-L-lactide) was used as a film former. Stereocomplexation, mechanical properties and heat resistance of the scPLA/copolyester blend films were investigated by differential scanning calorimetry (DSC), tensile testing and dynamic mechanical analysis (DMA), respectively. The PDLA fractions enhanced stereocomplexation and heat resistance of the blend films while the copolyester fraction reduced film brittleness. Dimensional stability to heat of blend films was also determined and was accorded to their DMA results. It was concluded that the high heat-resistant and less brittle scPLA films could be prepared using 70/30 (w/w) PLLA/PDLA with 20 wt% copolyester through melt blending before compression molding. This film showed similar stress at break and heat resistance to those of polypropylene film but with lower strain at break.