Photocatalytic Degradation of Organic Dyes Contaminated Aqueous Solution Using Binary CdTiO2 and Ternary NiCdTiO2 Nanocomposites

The synergistic effect of binary CdTiO2 and ternary NiCdTiO2 on the photocatalytic efficiency of TiO2 nanoparticles was investigated. The SEM analysis demonstrates spherical TiO2 NPs of different sizes present in agglomerated form. The structural analysis of the nanocomposites reveals a porous structure for TiO2 with well deposited Cd and Ni NPs. TEM images show NiCdTiO2 nanocomposites as highly crystalline particles having spherical and cubical geometry with an average particle size of 20 nm. The EDX and XRD analysis confirm the purity and anatase phase of TiO2, respectively. Physical features of NiCdTiO2 nanocomposite were determined via BET analysis which shows that the surface area, pore size and pore volume are 61.2 m2/g, 10.6 nm and 0.1 cm3/g, respectively. The absorbance wavelengths of the CdTiO2 and NiCdTiO2 nanocomposites have shown red shift as compared to the neat TiO2 due to coupling with Ni and Cd that results in the enhanced photocatalytic activity. The photocatalytic activity demonstrated that TiO2, CdTiO2 and NiCdTiO2 degrade methylene blue (MB) and methyl green (MG) about 76.59, 82, 86% and 63.5, 88, 97.5%, respectively, at optimum reaction conditions.

Recent Progress in Electrospun Polyacrylonitrile Nanofiber-Based Wound Dressing

Bleeding control plays a very important role in worldwide healthcare, which also promotes research and development of wound dressings. The wound healing process involves four stages of hemostasis, inflammation, proliferation and remodeling, which is a complex process, and wound dressings play a huge role in it. Electrospinning technology is simple to operate. Electrospun nanofibers have a high specific surface area, high porosity, high oxygen permeability, and excellent mechanical properties, which show great utilization value in the manufacture of wound dressings. As one of the most popular reactive and functional synthetic polymers, polyacrylonitrile (PAN) is frequently explored to create nanofibers for a wide variety of applications. In recent years, researchers have invested in the application of PAN nanofibers in wound dressings. Research on spun nanofibers is reviewed, and future development directions and prospects of electrospun PAN nanofibers for wound dressings are proposed.

β-Cyclodextrin/CMK-8-Based Electrochemical Sensor for Sensitive Detection of Cu2+

In this work, β-cyclodextrin (β-CD)/mesoporous carbon (CMK-8) nanocomposite was synthesized and used as an electrochemical sensing platform for highly sensitive and selective detection of Cu2+. The morphology and structure of β-CD/CMK-8 were characterized by scanning electron microscope (SEM) and X-ray diffraction (XRD). In addition, the dates from electrochemical impedance spectroscopy (EIS) and Cyclic voltammetry (CV) demonstrated that the β-CD/CMK-8 possessed a fast electronic transfer rate and large effective surface area. Besides this, the β-CD/CMK-8 composite displayed high enrichment ability toward Cu2+. As a result of these impressive features, the β-CD/CMK-8 modified electrode provided a wide linear response ranging from 0.1 ng·L−1 to 1.0 mg·L−1 with a low detection limit of 0.3 ng·L−1. Furthermore, the repeatability, reproducibility and selectivity of β-CD/CMK-8 towards Cu2+ were commendable. The sensor could be used to detect Cu2+ in real samples. All in all, this work proposes a simple and sensitive method for Cu2+ detection, which provides a reference for the subsequent detection of HMIs.

Effects of chitosan and Tween 80 addition on the properties of nanofiber mat through the electrospinning

Chitosan (CS) with excellent biomedical properties was mixed with polyvinyl alcohol (PVA) to be used as the spinning solution. The spinning solutions with various concentrations of CS:PVA from 10:90% to 50:50% (v/v) were investigated. Tween 80 (T80) was added in the spinning solutions of CS and PVA. The nanofiber mats with and without T80 addition obtained from the spinning solutions by electrospinning technique were investigated and addressed. The results showed that the viscosity of the CS and PVA spinning solutions increased with increasing the CS concentration, whereas the viscosity decreased after T80 addition. The nanofiber mats with 10–30% CS concentrations were prepared successfully as a smooth surface and high dense nanofiber mat. The average diameter of the nanofiber decreased with increasing the CS concentration. The increase in the CS concentration of the nanofiber mat can increase the mechanical and antibacterial properties, whereas the wettability and drug release property were decreased. Moreover, the nanofiber mats with T80 addition had higher mechanical property and wettability than the nanofiber mats without T80 addition. Finally, the T80 addition can enhance hydrophilicity and promote the drug release property of the nanofiber mat.