Exploring the Effect of Specimen Size on Elastic Properties of Fused-Filament-Fabrication-Printed Polycarbonate and Thermoplastic Polyurethane

Additive manufacturing (AM) is often used to create designs inspired by topology optimization and biological structures, yielding unique cross-sectional geometries spanning across scales. However, manufacturing defects intrinsic to AM can affect material properties, limiting the applicability of a uniform material model across diverse cross-sections. To examine this phenomenon, this paper explores the influence of specimen size and layer height on the compressive modulus of polycarbonate (PC) and thermoplastic polyurethane (TPU) specimens fabricated using fused filament fabrication (FFF). Micro-computed tomography imaging and compression testing were conducted on the printed samples. The results indicate that while variations in the modulus were statistically significant due to both layer height and size of the specimen in TPU, variations in PC were only statistically significant due to layer height. The highest elastic modulus was observed at a 0.2 mm layer height for both materials across different sizes. These findings offer valuable insights into design components for FFF, emphasizing the importance of considering mechanical property variations due to feature size, especially in TPU. Furthermore, locations with a higher probability of failure are recommended to be printed closer to the print bed, especially for TPU, because of the lower void volume fraction observed near the heated print bed.

Effects of Fiber Orientation on the Coefficient of Thermal Expansion of Fiber-Filled Polymer Systems in Large Format Polymer Extrusion-Based Additive Manufacturing

Large format polymer extrusion-based additive manufacturing has been studied recently due to its capacity for high throughput, customizable bead size and geometry, and ability to manufacture large parts. Samples from three fiber-filled amorphous thermoplastic materials 3D printed using a Masterprint 3X machine from Ingersoll Machine Tools were studied, along with their neat counterparts. Characterization techniques included thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), and thermo-mechanical analysis (TMA). TGA results showed that the fillers decreased the degradation temperature for most of the materials investigated, with a 30 °C decrease for polycarbonate (PC) and a 12 °C decrease for polyethylene terephthalate glycol (PETG). For all the materials used, heat capacity increases with increasing temperature. Moreover, results show that a highly conductive filler increases the heat capacity. In contrast, a material with a lower conductivity decreases the heat capacity indicated in the 15.2% and 2.54% increase for acrylonitrile butadiene styrene (ABS) and PC and a 27.68% decrease for PETG. The TMA data show that the printed bead exhibits directional properties consistent with an orthotropic material. Smaller strains and coefficient of thermal expansion (CTE) were measured along the bead direction and across the bead compared to the through bead thickness showing that fillers are predominantly oriented in the bead direction, which is consistent with the literature. CTE values through bead thickness and neat material are similar in magnitude, which corresponds to the CTE of the matrix material. The experimental results serve to characterize the effect of fiber filler on the part thermal strains in three principal directions and two-part locations during the extrusion and bead deposition of large-format polymer extrusion-based additive manufacturing technologies.