High-Performance Reversible Furan-Maleimide Resins Based on Furfuryl Glycidyl Ether and Bismaleimides

Two reversible furan-maleimide resins, in which there are rigid -Ph-CH2-Ph- structures and flexible -(CH2)6- structures in bismaleimides, were synthesized from furfuryl glycidyl ethers (FGE), 4,4'-diaminodiphenyl ether (ODA), N,N'-4,4'-diphenylmethane-bismaleimide (DBMI), and N,N'-hexamethylene-bismaleimide (HBMI). The structures of the resins were confirmed using Fourier transform infrared analysis, and the thermoreversibility was evidenced using differential scanning calorimetry (DSC) analysis, as well as the sol-gel transformation process. Mechanical properties and recyclability of the resins were preliminarily evaluated using the flexural test. The results show the Diels-Alder (DA) reaction occurs at about 90 °C and the reversible DA reaction occurs at 130-140 °C for the furan-maleimide resin. Thermally reversible furan-maleimide resins have high mechanical properties. The flexural strength of cured FGE-ODA-HBMI resin arrives at 141 MPa. The resins have a repair efficiency of over 75%. After being hot-pressed three times, two resins display flexural strength higher than 80 MPa.

Towards Thermally Reversible Networks Based on Furan-Functionalization of Jatropha Oil

A novel biobased monomer for the preparation of thermally reversible networks based on the Diels-Alder reaction was synthesized from jatropha oil. The oil was epoxidized and subsequently reacted with furfurylamine to attach furan groups via an epoxide ring opening reaction. However, furfurylamine also reacted with the ester groups of the triglycerides via aminolysis, thus resulting in short-chain molecules that ultimately yielded brittle thermally reversible polymers upon cross-linking via a Diels-Alder reaction. A full-factorial experimental design was used in finding the optimum conditions to minimize ester aminolysis and to maximize the epoxide ring opening reaction as well as the number of furans attached to the modified oil. The optimum conditions were determined experimentally and were found to be 80 °C, 24 h, 1:1 molar ratio, with 50 mol % of LiBr with respect to the modified oil, resulting in 35% of ester conversion, 99% of epoxide conversion, and an average of 1.32 furans/triglyceride. Ultimately, further optimization by a statistical approach led to an average of 2.19 furans per triglyceride, which eventually yielded a flexible network upon cross-linking via a Diels-Alder reaction instead of the brittle one obtained when the furan-functionalization reaction was not optimized.

Thermally Reversible Polymeric Networks from Vegetable Oils

Low cross-link density thermally reversible networks were successfully synthesized from jatropha and sunflower oils. The oils were epoxidized and subsequently reacted with furfurylamine to attach furan groups onto the triglycerides, preferably at the epoxide sites rather than at the ester ones. Under the same reaction conditions, the modified jatropha oil retained the triglyceride structure more efficiently than its sunflower-based counterpart, i.e., the ester aminolysis reaction was less relevant for the jatropha oil. These furan-modified oils were then reacted with mixtures of aliphatic and aromatic bismaleimides, viz. 1,12-bismaleimido dodecane and 1,1'-(methylenedi-4,1-phenylene)bismaleimide, resulting in a series of polymers with T_g ranging between 3.6 and 19.8 °C. Changes in the chemical structure and mechanical properties during recurrent thermal cycles suggested that the Diels-Alder and retro-Diels-Alder reactions occurred. However, the reversibility was reduced over the thermal cycles due to several possible causes. There are indications that the maleimide groups were homopolymerized and the Diels-Alder adducts were aromatized, leading to irreversibly cross-linked polymers. Two of the polymers were successfully applied as adhesives without modifications. This result demonstrates one of the potential applications of these polymers.

Poly(ethylene-co-propylene)/poly(ethylene glycol) elastomeric hydrogels with thermoreversibly cross-linked networks

A series of elastomeric hydrogels with repeated processability were prepared in this work.