Nano/microstructures of shape memory polymers: from materials to applications

Shape memory polymers (SMPs) are macromolecules in which linear chains and crosslinking points play a key role in providing a shape memory effect. As smart polymers, SMPs have the ability to change shape, stiffness, size, and structure when exposed to external stimuli, leading to potential uses for SMPs throughout our daily lives in a diverse range of areas including the aerospace and automotive industries, robotics, biomedical engineering, smart textiles, and tactile devices. SMPs can be fabricated in many forms and sizes from the nanoscale to the macroscale, including nanofibers, nanoparticles, thin films, microfoams, and bulk devices. The introduction of nanostructure into SMPs can result in enhanced mechanical properties, unique structural color, specific surface area, and multiple functions. It is necessary to enhance the current understanding of the various nano/microstructures of SMPs and their fabrication, and to find suitable approaches for constructing SMP-based nano/microstructures for different applications. In this review, we summarize the current state of different SMP nano/microstructures, fabrication techniques, and applications, and give suggestions for their future development.

Synthesis and characterization of polyethylene glycol-phenol-formaldehyde based polyurethane composite

A series of phenol-formaldehyde-polyethylene glycol polyether polyols (PF-PEGs) were synthesized through the condensation polymerization and etherification of phenol, formaldehyde, and poly(ethylene glycol) (PEG) under alkaline conditions and subsequently reacted with 1,6-hexamethylene diisocyanate to obtain polyurethane (PU) films using acetone as solvents. The influence of phenol and formaldehyde to PEG mass ratio ((P + F)/PEG) on the hydroxyl number of PF-PEGs and mechanical properties, thermal stabilities, crystallization behaviors, as well as microstructure of polyurethane composite films were studied using chemical analysis, mechanical tests, thermogravimetric analyses (TGA), dynamic mechanical analyses (DMA), X-ray diffraction (XRD), scanning and transmission electron microscopies (SEM and TEM), respectively. Results demonstrated that PF-PEGs with (P + F)/PEG of 50/50 had the highest hydroxyl number of 323 mg K(OH)/g. The incorporation of phenol and formaldehyde into PEG improved the mechanical properties of polyurethane films, glass transition temperature (T_g), and thermal properties but resulted in the brittleness characteristic of the composite films and low crystallization properties. Moreover, the synthesis mechanism of PF-PEGs polyurethane composite films was revealed, which would provide a theoretical base for the preparation of the rigid polyurethane foams based on phenolic resins.