Interlink between solubility, structure, surface and thermodynamics in the ThO2(s, hyd)–H2O(l) system

The impact of temperature on a freshly precipitated ThO2(am, hyd) solid phase was investigated using a combination of undersaturation solubility experiments and a multi-method approach for the characterization of the solid phase. XRD and EXAFS confirm that ageing of ThO2(am, hyd) at T = 80°C promotes a significant increase of the particle size and crystallinity. TG-DTA and XPS support that the ageing process is accompanied by an important decrease in the number of hydration waters/hydroxide groups in the original amorphous Th(IV) hydrous oxide. However, while clear differences between the structure of freshly precipitated ThO2(am, hyd) and aged samples were observed, the characterization methods used in this work are unable to resolve clear differences between solid phases aged for different time periods or at different pH values. Solubility experiments conducted at T = 22°C with fresh and aged Th(IV) solid phases show a systematic decrease in the solubility of the solid phases aged at T = 80°C. In contrast to the observations gained by solid phase characterization, the ageing time and ageing pH significantly affect the solubility measured at T = 22°C. These observations can be consistently explained considering a solubility control by the outermost surface of the ThO2(s, hyd) solid, which cannot be properly probed by any of the techniques considered in this work. Solubility data are used to derive the thermodynamic properties (log *K°s,0, ΔfG°m) of the investigated solid phases, and discussed in terms of particle size using the Schindler equation. These results provide new insights on the interlink between solubility, structure, surface and thermodynamics in the ThO2(s, hyd)–H2O(l) system, with special emphasis on the transformation of the amorphous hydrous/hydroxide solid phases into the thermodynamically stable crystalline oxides.

SAXS study of the formation and structure of polynuclear thorium(IV) colloids and thorium dioxide nanoparticles

Stable actinide colloids and nanoparticles are of interest because of their potential to affect the transportation of radionuclides in the near-field of a nuclear waste repository. At high concentrations, thorium(IV) can precipitate to form intrinsic colloids. In the present study, polynuclear thorium colloids and thorium dioxide crystallites, formed by the condensation of hydrolyzed Th⁴⁺ solutions (3 mM; initial pH 5.5) aged for up to 18 months, were studied using small-angle X-ray scattering. Scattering profiles were fitted using a unified Guinier/power-law model (Beaucage model) to extract the radii of gyration and Porod exponents. Analysis of the scattering profiles from a dispersion aged for 5 months indicated that both polymer coils and more compacted structures (radius of gyration R_g ≃ 10 nm) were present, which translated in the Kratky plots as a plateau and a peak maximum, respectively. After 18 months, the SAXS data were consistent with the presence of agglomerates of ThO₂ particles suspended in aqueous solution (pH 3.2; [Th] = 1.45 mM). The measured radius of gyration (R_g) of the agglomerates was 5.8 nm, whereas the radius of the ThO₂ particles was 2.5 nm.

The Application of HEXS and HERFD XANES for Accurate Structural Characterisation of Actinide Nanomaterials: The Case of ThO2

The structural characterisation of actinide nanoparticles (NPs) is of primary importance and hard to achieve, especially for non-homogeneous samples with NPs less than 3 nm. By combining high-energy X-ray scattering (HEXS) and high-energy-resolution fluorescence-detected X-ray absorption near-edge structure (HERFD XANES) analysis, we have characterised for the first time both the short- and medium-range order of ThO2 NPs obtained by chemical precipitation. By using this methodology, a novel insight into the structures of NPs at different stages of their formation has been achieved. The pair distribution function revealed a high concentration of ThO2 small units similar to thorium hexamer clusters mixed with 1 nm ThO2 NPs in the initial steps of formation. Drying the precipitates at around 150 °C promoted the recrystallisation of the smallest units into more thermodynamically stable ThO2 NPs. HERFD XANES analysis at the thorium M4 edge, a direct probe for f states, showed variations that we have correlated with the breakdown of the local symmetry around the thorium atoms, which most likely concerns surface atoms. Together, HEXS and HERFD XANES are a powerful methodology for investigating actinide NPs and their formation mechanism.