Intermediate ytterbium valence in YbRhSn 2. ZEITSCHRIFT FUR NATURFORSCHUNG SECTION B-A JOURNAL OF CHEMICAL SCIENCES 2022. [DOI: 10.1515/znb-2022-0099] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 11/15/2022]
Abstract
Abstract
The stannide YbRhSn2 has been synthesized. An arc-melted Rh25Sn48 precursor sample was reacted with ytterbium in a sealed tantalum ampoule in an induction furnace. The structure of YbRhSn2 was refined from single-crystal X-ray diffractometer data: MgCuAl2 type, Cmcm, a = 433.10(3), b = 1076.63(8), c = 739.36(5) pm, wR2 = 0.0676, 444 F
2 values and 16 variables. The rhodium and tin atoms form a three-dimensional [RhSn2]
δ−
polyanionic network with short Rh–Sn (271–273 pm) and Sn–Sn (301–324 pm) distances. The tin substructure is an orthorhombically distorted lonsdaleite network. YbRhSn2 shows paramagnetic behavior with a reduced magnetic moment of 2.2(1) µB per ytterbium atom, classifying it as an intermediate-valent compound.
Collapse
|