Positive Biomechanical Effects of Titanium Oxide for Sandblasting Implant Surface as an Alternative to Aluminium Oxide

Surface-modified titanium and titanium-based alloys for improved osteogenesis: A critical review

As implantable materials, titanium, and its alloys have garnered enormous interest from researchers for dental and orthopedic procedures. Despite their success in wide clinical applications, titanium, and its alloys fail to stimulate osteogenesis, resulting in poor bonding strength with surrounding bone tissue. Optimizing the surface topology and altered compositions of titanium and titanium-based alloys substantially promotes peri-implant bone regeneration. This review summarizes the utilization and importance of various osteogenesis components loaded onto titanium and its alloys. Further, different surface-modification methods and the release efficacy of loaded substances are emphasized. Finally, we summarize the article with prospects. We believe that further investigation studies must focus on identifying novel loading components, exploring various innovative, optimized surface-modification methods, and developing a sustained-release system on implant surfaces to improve peri-implant bone formation.

Surface modification of titanium implants with Mg-containing coatings to promote osseointegration

Titanium (Ti) and Ti alloys are commonly used in dental implants, which have good biocompatibility, mechanical strength, processability, and corrosion resistance. However, the surface inertia of Ti implants leads to delayed integration of Ti and new bone, as well as problems such as aseptic loosening and inadequate osseointegration. Magnesium (Mg) ions can promote bone regeneration, and many studies have used Mg-containing materials to modify the Ti implant surface. This systematic review summarizes the methods, effects, and clinical applications of surface modification of Ti implants with Mg-containing coatings. Database collection was completed on Janury 1, 2023, and a total of 29 relevant studies were ultimately included. Mg can be compounded with different materials and coated to the surface of Ti implants using different methods. In vitro and in vivo experiments have shown that Mg-containing coatings promote cell adhesion and osteogenic differentiation. On the one hand, the surface roughness of implants increases with the addition of Mg-containing coatings, which is thought to have an impact on the osseointegration of the implant. On the other hand, Mg ions promote cell attachment through binding interactions between the integrin family and FAK-related signaling pathways. And Mg ions could induce osseointegration by activating PI3K, Notch, ERK/c-Fos, BMP-4-related signaling pathways and TRPM7 protein channels. Overall, Mg-based coatings show great potential for the surface modification of Ti implants to promote osseointegration. STATEMENT OF SIGNIFICANCE: The inertia surface of titanium (Ti) implants leads to delayed osseointegration. Magnesium (Mg) ions, known for promoting bone regeneration, have been extensively studied to modify the surface of Ti implants. However, no consensus has been reached on the appropriate processing methods, surface roughness and effective concentration of Mg-containing coatings for osseointegration. This systematic review focus on the surface modification of Ti implants with Mg-containing compounds, highlighting the effects of Mg-containing coatings on the surface properties of Ti implants and its associated mechanisms. Besides, we also provide an outlook on future directions to promote the clinical application of Mg-modified implants.

Nanoscale Morphologies on the Surface of 3D-Printed Titanium Implants for Improved Osseointegration: A Systematic Review of the Literature

Three-dimensional (3D) printing is serving as the most promising approach to fabricate personalized titanium (Ti) implants for the precise treatment of complex bone defects. However, the bio-inert nature of Ti material limits its capability for rapid osseointegration and thus influences the implant lifetime in vivo. Despite the macroscale porosity for promoting osseointegration, 3D-printed Ti implant surface morphologies at the nanoscale have gained considerable attention for their potential to improve specific outcomes. To evaluate the influence of nanoscale surface morphologies on osseointegration outcomes of 3D-printed Ti implants and discuss the available strategies, we systematically searched evidence according to the PRISMA on PubMed, Embase, Web of Science, and Cochrane (until June 2022). The inclusion criteria were in vivo (animal) studies reporting the osseointegration outcomes of nanoscale morphologies on the surface of 3D-printed Ti implants. The risk of bias (RoB) was assessed using the Systematic Review Centre for Laboratory Animal Experimentation (SYRCLE's) tool. The quality of the studies was evaluated using the Animal Research: Reporting of In Vivo Experiments (ARRIVE) guidelines. (PROSPERO: CRD42022334222). Out of 119 retrieved articles, 9 studies met the inclusion criteria. The evidence suggests that irregular nano-texture, nanodots and nanotubes with a diameter of 40-105nm on the surface of porous/solid 3D-printed Ti implants result in better osseointegration and vertical bone ingrowth compared to the untreated/polished ones by significantly promoting cell adhesion, matrix mineralization, and osteogenic differentiation through increasing integrin expression. The RoB was low in 41.1% of items, unclear in 53.3%, and high in 5.6%. The quality of the studies achieved a mean score of 17.67. Our study demonstrates that nanostructures with specific controlled properties on the surface of 3D-printed Ti implants improve their osseointegration. However, given the small number of studies, the variability in experimental designs, and lack of reporting across studies, the results should be interpreted with caution.

Immediate placement of extra-short implants in refined scapula tip microvascular free flaps: In house virtual planning and surgical technique - Proof of concept

Scapula tip flaps have been introduced in the literature as an ideal surgical treatment option for large defects in the horizontal plane of the maxilla. This article aims to present a unique step by step protocol for a near total maxillectomy with a pterygoid bone resection and consecutive microvascular reconstruction with a harvested scapula tip flap. The protocol includes immediate placement of extra-short implants in donor bone with the aid of Virtual Surgical Planning (VSP), and an in-house 3D printing of medical 3D models and surgical guides. So far, there has been no presented surgical technique combining immediate implant placement in the scapula region with simultaneous microvascular repair. This technique allows: tumour resection; flap harvesting; extra-short implant placements and reconstruction to be performed in one simultaneous procedure. The technique is presented with illustrations, VSP (presented on videos), radiographs, and surgical findings. We discovered that this refinement of the scapula tip surgery has enabled reconstructive procedures to be performed at the same time as implant placements, providing expedited functional and aesthetic outcomes in selected cases. Moreover, modification of the surgical technique could enhance the competence of the oropharyngeal edge. In conclusion, this new surgical protocol utilizing VSP, 3D models and simultaneous extra-short implant placement provides indispensable advantages for such a complicated surgical procedures, while significantly shortening the duration of surgery.

A new technology for the removal of corundum residues on dental implants

Surface modification is an important measure to improve dental implants. Corundum residues, which are part of current dental implant blasting, on Straumann dental implants, were found to have disappeared in recent publications. We further evaluated this new cleaning technology by evaluating the surface of four different Straumann implants using scanning electron microscopy (SEM) and energy-dispersive radiographic spectroscopy (EDX). The involved technology fits to a Straumann patent involving a dextran coating allowing easy corundum particle removal by aqueous solution.

Preparation of Visible-Light Active Oxygen-Rich TiO2 Coatings Using Low Pressure Cold Spraying

Visible-light active photocatalysts in the form of coatings that can be produced using large-scale methods have attracted considerable attention. Here we show a facile approach to deposit coatings using the low pressure cold spray (LPCS) from oxygen-rich amorphous titanium dioxide, which is a structurally-unconventional feedstock powder for LPCS. We synthesized amorphous TiO2, in which we introduced numerous defects, such as oxide groups (peroxy and superoxy) in volume and hydroxyl groups on the surface. Then we deposited as-prepared powder preserving the presence of active groups, which we demonstrated using Raman spectroscopy. To show the activity of the prepared coatings, we perform methylene blue degradation under visible light. Our research shows that it is worth considering the internal atomic structure and surface chemistry of the powders to be preserved after low pressure cold spraying.

Combining Sandblasting, Alkaline Etching, and Collagen Immobilization to Promote Cell Growth on Biomedical Titanium Implants

Our objective in this study was to promote the growth of bone cells on biomedical titanium (Ti) implant surfaces via surface modification involving sandblasting, alkaline etching, and type I collagen immobilization using the natural cross-linker genipin. The resulting surface was characterized in terms topography, roughness, wettability, and functional groups, respectively using field emission scanning electron microscopy, 3D profilometry, and attenuated total reflection-Fourier transform infrared spectroscopy. We then evaluated the adhesion, proliferation, initial differentiation, and mineralization of human bone marrow mesenchymal stem cells (hMSCs). Results show that sandblasting treatment greatly enhanced surface roughness to promote cell adhesion and proliferation and that the immobilization of type I collagen using genipin enhanced initial cell differentiation as well as mineralization in the extracellular matrix of hMSCs. Interestingly, the nano/submicro-scale pore network and/or hydrophilic features on sandblasted rough Ti surfaces were insufficient to promote cell growth. However, the combination of all proposed surface treatments produced ideal surface characteristics suited to Ti implant applications.

Nanotubular Oxide Layer Formed on Helix Surfaces of Dental Screw Implants

Surface modification is used to extend the life of implants. To increase the corrosion resistance and improve the biocompatibility of metal implant materials, oxidation of the Ti-13Nb-13Zr titanium alloy was used. The samples used for the research had the shape of a helix with a metric thread, with their geometry imitating a dental implant. The oxide layer was produced by a standard electrochemical method in an environment of 1M H3PO4 + 0.3% HF for 20 min, at a constant voltage of 30 V. The oxidized samples were analyzed with a scanning electron microscope. Nanotubular oxide layers with internal diameters of 30–80 nm were found. An analysis of the surface topography was performed using an optical microscope, and the Sa parameter was determined for the top of the helix and for the bottom, where a significant difference in value was observed. The presence of the modification layer, visible at the bottom of the helix, was confirmed by analyzing the sample cross-sections using computed tomography. Corrosion tests performed in the artificial saliva solution demonstrated higher corrosion current and less noble corrosion potential due to incomplete surface coverage and pitting. Necessary improved oxidation parameters will be applied in future work.

Influence of Three Dental Implant Surfaces on Cell Viability and Bone Behavior. An In Vitro and a Histometric Study in a Rabbit Model

The chemical composition and the surface characteristics of dental implants are factors that have a decisive effect on the osseointegration process. The surface characterization at the compositional and topographic level of three dental implants available in the market was performed with different surface treatments: (1) sandblasted and acid etched surface (SLA), (2) hydroxyapatite (HA) and tricalcium phosphate (TCP) blasted surface (HA/TCP), and (3) HA-blasted and non-etching acid washed surface (HA + AW). In addition, an in vitro viability study of MG-63 osteoblast cells was performed with a JC-1 test. To complete the study, an in vivo study was conducted in New Zealand rabbits. The study analyzed the histometric characteristics of the bone formed around the implants at the level of area, volume, bone density, accumulated bone density, and bone–implant contact (BIC). The rabbits were sacrificed at 6 weeks after implants were placed in the tibial metaphysis. No statistically significant differences were observed at the level of cell viability or histometric parameters between the different study groups (p > 0.05). SLA and HA/TCP surfaces were the ones that obtained a higher BIC value. Taking into account the limitations of this study, it can be concluded that the different implant surfaces analyzed favor a good bone response.

Multi-Scale Surface Treatments of Titanium Implants for Rapid Osseointegration: A Review

The propose of this review was to summarize the advances in multi-scale surface technology of titanium implants to accelerate the osseointegration process. The several multi-scaled methods used for improving wettability, roughness, and bioactivity of implant surfaces are reviewed. In addition, macro-scale methods (e.g., 3D printing (3DP) and laser surface texturing (LST)), micro-scale (e.g., grit-blasting, acid-etching, and Sand-blasted, Large-grit, and Acid-etching (SLA)) and nano-scale methods (e.g., plasma-spraying and anodization) are also discussed, and these surfaces are known to have favorable properties in clinical applications. Functionalized coatings with organic and non-organic loadings suggest good prospects for the future of modern biotechnology. Nevertheless, because of high cost and low clinical validation, these partial coatings have not been commercially available so far. A large number of in vitro and in vivo investigations are necessary in order to obtain in-depth exploration about the efficiency of functional implant surfaces. The prospective titanium implants should possess the optimum chemistry, bionic characteristics, and standardized modern topographies to achieve rapid osseointegration.

Nano-scale modification of titanium implant surfaces to enhance osseointegration

The main aim of this review study was to report the state of art on the nano-scale technological advancements of titanium implant surfaces to enhance the osseointegration process. Several methods of surface modification are chronologically described bridging ordinary methods (e.g. grit blasting and etching) and advanced physicochemical approaches such as 3D-laser texturing and biomimetic modification. Functionalization procedures by using proteins, peptides, and bioactive ceramics have provided an enhancement in wettability and bioactivity of implant surfaces. Furthermore, recent findings have revealed a combined beneficial effect of micro- and nano-scale modification and biomimetic functionalization of titanium surfaces. However, some technological developments of implant surfaces are not commercially available yet due to costs and a lack of clinical validation for such recent surfaces. Further in vitro and in vivo studies are required to endorse the use of enhanced biomimetic implant surfaces. STATEMENT OF SIGNIFICANCE: Grit-blasting followed by acid-etching is currently used for titanium implant modifications, although recent technological biomimetic physicochemical methods have revealed enhanced osteoconductive and anti-microbial outcomes. An improvement in wettability and bioactivity of titanium implant surfaces has been accomplished by combining micro and nano-scale modification and functionalization with protein, peptides, and bioactive compounds. Such morphological and chemical modification of the titanium surfaces induce the migration and differentiation of osteogenic cells followed by an enhancement of the mineral matrix formation that accelerate the osseointegration process. Additionally, the incorporation of bioactive molecules into the nanostructured surfaces is a promising strategy to avoid early and late implant failures induced by the biofilm accumulation.

Impact of Different Titanium Implant Thread Designs on Bone Healing: A Biomechanical and Histometric Study with an Animal Model

Threads of dental implants with healing chamber configurations have become a target to improve osseointegration. This biomechanical and histometric study aimed to evaluate the influence of implant healing chamber configurations on the torque removal value (RTv), percentage of bone-to-implant contact (BIC%), bone fraction occupancy inside the thread area (BAFO%), and bone and osteocyte density (Ost) in the rabbit tibia after two months of healing. Titanium implants with three different thread configurations were evaluated: Group 1 (G1), with a conventional “v” thread-shaped implant design; Group 2 (G2), with square threads; and Group 3 (G3), the experimental group with longer threads (healing chamber). Ten rabbits (4.5 ± 0.5 kg) received three implants in each tibia (one per group), distributed in a randomized manner. After a period of two months, the tibia blocks (implants and the surrounding tissue) were removed and processed for ground sectioning to evaluate BIC%, BAFO%, and osteocyte density. The ANOVA one-way statistical test was used followed by the Bonferoni’s multiple comparison test to determine individual difference among groups, considering a statistical difference when p < 0.05. Histometric evaluation showed a higher BAFO% values and Ost density for G3 in comparison with the other two groups (G1 and G2), with p < 0.05. However, the RTv and BIC% parameters were not significantly different between groups (p > 0.05). The histological data suggest that the healing chambers in the implant macrogeometry can improve the bone reaction in comparison with the conventional thread design.

Effect of Different Morphology of Titanium Surface on the Bone Healing in Defects Filled Only with Blood Clot: A New Animal Study Design

Background

The objective of the present histologic animal study was to analyze whether roughness of the titanium surface can influence and/or stimulate the bone growth in defects filled with the blood using a rabbit tibia model.

Materials and Methods

Forty sets (implant and abutment), dental implant (3.5 mm in diameter and 7 mm in length) plus healing abutment (2.5 mm in diameter), were inserted in the tibiae of 10 rabbits. Moreover, twenty titanium discs were prepared. The abutment and discs were treated by 4 different methods and divided into 4 groups: (group A) machined abutments (smooth); (group B) double acid etching treatment; (group C) treatment with blasting with particles of aluminum oxide blasted plus acid conditioning; (group D) treatment with thorough blasting with particles of titanium oxide plus acid conditioning. The discs were used to characterize the surfaces by a profilometer and scanning electronic microscopy.

Results

After 8 weeks, the new bone formation around the sets of the samples was analyzed qualitatively and quantitatively in relation to bone height from the base of the implant and presence of osteocytes. Group C (1.50±0.20 mm) and group D (1.62±0.18 mm) showed bone growth on the abutment with higher values compared to group A (0.94±0.30 mm) and group B (1.19±0.23 mm), with significant difference between the groups (P < 0.05). In addition, osteocyte presence was higher in groups with surface treatment related to machined (P < 0.05).

Conclusions

Within the limitations of the present study, it was possible to observe that there is a direct relationship between the roughness present on the titanium surface and the stimulus for bone formation, since the presence of larger amounts of osteocytes on SLA surfaces evidenced this fact. Furthermore, the increased formation of bone tissue in height demonstrates that there is an important difference between the physical and chemical methods used for surface treatment.

Effects on the osseointegration of titanium implants incorporating calcium-magnesium: a resonance frequency and histomorphometric analysis in rabbit tibia

OBJECTIVE

This study assessed the bone formation around titanium surface incorporating the calcium-magnesium (CaMg) deposited by blasted in rabbit tibia bone to determine whether this surface would further enhance bone healing compared with commercially available implant surface.

MATERIAL AND METHODS

The deposition of CaMg on the titanium SLA surface were obtained by blasting formed the experimental group (EX group), while implants with traditional SLA surface were used as control group (CO group), in this study. Fifty cylindrical threaded implants with a length of 8 mm were used (P = 25 per group). Five implants of each group were used to surface characterization by scanning electron microscopy, energy dispersive spectrometry, and optical profilometry. Ten New Zealand white rabbits received 40 implants (n = 20 per group). Resonance frequency analysis was performed three times (0, 4, and 6 weeks). Histomorphometric analysis was performed 4 and 6 weeks after implantation. Statistical significance was set at P < 0.05.

RESULTS

Blasted CaMg deposition on SLA implant surface displayed almost identical surface morphologies and R(a) values at the micron scale. In comparing the implant stability quotient at the three time points, highly significant statistic differences were found (P < 0.001). Histomorphological analysis showed higher degrees of bone organization in the samples of test implant surfaces at both implantation times.

CONCLUSION

Within the limitations of this study, the results indicate that the deposition of CaMg on the SLA titanium surface may be effective in enhancing the osseointegration of moderately rough grit-blasted implants by increasing the degree of bone-implant contact.