Esthetic Intracanal Posts

The luminous transmittance of the quartz-glass fiber posts is superior to glass fiber posts

Fiber-reinforced prefabricated intraarticular posts have gained popularity due to several favorable characteristics for clinical use compared to metallic intraradicular posts.

AIM

To evaluate the light transmission capacity of two types of fiber posts, using two different methods.

MATERIALS AND METHOD

The posts were divided into two groups: experimental group - quartz-glass fiber posts (n=10) and control group - glass fiber posts (n=10). The light transmittance of the samples was compared by means of light intensity test by photographs and ultraviolet-visible spectrophotometer. This test was analyzed by thirds: coronal, middle, and apical. The spectophotometer tested the luminous transmittance along the length of the post. The statistical analysis was conducted with a significance level of 0.05.

RESULTS

Light transmission was 97% on the coronal third, 68% in the middle third, and 27.66% in the apical third in the posts of the experimental group. In the posts of the control group, the light transmission was 95.33% in the coronal third, 80.66% in the middle third, and 41.33% in the apical third. Light transmission was significantly higher in the middle third of the posts of the experimental group when compared to the control group (p<0.05). The luminous transmittance of the posts of the experimental group was 97.4% with wavelengths of 400 nm, 97% at 450 and 500 nm, and 96.9% at 550 nm. In the posts of the control group, the luminous transmittance was 72.3% with wavelengths of 400 nm, 68.6% at 450 nm; 64.6% at 500 nm and 61.5% at 550 nm. The posts of the experimental group demonstrated significantly higher light transmittance than the control group (p<0.001).

Efficiency of Erbium-Doped Yttrium Aluminum Garnet Laser in Debonding Cemented Glass Fiber Posts: an in vitro Study

Statement of the Problem:

The efficacy of erbium-doped yttrium aluminum garnet (Er; YAG) laser on the debonding properties of certain post materials has remained largely unexplored.

Purpose:

This study aimed to investigate the effect of Er; YAG laser irradiation on debonding of cemented glass fiber posts in root canal treated teeth.

Materials and Method:

In this in vitro study, forty root canal treated mandibular premolar teeth were used in this study. Glass fiber posts were bonded using Panavia F 2.0 cement in the root canal space, and samples were divided into two groups. In the test group, samples were exposed to laser radiation of 7W, 350mJ, frequency of 20Hz and discontinued washing spray. In the control group, samples were left untouched. In each group, samples were sectioned into 1.5mm thick slices from the coronal, middle, and apical thirds of the root (N=120). Tensile bond strengths were evaluated using the push-out test and the failure patterns were evaluated using scanning electron microscopy (SEM). To compare the laser and non-laser groups at each location, independent sample t test was applied, and to compare bond strength between the locations in each group, one-way ANOVA and Tukey’s HSD post hoc was applied.

Results:

A significant difference in tensile strength was observed between the laser-irradiated group and control group; tensile bond strength was much higher in the control group (p<0.001). The highest frequency of fractures was observed at the cement-dentin interface. Given the used parameters, complete debonding was not achieved in the laser-irradiated group.

Conclusion:

Laser radiation reduced the bond strength of glass fiber posts to resin cement without complete debonding.