Effect of irrigation protocols on root canal wall after post preparation: a micro-CT and microhardness study

2D and 3D Erosion Landscape Analysis of Endodontic-Treated Teeth Using EDTA and HEDP as Chelating Agents: A High-Resolution Micro-Computed Tomographic Study

This study aimed to assess the amount of erosion during activated endodontic irrigation with either HEDP or EDTA via high-resolution micro-computed tomography. Two root canals of twenty premolars were prepared with ProTaper Next and irrigated with sodium hypochlorite. Palatal canals, which served as control groups, were sealed, while buccal canals were further irrigated with either EDTA (n = 10) or HEDP (n = 10), which served as test groups. Micro-CT was performed to measure erosion depth. For 2D and 3D measurements, non-parametric repeated ANOVA measurements and post hoc tests were performed. 2D analysis showed highly significant differences between the case groups at each position of the root (p ≤ 0.01). The cervical and apical positions showed significant differences in the EDTA group (p = 0.03). The 3D analysis also showed significant differences between both chelating agents (p < 0.01) and the case and control groups (p = 0.01). The mean erosion depths in the cervical, middle, and apical thirds of the EDTA group were 45.75, 41.79, and 32.25 µm, and for the HEDP group were 20.25, 16.40, and 15.96 µm, respectively. HEDP seems to have a significantly less erosive effect. Different irrigation protocols with harsher conditions, as might be the case during endodontic retreatment, could be assessed with micro-CT.

Survival of severely compromised endodontically treated teeth restored with or without a fiber glass post

OBJECTIVE

The use of a fiber glass post (FGP) type and choice of FGP diameter to restore endodontically treated incisors without ferrule is controversial. This study evaluated survival rate and failure mode of severely compromised central incisors without ferrule rehabilitated using resin-based composite (RBC) with or without FGP with different diameters.

METHODOLOGY

A total of 60 decoronated bovine incisors without a ferrule were endodontically treated and prepared for 1.4, 1.6, and 1.8 mm diameter FGPs (Whitepost System DC 0.5, Fit 0.4, and DCE 0.5; FGM). Half of the teeth received FGPs cemented using dual-cure resin cement (Allcem Core; FGM), the other half were filled using only bulk-fill RBC (OPUS Bulk Fill; FGM). The crowns were directly restored with RBC. The roots were embedded in polystyrene resin and the periodontal ligament was simulated with polyether impression material. Fatigue testing was conducted under 5 Hz cyclic loading at 30 degrees to the incisal edge, beginning at 50 N (5,000 cycles) as a warmup. After, the load was increased 100 N every 15,000 cycles until fracture occurred. All specimens were subjected to transillumination, micro-CT analysis, and digital radiography before and after fatigue testing. Fracture mode was classified according to severity and repair potential. Data were analyzed with Kaplan-Meier survival test and post hoc log-rank test (α=0.05) for pairwise comparisons.

RESULTS

Using FGP significantly increased the number of cycles to failure, irrespective of FGP diameters (p=0.001). The FGP diameters had no statistically significant effect on cycles to failure or failure mode.

CONCLUSION

Using FGP without ferrule improved survival rate of structurally severely compromised central incisors compared with rehabilitation without FGP. The diameter of the FGPs had no effect on the survival rate and failure mode.