Effect of Glass Fiber Post Diameter on Fracture Resistance of Endodontically Treated Teeth

Fracture resistance of endodontically treated teeth, restored with two post-core systems in different post space diameters (in vitro study)

BACKGROUND

Fracture resistance of post-core restoration depends on the design of the post, post diameter, post length, the type of adhesive cement used along with material of the core. Despite the different studies concerning the effect of post space diameter on the fracture resistance of endodontically treated teeth, more information regarding fracture resistance and the effect of different post space systems/materials and diameters is required.

AIM OF THE STUDY

This study aimed to evaluate fracture resistance of endodontically treated teeth, restored with two post-core systems in different post space diameters.

MATERIALS AND METHODS

Twenty freshly extracted maxillary central incisors were collected for this study. They were randomly divided into four groups according to intracanal post and its diameter. Group GN (glass-fiber post of 10-mm length and 1.3-mm diameter with composite core), group GW (glass-fiber post of 10-mm length and 1.75-mm diameter with composite core), group ZN (custom-made zirconia one-piece post-core of 10-mm length and 1.3-mm diameter) and group ZW(custom-made zirconia one-piece post-core of 10-mm length and 1.75-mm diameter). Fracture resistance for all samples was evaluated using the universal testing machine under a static load. The data was collected and statistically analyzed using One-Way ANOVA test. Modes of failure were assessed using stereomicroscope for each group.

RESULTS

The highest mean fracture resistance was recorded in group GW (638.7 ± 285.1 N), followed by group ZW (598.5 ± 127.6 N), then GN group (442.8 ± 65.38 N). The lowest mean fracture resistance was recorded in group ZN (435.3 ± 117.3 N). One-Way ANOVA test revealed that there was no statistically significant difference in fracture resistance values among the groups.

CONCLUSION

Post space diameter had an impact over the fracture resistance of endodontically treated teeth. Modulus of elasticity of post material had a major effect on the fracture resistance and mode of failure along with the restorability of the restored tooth. However, there was no statistically significant difference among the tested groups.

Effect of Root Dentin Pretreatment on Micro-Push-Out Bond Strength of Fiber Posts to Root Canal Dentin: Cold Atmospheric Argon Plasma (CAAP) and Ethylenediaminetetraacetic Acid (EDTA)

Purpose

Debonding from the root canal dentin is the most common failure mode of fiber posts. This study aimed to assess the effects of cold atmospheric argon plasma (CAAP) and ethylenediaminetetraacetic acid (EDTA) on micro-push-out bond strength of fiber posts to root canal dentin.

Materials and Methods

Forty maxillary canine teeth were decoronated, underwent endodontic treatment, and were stored in an incubator for 7 days. After post space preparation, the teeth were randomly divided into four groups for different surface treatments: (I) saline, (II) 17% EDTA, (III) CAAP, and (IV) 17% EDTA + CAAP. Fiber posts (Whitepost no. 2, FGM) were cemented into the root canals using Panavia F2.0 resin cement, and 1 mm-thick sections were made at the coronal, middle, and apical thirds of the roots. The samples underwent micro-push-out bond strength test. The mode of failure was also determined under a stereomicroscope. Data were analyzed using three-way ANOVA and Tukey's post hoc test (α = 0.05). The mode of failure data were analyzed using the chi-square test.

Results

The mean micro-push-out bond strength of fiber posts was not significantly different in the four groups (P > 0.05). However, the bond strength values in the coronal third were significantly higher than the corresponding values in the apical third (P=0.01). There was no significant difference in the modes of failure between the groups (P > 0.05).

Conclusion

Application of CAAP alone or in combination with 17% EDTA could not successfully increase the bond strength of fiber posts to root canal dentin.