Torsional Resistance of Two New Heat Treated Nickel Titanium Rotary Instruments: An in Vitro Evaluation

Angle of Insertion and Torsional Resistance of Nickel-Titanium Rotary Instruments

Previously published studies have investigated the influence of instrument access on cyclic fatigue resistance. However, no studies have evaluated the relationship between angulated access and torsional resistance. The aim of this study was to investigate the influence of the angle of access on the torsional resistance of endodontic instruments. One hundred and eighty instruments were selected: 90 F-One Blue 25/04 and 90 HeroShaper 25/04 instruments. Three subgroups (n = 30) for each instrument type (A and B) were established according to the angle of insertion of the instruments inside the artificial canal (0°, 10° and 20°). The tests were performed using a custom-made device consisting of the following: a motor that can record torque values of 0.1 s; interchangeable stainless-steel canals with different curvature (0°, 10° and 20°) that allow the instrument’s angulated insertion and keep it flexed during testing procedures; and a vise used to secure the instrument at 3 mm from the tip. Torque limit was set to 5.5 Ncm, and each instrument was rotated at 500 rpm until fracture occurred. Torque to fracture (TtF) was registered by the endodontic motor, and the fragment length (FL) was measured with a digital caliper. Fractographic analysis was performed using a scanning electron microscopy (SEM) evaluation to confirm the cause of failure. TtF values and fragment length (FL) values were statistically analyzed using one-way analysis of variance (ANOVA) test and the Bonferroni correction for multiple comparisons across the groups with significance set to a 95% confidence level. Regarding the F-One Blue instruments, the results showed a higher TtF for group A3 (20°) than for group A1 (0°) and group A2 (10°), with a statistically significant difference between group A3 and the other two groups (p < 0.05), whereas no statistically significant difference was found between group A1 and group A2 (p > 0.05). Regarding the HeroShaper instrument, the results showed the highest TtF for group B3, with a statistically significant difference between the three subgroups B1, B2 and B3 (p < 0.05). The results showed that the torsional resistance increases as the angle of instrument access increases with a varying intensity, according to the crystallographic phase of the instrument selected.

Combining apical torsional load and cyclic fatigue resistance of NiTi instruments: New approach to determine the effective lifespan of rotary instruments

In the described proof-of-principle experiments, we introduced a novel testing device to investigate how different concurrent torsional loads influence the cyclic fatigue (CF) resistance of a nickel-titanium (NiTi) instrument. The device was designed to test CF resistance of NiTi files with a standardized load on the apical 5 mm; a movable cylinder controlled by a lever provided a uniform real-time load. Thirty-three NiTi instruments 25.04 (F360, Komet, Lemgo, Germany) were rotated until fracture at 30° curvature under three different torsional loads (n = 11 each); Group A: 2.5 Ncm; Group B: 5 Ncm; Group C: 10 Ncm. anova, multiple comparisons Tamhane tests, regression and Kaplan-Meyer analysis were performed to contrast means. Resistance to cyclic fatigue differed significantly among groups (P = 0.0001). Increased torsional loads led to a decrease in time to failure. An inverse correlation (r = -0.721, P = 0.001) was observed between time and torsional load, with higher torsional loads correlated to shorter times to fracture.

A Digital Microscopic Inspection of Dentinal Defects after Using Endodontic Retreatment Files

Aim

The study aimed at evaluating the incidence of dentinal defects after root canal retreatment with ProTaper Universal retreatment (PTUR) and XP-endo Shaper and Finisher R (XP).

Materials and Methods

Sixty extracted single-rooted human premolars were selected and divided into 4 groups of 15 teeth each. In the negative control group, the teeth were left unprepared. In the positive control group, the teeth were prepared with ProTaper Next and obturated with no further retreatment. In the PTUR and XP groups, the teeth were prepared and obturated followed by removal of the filling material at body temperature using PTUR and XP instruments, respectively. The roots were then sectioned at 3, 6, and 9 mm from the apex and observed under a digital microscope to detect defects.

Results

PTUR group showed significantly higher (p value <0.05) incidence of defects than the other groups. Comparison of no defects versus defects between groups in different areas of root canals demonstrated significant difference among the groups in the apical and cervical regions.

Conclusion

Within the limitations of the present study, PTUR files created significantly more dentinal defects than XP files, with most of those defects at the cervical and apical areas of the root canals.

Impact of Peracetic Acid on the Dynamic Cyclic Fatigue of Heat-Treated Nickel-Titanium Rotary Endodontic Instrument

Peracetic acid (PAA) is widely used as a sterilizing/disinfecting agent, and, in endodontics, it has been introduced as a promising irrigant in root canal treatment. It has been used at different concentrations to achieve various functions. However, endodontic instruments in contact with PAA of a certain concentration may affect their fatigue resistance. Therefore, the aim of this study was to investigate the impact of PAA on the cyclic fatigue resistance of three commercial heat-treated nickel-titanium (NiTi) rotary files. Three types of heat-treated NiTi rotary files were selected: One Curve (OC), ProTaper Gold (PTG), and Wave One Gold (WOG). Each type was divided into three subgroups (n = 6 for each file type): (1) untreated instruments; (2) files immersed in 0.002% PAA; and (3) files immersed in 0.35% PAA. The performance of each file type was tested in a simulated canal. The number of cycles to fracture (NCF) was determined to assess cyclic fatigue resistance of the files. Independent sample t-test was applied to compare each treated file within a subgroup with its respective control group, and one-way ANOVA was used for comparison among the main groups. All types of tested files revealed a significant decline in the cyclic fatigue resistance after exposure to 0.002% PAA except the PTG (P=0.209). After exposure of the files to a higher concentration (0.35% PAA), a dramatic reduction was demonstrated by all the groups. Before and after exposure of the files to PAA, PTG displayed the highest cyclic fatigue resistance, followed by the WOG, while the OC showed the lowest resistance. Exposure of heated-treated NiTi files to PAA in a relatively high or low concentration adversely affects the cyclic fatigue resistance. The PTG files demonstrated the best performance among the tested types and can be disinfected with 0.002% PAA for clinical purpose.

A New Device to Test the Bending Resistance of Mechanical Endodontic Instruments

The aims of the present study were to propose a new machine for testing the bending behavior of an instrument at multiple specific points along the cutting surface and to compare the influence of proprietary heat treatment on the bending ability of EdgeTaper (ET), Protaper Universal (PTU), EdgeTaper Platinum (ETP), and Protaper Gold (PTG). A total of 320 instruments were examined in the present study: 80 ET, 80 PTU, 80 ETP, and 80 PTG. The bending ability of all instruments was tested at a 45° angle and on three different portions of the instrument at 3, 6, and 9 mm from the tip using a customized device. Statistical analysis showed significant differences among each single instrument of the series and between ET and PTU as well as ETP and PTG. The bending behavior of a nickel–titanium rotary instrument is its ability to bend without any plastic deformation. This feature, according to the results of the present study, is variable along the cutting surface; therefore, it should be evaluated. Due to the present testing device, it would be possible to obtain reliable and trustworthy information about an instrument’s bending ability.

Assessment of Real-Time Operative Torque during Nickel–Titanium Instrumentation with Different Lubricants

The aim of the present study is twofold: to assess ex vivo the role of different lubricants on real-time torque generated during intracanal instrumentation and to check whether two different kinds of torque parameters, operative torque (OT) and average peak torque (APT), could produce similar results. Forty extracted single-rooted teeth were selected for the present study and divided into four equal groups (n = 10): Group A, NaCl 0.2%; Group B, NaOCl 5%; Group C, ethylenediaminetetraacetate (EDTA), and Group D, EDTA and hydrogen peroxide. Afterwards, Edge Taper F2 (Edge Endo, Albuquerque, New Mexico) were rotated clockwise at 300 rpm with 3 Ncm maximum torque by an endodontic torque recording motor. In each sample, mean OT and mean APT were recorded and statistically analyzed with one-way ANOVA and a post hoc Bonferroni between groups (p < 0.05). EDTA (12.11 ± 4.45 Ncm) showed statistically significant (p < 0.05) lower values compared with the other tested irrigant for both parameters. Overall, the two different parameters were both able to differentiate between the influence of lubricants on torsional loads.