Effects of silica coating and silane surface conditioning on the bond strength of rebonded metal and ceramic brackets

Residual Adhesive Removal Methods for Rebonding of Debonded Orthodontic Metal Brackets: Systematic Review and Meta-Analysis

Debonding of orthodontic brackets is a common occurrence during orthodontic treatment. Therefore, the best option for treating debonded brackets should be indicated. This study aimed to evaluate the bond strength of rebonded brackets after different residual adhesive removal methods. This systematic review and meta-analysis was conducted according to the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) statement. PubMed, Web of Science, The Cochrane Library, SciELO, Scopus, LILACS, IBECS, and BVS databases were screened up to December 2020. Bond strength comparisons were made considering the method used for removing the residual adhesive on the bracket base. A total of 12 studies were included for the meta-analysis. Four different adhesive removal methods were identified: sandblasting, laser, mechanical grinding, and direct flame. When compared with new orthodontic metallic brackets, bond strength of debonded brackets after air abrasion (p = 0.006), mechanical grinding (p = 0.007), and direct flame (p < 0.001) was significantly lower. The use of an erbium-doped yttrium aluminum garnet (Er:YAG) laser showed similar shear bond strength (SBS) values when compared with those of new orthodontic brackets (p = 0.71). The Er:YAG laser could be considered an optimal method for promoting the bond of debonded orthodontic brackets. Direct flame, mechanical grinding, or sandblasting are also suitable, obtaining clinically acceptable bond strength values.

Debonding force and shear bond strength of an array of CAD/CAM-based customized orthodontic brackets, placed by indirect bonding- An In Vitro study

Based on three-dimensional scanning and computer-aided design and computer-aided manufacturing (CAD/CAM) techniques, customized bracket systems are increasingly used. However, data remain limited regarding customized bracket design, characteristics, and stability. This study was undertaken to evaluate the design, bond strength, and residual adhesives of four different CAD/CAM customized brackets that were attached to human tooth specimens by indirect bonding. Thirty extracted human upper premolars were divided into five groups: Group 1, preadjusted self-ligating labial metal bracket; Group 2, lingual self-ligating metal injection molding customized bracket; Group 3, gold-casted lingual customized bracket; Group 4, labial self-ligating milled customized bracket; Group 5, labial customized resin base bracket. Except in Group 1, premolar specimens were scanned via model scanner, and the images were sent to each manufacturing company to fabricate customized brackets and transfer trays/jigs. Debonding force (DF; N) was measured by Instron universal testing machine and shear bond strength (SBS; MPa) was calculated via dividing DF by bonding area. Adhesive remnants were analyzed via stereo microscopic images. Group 2 (196.90±82.75 N) exhibited significantly higher DF than Group 1 (62.77±12.65 N); other groups exhibited similar DFs, compared with Group 1. No customized bracket groups exhibited significant differences in SBS, relative to Group 1 (6.73±1.36 MPa). However, SBS in Group 5 (11.46±7.22 MPa) was significantly higher than in Group 3 (3.58±2.14 MPa). Group 3 had significantly lower ARI scores than other groups (P<0.05). Customized brackets exhibited large deviations in DF and SBS; all customized bracket systems exhibited DF that was equivalent or superior to that of preadjusted brackets, even when placed by indirect bonding.

The effect of repeated bonding on the shear bond strength of different resin cements to enamel and dentin

PURPOSE

Cementation failures of restorations are frequently observed in clinical practice. The purpose of this study is to compare the effect of initial and repeated bonding on the bond strengths of different resin cements to enamel and dentin.

MATERIALS AND METHODS

Ninety human maxillary central incisors were bisected longitudinally. The 180 tooth halves were divided into 2 groups (n = 90) for enamel and dentin bonding. The enamel and dentin groups were further divided into 3 groups (n = 30) for different resin cement types. Composite resin (Filtek Ultimate) cylinders (3 × 3 mm) were prepared and luted to enamel and dentin using Variolink II (Group V), RelyX ARC (Group R), or Panavia F 2.0 (Group P) resin cement. After 24 hours, initial shear bond strengths of the resin cements to enamel and dentin were measured. Using new cylinders, the specimens were de-bonded and re-bonded twice to measure the first and the second bond strengths to enamel and dentin. Failure modes and bonding interfaces were examined. Data were statistically analyzed.

RESULTS

Initial and repeated bond strengths to enamel were similar for all the groups. The first (15.3 ± 2.2 MPa) and second (10.4 ± 2.2 MPa) bond strengths to dentin were significantly higher in Group V (P<.0001). Second bond strengths of dentin groups were significantly lower than initial and first bond strengths to dentin (P<.0001).

CONCLUSION

All resin cements have similar initial and repeated bond strengths to enamel. Variolink II has the highest first and second bond strength to dentin. Bond strength to dentin decreases after the first re-bonding for all resin cements.

Effect of different surface treatments for ceramic bracket base on bond strength of rebonded brackets

The aim of this study was to evaluate the shear bond strength of rebonded ceramic brackets after subjecting the bracket base to different treatments. Seventy-five premolars were selected and randomly distributed into five groups (n=15), according to the type of the bracket surface treatment: I, no treatment, first bonding (control); II, sandblasting with aluminum oxide; III, sandblasting + silane; IV, silica coating + silane; and V, silicatization performed in a laboratory (Rocatec system). The brackets were fixed on an enamel surface with Transbond XT resin without acid etching. The brackets were then removed and their bases were subjected to different treatments. Thereafter, the brackets were fixed again to the enamel surface and the specimens were subjected to shear bond strength (SBS) test. The adhesive remnant index (ARI) was then evaluated for each specimen. Data were subjected to ANOVA and Tukey's tests (α=0.05). A statistically significant difference was observed only between Rocatec and the other groups; the Rocatec group showed the lowest SBS values. The highest SBS values were observed for group 1, without any significant difference from the values for groups II, III and IV. Most groups had a higher percentage of failures at the enamel-resin interface (score 1). It was concluded that the surface treatments of rebonded ceramic brackets were effective, with SBS values similar to that of the control group, except Rocatec group.

Analysis of Shear Bond Strength and Morphology of Er:YAG Laser-Recycled Ceramic Orthodontic Brackets

Objective. The aim of this study was to compare the recycling of deboned ceramic brackets via an Er:YAG laser or via the traditional chairside processing methods of flaming and sandblasting; shear bond strength and morphological changes were evaluated in recycled brackets versus new brackets. Materials and Methods. 3M Clarity Self-Ligating Ceramic Brackets with a microcrystalline base were divided into groups subjected to flaming, sandblasting, or exposure to an Er:YAG laser. New ceramic brackets served as a control group. Shear bond strengths were determined with an Electroforce test machine and tested for statistical significance through analysis of variance. Morphological examinations of the recycled ceramic bracket bases were conducted with scanning electron microscopy and confocal laser scanning microscopy. Residue on the bracket base was analyzed with Raman spectroscopy. Results. Faded, dark adhesive was left on recycled bracket bases processed via flaming. Adhesive was thoroughly removed by both sandblasting and exposure to an Er:YAG laser. Compared with new brackets, shear bond strength was lower after sandblasting (p < 0.05), but not after exposure to an Er:YAG laser. The Er:YAG laser caused no damage to the bracket. Conclusion. Er:YAG lasers effectively remove adhesive from the bases of ceramic brackets without damaging them; thus, this method may be preferred over other recycling methods.

Heat treatment following surface silanization in rebonded tribochemical silica-coated ceramic brackets: shear bond strength analysis

OBJECTIVE

This study aimed to evaluate the effects of heat treatment on the tribochemical silica coating and silane surface conditioning and the bond strength of rebonded alumina monocrystalline brackets.

MATERIAL AND METHODS

Sixty alumina monocrystalline brackets were randomly divided according to adhesive base surface treatments (n=20): Gc, no treatment (control); Gt, tribochemical silica coating + silane application; Gh, as per Gt + post-heat treatment (air flux at 100ºC for 60 s). Brackets were bonded to the enamel premolars surface with a light-polymerized resin and stored in distilled water at 37ºC for 100 days. Additionally, half the specimens of each group were thermocycled (6,000 cycles between 5-55ºC) (TC). The specimens were submitted to the shear bond strength (SBS) test using a universal testing machine (1 mm/min). Failure mode was assessed using optical and scanning electron microscopy (SEM), together with the surface roughness (Ra) of the resin cement in the bracket using interference microscopy (IM). 2-way ANOVA and the Tukey test were used to compare the data (p>0.05).

RESULTS

The strategies used to treat the bracket surface had an effect on the SBS results (p=0.0), but thermocycling did not (p=0.6974). Considering the SBS results (MPa), Gh-TC and Gc showed the highest values (27.59±6.4 and 27.18±2.9) and Gt-TC showed the lowest (8.45±6.7). For the Ra parameter, ANOVA revealed that the aging method had an effect (p=0.0157) but the surface treatments did not (p=0.458). For the thermocycled and non-thermocycled groups, Ra (µm) was 0.69±0.16 and 1.12±0.52, respectively. The most frequent failure mode exhibited was mixed failure involving the enamel-resin-bracket interfaces.

CONCLUSION

Regardless of the aging method, Gh promoted similar SBS results to Gc, suggesting that rebonded ceramic brackets are a more effective strategy.

Heat treatment following surface silanization in rebonded tribochemical silica-coated ceramic brackets: shear bond strength analysis

OBJECTIVE

This study aimed to evaluate the effects of heat treatment on the tribochemical silica coating and silane surface conditioning and the bond strength of rebonded alumina monocrystalline brackets.

MATERIAL AND METHODS

Sixty alumina monocrystalline brackets were randomly divided according to adhesive base surface treatments (n=20): Gc, no treatment (control); Gt, tribochemical silica coating + silane application; Gh, as per Gt + post-heat treatment (air flux at 100ºC for 60 s). Brackets were bonded to the enamel premolars surface with a light-polymerized resin and stored in distilled water at 37ºC for 100 days. Additionally, half the specimens of each group were thermocycled (6,000 cycles between 5-55ºC) (TC). The specimens were submitted to the shear bond strength (SBS) test using a universal testing machine (1 mm/min). Failure mode was assessed using optical and scanning electron microscopy (SEM), together with the surface roughness (Ra) of the resin cement in the bracket using interference microscopy (IM). 2-way ANOVA and the Tukey test were used to compare the data (p>0.05).

RESULTS

The strategies used to treat the bracket surface had an effect on the SBS results (p=0.0), but thermocycling did not (p=0.6974). Considering the SBS results (MPa), Gh-TC and Gc showed the highest values (27.59±6.4 and 27.18±2.9) and Gt-TC showed the lowest (8.45±6.7). For the Ra parameter, ANOVA revealed that the aging method had an effect (p=0.0157) but the surface treatments did not (p=0.458). For the thermocycled and non-thermocycled groups, Ra (µm) was 0.69±0.16 and 1.12±0.52, respectively. The most frequent failure mode exhibited was mixed failure involving the enamel-resin-bracket interfaces.

CONCLUSION

Regardless of the aging method, Gh promoted similar SBS results to Gc, suggesting that rebonded ceramic brackets are a more effective strategy.

Comparison of shear bond strength of metal brackets bonded to porcelain surface using different surface conditioning methods: an in vitro study

AIM

To evaluate and compare the shear bond strength of metal brackets bonded to ceramic surfaces using different conditioning methods and to assess the site of bond failure after debonding.

MATERIALS AND METHODS

A total of 70 ceramic surfaces were produced with uniform shape, size and composition. The samples were divided into 7 groups (each of 10 samples). Group 1 was the control group (untreated surface); in group 2 the surface were roughened with a diamond bur; in group 3 the surface were etched with hydrofluoric acid; in group 4 the surfaces were sandblasted; in group 5 the surfaces roughened with bur and silane applied; in group 6 the surfaces were etched with hydrofluoric acid and silane applied and in group 7 the surfaces were sandblasted and silane applied. To all the above groups, metal orthodontic brackets were bonded with light cure adhesive. The brackets were later stored in artificial saliva and incubated at 37°C (24 hours). The samples were then subjected to shear bond strength test using an Instron universal testing machine. The debonded porcelain surfaces were then studied under stereomicroscope to assess site of bond failure.

RESULTS

Sandblasting the ceramic surface and silane application showed the highest bond strength. Stereomicroscope examination after debonding showed that the bond failure is at bracket-adhesive interface in four groups namely hydrofluoric acid, sandblasting, hydrofluoric acid with silane and sandblasting with silane.

CONCLUSION

Sandblasting with silane combination produced the highest shear bond strength, so it is a clinically suitable method for bonding orthodontic metal brackets onto ceramic surface.

CLINICAL RELEVANCE

Bonding orthodontic brackets to ceramic crowns of patients has been a tough task. In this study, different conditioning methods were used to treat the ceramic surfaces before bonding. The results showed that sandblasting the ceramic surface prior to application of silane produced the highest shear bond strength which is clinically suitable to reduce bond failures.