Diethylene Glycol-Assisted Organized TiO2 Nanostructures for Photocatalytic Wastewater Treatment Ceramic Membranes

A high-performance photocatalytic ceramic membrane was developed by direct growth of a TiO2 structure on a macroporous alumina support using a hydrothermal method. The morphological nanostructure of TiO2 on the support was successfully controlled via the interaction between the TiO2 precursor and a capping agent, diethylene glycol (DEG). The growth of anatase TiO2 nanorods was observed both on the membrane surface and pore walls. The well-organized nanorods TiO2 reduced the perturbation of the alumina support, thus controlling the hydrolysis rate of the TiO2 precursor and reducing membrane fouling. However, a decrease in the amount of the DEG capping agent significantly reduced membrane permeability, owing to the formation of nonporous clusters of TiO2 on the support. Distribution of the organized TiO2 nanorods on the support was very effective for the improvement of the organic removal efficiency and antifouling under ultraviolet illumination. The TiO2 nanostructure associated with the reactive crystalline phase, rather than the amount of layered TiO2 formed on the support, which was found to be the key to controlling photocatalytic membrane reactivity. These experimental findings would provide a new approach for the development of efficacious photocatalytic membranes with improved performance for wastewater treatment.

Recent advances in the synthesis and application of photocatalytic metal–metal oxide core–shell nanoparticles for environmental remediation and their recycling process

Metal–metal oxide core–shell nanoparticles have received enormous research attention owing to their fascinating physicochemical properties and extensive applications. In this review we have discussed the challenges and recent advances in their synthesis and application.

Superhydrophobic polymethylsilsesquioxane pinned one dimensional ZnO nanostructures for water remediation through photo-catalysis

In this work we have developed ultra-dense high aspect ratio ZnO nano-forest like structures and explored their potential as photo-catalysts.