Polymer Film Blend of Polyvinyl Alcohol, Trichloroethylene and Cresol Red for Gamma Radiation Dosimetry

This study investigated the polymer film composite of polyvinyl alcohol (PVA), trichlorethylene (TCE) and cresol red (CR) dye irradiated with gamma (γ) rays for potential application as radiation dosimetry. The film was prepared via the solvent-casting method with varying concentrations of TCE. Film samples were exposed to radiation from a γ-rays radiation source of ⁶⁰Cobalt isotope. Color changes before and after γ-rays irradiation were observed, and the optical properties of the polymer films were investigated by spectrophotometry. Results show that increasing the radiation dose physically changed the color of the polymer film, from purple (pH > 8.8) without radiation (0 kGy) to yellow (almost transparent) (2.8 < pH < 7.2) at the highest dose (12 kGy). The concentration of acid formed due to irradiation increased with the increase in irradiation doses and at higher TCE content. The critical doses of PVA-TCE composites decreased linearly with the increase of TCE composition, facilitating an easy calibration process. The dose response at 438 nm increased exponentially with increasing radiation dose, but showed an opposite trend at the 575 nm band. An increase in the TCA concentration indicated a decrease in the absorption edge and an increase in activation energy, but both decreased for all TCE concentrations at higher doses. The energy gap for the direct and the indirect transitions decreased with increasing TCE concentration and γ-rays radiation dose. The results of this study demonstrated the potential application of PVA-TCE-CR polymer film as γ-rays irradiation dosimetry in a useful dose range of 0-12 kGy.

Novel radiochromic porphyrin-based film dosimeters for γ ray dosimetry: investigation on metal and ligand effects

As the utilizing of porphyrins and metalloporphyrins in high dose dosimetry becomes more prevalent, research on structural effects of these molecules on dosimetric characteristics and physicochemical properties of their film dosimeters becomes more and more essential. The present study emphasizes dosimetry (measuring radiolytic bleaching of two novel film dosimeters with spectrophotometric methods against 60Co γ-rays exposure in dose range of 0–100 kGy) and evaluating substituent effects on the radiation response of the film dosimeters (role of organic groups and changing the metal core of porphyrins). With casting of solutions of polycarbonate (PC) containing 0.5 wt.% 5,10,15,20-Tetrakis(2,4,6-trimethoxyphenyl) porphyrin (TTMPP) and 5,10,15,20-Tetraphenyl-21H,23H-porphine manganese (III) chloride (Mn-TPP), two novel radiochromic films with the thickness of 20 μm were fabricated. The presence of porphyrin fragments has been observed in the UV–Vis spectra after γ radiation. Due to the changes of the metal core and substituents of the dye ring, meaningful shifts of maximum absorbance of Soret bands of porphyrins and different radiation response of film-dosimeters were observed. The results were compared with the other polycarbonate/porphyrin film dosimeters. The results indicate that the radiation-induced decoloration of PC/Porphyrin films can be reliably tuned and used in high dose dosimetry.

Dosimetric characterization of novel polycarbonate/porphyrin film dosimeters for high dose dosimetry: study on complexation effect

Two novel radiochromic films with 20 μm thickness were made from casting of solutions of polycarbonate (PC) containing 0.5 wt.% tetra phenyl porphyrin (TPPH2) and 5,10,15,20-tetraphenyl-21H,23H-porphine iron(III) chloride (Fe-TPP). Dosimetric characterization of the films as routine dosimeters were studied by spectrophotometric method. On subjecting TPPH2/PC and Fe-TPP/PC film dosimeters to gamma radiation, radiolytic bleaching of films was observed. The effects of metal-complexation on the radiation response of the film dosimeters were studied under 60Co γ-rays exposure in dose range of 0–100 kGy. The results were also compared with the PC/TPPF20 (PC/tetrakis (pentafluorophenyl) porphyrin) dosimeter to evaluate the substituent effect (role of fluorine groups). Experimental parameters including humidity, temperature and pre-irradiation (shelf-life) and post-irradiation storage in dark and in indirect sunlight were examined. The maximum absorbance of Soret band of dyes had meaningful shifts and reduction which arose from complexation and substituents. The dyed films characteristics were found to be stable enough in media with high degrees of temperature and humidity. The results indicate that the radiation-induced decoloration of TPPH2/PC and Fe-TPP/PC films can be reliably tuned and used in high dose dosimetry.

Fabrication of a flexible polycarbonate/porphyrin film dosimeter for high dose dosimetry

Dyed polycarbonate (PC) Radiochromic films with 20 μm thickness were prepared by casting of organic solution of PC containing 0.5 wt.% tetrakis (pentafluorophenyl) porphyrin (TPPF20) on a glass petri dish. Characterization of the film as a routine dosimeter was studied. On subjecting PC/TPPF20 film dosimeter to gamma radiation, a gradual decrease in the color of films was observed. The sensitivity of these films and the linearity of dose-response curves were studied under 60Co γ-rays expose in dose range of 0–100 kGy. The results were compared with the commercial and non-commercial dosimeters. Experimental parameters including humidity, temperature and pre-irradiation (shelf-life) and post-irradiation storage in dark and in indirect sunlight were examined. The maximum absorbance of soret band of TPPF20 had a bathochromic shift and appeared at 414 nm which remained intact in the investigated dose range. The dyed films characteristics were found to be stable enough in media with high degrees of temperature and humidity. The results indicate that radiation induced decoloration of PC/TPPF20 films can be reliably used in high dose dosimetry.