In vivo wear of a squeaky alumina-on-alumina hip prosthesis: a case report

Implant factors that might influence components' survival in primary total hip arthroplasty

Primary total hip arthroplasty (THA) is an invaluable surgical procedure that has revolutionised the treatment of various end-stage hip pathologies. Aseptic loosening of either acetabular cup and/or femoral stem as well as components' dislocation are well-known post-operative complications due to so many factors: environmental, surgeon, patient related, disease related or implant design. The aim of this literature review is to look at some relevant implant designs that might influence acetabular and femoral components' survival for primary cementless THA using revision for aseptic loosening and dislocation as criteria for failure. This may also assist the surgeon in making an informed choice of using appropriate implants to match the demographic and disease-specific need of the patients undergoing the surgical procedure. This review article was performed using an online literature search on relevant publications.

Hip Squeaking after Ceramic-on-ceramic Total Hip Arthroplasty

Objective:

The present study aimed to review the characteristics and influencing factors of squeaking after ceramic-on-ceramic (CoC) total hip arthroplasty (THA) and to analyze the possible mechanisms of the audible noise.

Data Sources:

The data analyzed in this review were based on articles from PubMed and Web of Science.

Study Selection:

The articles selected for review were original articles and reviews found based on the following search terms: “total hip arthroplasty”, “ceramic-on-ceramic”, “hip squeaking”, and “hip noise.”

Results:

The mechanism of the squeaking remains unknown. The possible explanations included stripe wear, edge loading, a third body, fracture of the ceramic liner, and resonance of the prosthesis components. Squeaking occurrence is influenced by patient, surgical, and implant factors.

Conclusions:

Most studies indicated that squeaking after CoC THA was the consequence of increasing wear or impingement, caused by prosthesis design, patient characteristics, or surgical factors. However, as conflicts exist among different articles, the major reasons for the squeaking remain to be identified.

Clinical failure analysis of contemporary ceramic-on-ceramic total hip replacements

The present study investigates the performance of ceramic-on-ceramic total hip replacements by combining a retrieval analysis with a survivorship analysis to elucidate mechanisms that led to clinical failure. Semiquantitative surface damage assessment, contact profilometry, contour measurements, and scanning electron microscopy were performed to characterize the types and quantify the extent of surface damage on the retrieved ceramic components. The implantation period was positively correlated with both damage scores of the femoral heads (R = 0.573, p < 0.001) and the acetabular cups (R = 0.592, p < 0.001). Increased maximal out-of-roundness values of the femoral heads correlated with both increased metal transfer damage score (R = 0.384, p = 0.023) and increased stripe damage score (R = 0.729, p ≤ 0.001) of the acetabular liners. The damage rate (damage score/year) for both the retrieved heads and acetabular liners was at least 2.2-fold greater at inclination angles of >45° than the damage rate at inclination angles of ≤45°. For the retrieved femoral heads only, the linear wear rate of 25.5 ± 21.3 µm/year at inclination angles of >45° was 6-fold greater than the linear wear rate of 4.2 ± 2.3 µm/year at inclination angles of ≤45°. Metal transfer on the ceramic bearing surface could possibly contribute to fluid-film starvation and, in combination with an increased inclination angle, may facilitate an adhesive wear mechanism associated with stripe surface damage. At our institution, the clinical survivorship of ceramic-on-ceramic total hip replacements was 98.9% (a total of 9 out of 815 patients were revised within 10 years after total hip arthroplasty) with revision as the end point, suggesting their safe use in younger patients.

Catastrophic failure of ceramic-on-ceramic total hip arthroplasty presenting as squeaking hip

A 68-year-old woman with osteoarthritis had a ceramic-on-ceramic left total hip arthroplasty, including ceramic femoral head and acetabular liner. At 5 years after surgery, the patient developed onset of a very loud squeaking noise, which could be heard 25 m from her, associated with limited hip movement. Findings at revision surgery included a broken ceramic femoral head component, complete wear of the ceramic acetabular component, and black wear debris. Squeaking hip after ceramic-on-ceramic total hip arthroplasty may be associated with catastrophic failure of the arthroplasty components.

Concomitant evolution of wear and squeaking in dual-severity, lubricated wear testing of ceramic-on-ceramic hip prostheses

Ceramic-on-ceramic (CoC) hip bearings were tested in short-term wear tests with a systematically varied contact force. Continuous vibration and intermittent surface roughness measurements were obtained to elucidate potential causes of in vivo hip joint squeaking. The three-phase test comprised alternating cycles of edge loading (EL) and concentric articulation (CA), always using ample serum lubricant. A 50,000-cycle wear trial in which the contact force during CA was distant from the head's wear patch yielded no squeaking and practically no liner roughening. In 10-cycle trials of an edge-worn head coupled with a pristine liner, the contact force was varied in magnitude and point of application; immediate, recurrent squeaking occurred only when the contact force exceeded a critical threshold value and was centered upon the head's wear patch. In a 27,000-cycle wear trial with the contact force applied near the margin of the head's wear patch, recurrent squeaking emerged progressively as the liner's inner surface was roughened via its articulation with the worn portion of the head. The results reveal key conditions that yield recurrent squeaking in vitro in various scenarios without resorting to implausible dry conditions. A fundamental theory explains that hip squeaking is induced by myriad stress waves emanating from asperity collisions; yet, the root cause is edge loading.