Metallosis in Total Hip Arthroplasty

Extreme Serum Titanium Concentration Induced by Acetabular Cup Failure: Unveiling a Unique Scenario of Titanium Alloy Debris Accumulation

The majority of contemporary total hip arthroplasty (THA) implants are constructed from Ti alloys, which are generally believed to generate fewer adverse local tissue reactions (ALTRs) compared to CoCr alloys. This study presents a case of unusual primary THA failure where a substantial release of Ti alloy debris was observed. A 52-year-old active male underwent THA after post-traumatic aseptic necrosis of the femoral head in 2006. Seventeen years after the procedure, the patient presented with groin pain and a restricted range of motion. X-rays revealed the protrusion of the alumina ceramic head through the Ti6Al4V acetabular cup. Trace element analysis indicated significantly elevated levels of serum Ti, Al, and V. CT and MRI confirmed Ti alloy cup failure and a severe ALTR. During revision surgery, it was found that the worn-out ceramic head was in direct contact with the acetabular cup, having protruded through a central hole it had created over time. No acetabular liner was found. Histological analysis of his tissue samples showed wear-induced synovitis with areas of multinucleated foreign body giant cells and the accumulation of numerous metal particles but no acute inflammatory response. Six months after the revision THA, the patient has experienced favourable outcomes. This case provides an instructive illustration for studying the consequences of the substantial release of Ti alloy debris from orthopedic implants.

Influence of Physical Activity and Cup Orientation on Metal Ion Release and Oxidative Stress in Metal-on-Metal and Ceramic-on-Metal Total Hip Arthroplasty

BACKGROUND

Metal-on-metal (M-M) total hip arthroplasty (THA) has shown adverse reactions to metal debris, abnormal soft-tissue reactions, and high blood metal ion levels. This study aims to: (1) assess whether the toxicity of high levels of ions is related to altered oxidative stress and (2) evaluate tribological factors related to increased blood levels of chromium (Cr) and cobalt (Co) ions.

METHODS

A cross-sectional analytical descriptive study was conducted on 75 patients. A total of 25 underwent M-M THA, 25 ceramic-on-metal (C-M) THA, and 25 were on the THA waiting list. Ion metallic levels in blood, oxidative stress, physical activity, and implant position were compared.

RESULTS

In the M-M group, Co and Cr levels were significantly higher than those found in the C-M group and the control group (p < 0.01). We found no differences in terms of oxidative stress between the groups. Also, we did not find a correlation between metal blood levels and oxidative stress indicators, the physical activity of the patients or the position of the implants between groups.

CONCLUSIONS

The use of M-M bearing surfaces in THA raises the levels of metals in the blood without modifying oxidative stress regardless of the physical activity levels of the patients. Therefore, although patients with M-M bearings require close monitoring, it does not seem necessary to recommend the restriction of physical activity in patients with M-M or C-M arthroplasties.