A disposable sensor based on one-pot synthesized tungsten oxide nanostructure-modified screen printed electrodes for selective detection of dopamine and uric acid

Here, screen-printed carbon electrodes (SPCEs) were modified with ultrafine and mainly mono-disperse sea urchin-like tungsten oxide (SUWO3) nanostructures synthesized by a simple one-pot hydrothermal method for non-enzymatic detection of dopamine (DA) and uric acid (UA) in synthetic urine. Sea urchin-like nanostructures were clearly observed in scanning electron microscope images and WO3 composition was confirmed with XRD, Raman, FTIR and UV-Vis spectrophotometer. Modification of SPCEs with SUWO3 nanostructures via the drop-casting method clearly reduced the Rct value of the electrodes, lowered the ∆Ep and enhanced the DA oxidation current due to high electrocatalytic activity. As a result, SUWO3/SPCEs enabled highly sensitive non-enzymatic detection of DA (LOD: 51.4 nM and sensitivity: 127 µA mM-1 cm-2) and UA (LOD: 253 nM and sensitivity: 55.9 µA mM-1 cm-2) at low concentration. Lastly, SUWO3/SPCEs were tested with synthetic urine, in which acceptable recoveries for both molecules (94.02-105.8%) were obtained. Given the high selectivity, the sensor has the potential to be used for highly sensitive simultaneous detection of DA and UA in real biological samples.

Sensitive pH measurement using EGFET pH-microsensor based on ZnO nanowire functionalized carbon-fibers

Herein, we report the fabrication of zinc oxide nanowire (ZnO NW) coated carbon fiber (CF) ultra-microelectrodes (UME). ZnO NWs were grown on commercial multifilament CFs through hydrothermal process in a teflon-lined autoclave at 90 °C for 4 h. X-ray diffraction (XRD), Raman and scanning electron microscopy characterizations showed that crystalline and well oriented NW structures were successfully obtained. The fabrication of the pH sensitive UME was carried out by a novel approach which allowed controlling the protruding length of the modified CF surface. The UME was then integrated with a metal-oxide-semiconductor field effect transistor (MOSFET) for the construction of an EGFET pH-microsensor. The present pH microsensor is expected to be useful for localized pH measurement in small volumes such single cell analysis.

Controlling Surface Oxygen Concentration of a Nanocarbon Film Electrode for Improvement of Target Analytes

A nanocarbon film consisting of nanocrystallites with mixed sp² and sp³ bonds formed by unbalanced magnetron sputtering, was studied with respect to changes in the characteristics caused by the surface oxygen concentration. An electrochemical pretreatment (ECP) was conducted to change the surface oxygen concentration of the nanocarbon film. X-ray photoelectron spectroscopy (XPS) measurements revealed that nanocarbon films with different amounts of surface oxygen could be prepared. In addition, we observed no significant increase of surface roughness (R_a) at the angstrom level after ECP, owing to a stable structure containing 40% of sp³ bonds. The electrode characteristics, including the potential window, and electrochemical properties for some redox species, such as Ru(NH₃)₆^3+/2+, Fe(CN)₆^3-/4- and some biomolecules, were investigated. The anodic potential limit became wider and ΔE_p of Fe(CN)₆^3-/4- became smaller at the treated nanocarbon film electrode than those of the as-deposited nanocarbon film electrode. Based on these results, we realized to measure uridylic acid (UMP) and inosine triphosphate (ITP) with a high oxidation potential by direct oxidation, which was difficult to measure at the as-deposited nanocarbon film electrode.