In vivo and in vitro investigations of a nanostructured coating material - a preclinical study

Bioactivity and Antibacterial Analysis of Plasticized PLA Electrospun Fibers Reinforced with MgO and Mg(OH)2 Nanoparticles

In this work, we focused on the bioactivity and antibacterial behavior of PLA-based electrospun fibers, efibers, reinforced with both MgO and Mg(OH)2 nanoparticles, NPs. The evolution of PLA-based efibers was followed in terms of morphology, FTIR, XRD, and visual appearance. The bioactivity was discussed in terms of hydroxyapatite growth after 28 days, considered as T28, of immersion in simulated body fluid, SBF. In particular, the biomineralization process evidenced after immersion in SBF started at T14 in both systems. The number of precipitated crystals increased by increasing the amount of both NPs. The chemical composition of the precipitated crystals was also characterized in terms of the Ca/P molar ratio after T28 of immersion in SBF, indicating the presence of hydroxyapatite on the surface of both reinforced efibers. Moreover, a reduction in the average diameter of the PLA-based efibers was observed, reaching a maximum reduction of 46 and 60% in the average diameter of neat PLA and PLA:OLA efibers, respectively, after 28 days of immersion in SBF. The antibacterial behavior of the MgO and Mg(OH)2 NPs in the PLA-based electrospun fibers was tested against Escherichia coli, E. coli, as the Gram-negative bacteria, and Staphylococcus aureus, S. aureus, as the Gram-positive bacteria, obtaining the best antibacterial activity against the Gram-negative bacteria E. coli of 21 ± 2% and 34 ± 6% for the highest concentration of MgO and Mg(OH)2 NPs, respectively.

Tri-Component Hydrogel as Template for Nanocrystalline Hydroxyapatite Deposition Using Alternate Soaking Method for Bone Tissue Engineering Applications

Composite hydrogels containing apatite-like particles can act as scaffolds for osteoblast proliferation, with applications in bone tissue engineering. In this respect, porous biocompatible hydrogels were obtained from chitosan, oxidized pullulan, and PVA in different ratios. The stability of the hydrogels was ensured both by covalent bonds between aldehyde groups of oxidized pullulan and free amino groups of chitosan, and by physical bonds formed during freeze-thaw cycles and lyophilization. The deposition of calcium phosphates was performed by alternate soaking of the porous hydrogels into solutions with calcium and phosphate ions, assuring a basic pH required for hydroxyapatite formation. The mineralized hydrogels were characterized using FTIR spectroscopy, scanning electron microscopy, X-ray diffraction, and thermogravimetric analysis, showing that inorganic particles containing between 80 and 92% hydroxyapatite were deposited in a high amount on the pore walls of the polymeric matrix. The composition of the organic matrix influenced the crystallization of calcium phosphates and the mechanical properties of the composite hydrogels. In vitro biological tests showed that mineralized hydrogels support the proliferation of MG-63 osteoblast-like cells to a greater extent compared to pristine hydrogels.

Bone Tissue Engineering (BTE) of the Craniofacial Skeleton, Part I: Evolution and Optimization of 3D-Printed Scaffolds for Repair of Defects

Bone tissue regeneration is a complex process that proceeds along the well-established wound healing pathway of hemostasis, inflammation, proliferation, and remodeling. Recently, tissue engineering efforts have focused on the application of biological and technological principles for the development of soft and hard tissue substitutes. Aim is directed towards boosting pathways of the healing process to restore form and function of tissue deficits. Continued development of synthetic scaffolds, cell therapies, and signaling biomolecules seeks to minimize the need for autografting. Despite being the current gold standard treatment, it is limited by donor sites' size and shape, as well as donor site morbidity. Since the advent of computer-aided design/computer-aided manufacturing (CAD/CAM) and additive manufacturing (AM) techniques (3D printing), bioengineering has expanded markedly while continuing to present innovative approaches to oral and craniofacial skeletal reconstruction. Prime examples include customizable, high-strength, load bearing, bioactive ceramic scaffolds. Porous macro- and micro-architecture along with the surface topography of 3D printed scaffolds favors osteoconduction and vascular in-growth, as well as the incorporation of stem and/or other osteoprogenitor cells and growth factors. This includes platelet concentrates (PCs), bone morphogenetic proteins (BMPs), and some pharmacological agents, such as dipyridamole (DIPY), an adenosine A 2A receptor indirect agonist that enhances osteogenic and osteoinductive capacity, thus improving bone formation. This two-part review commences by presenting current biological and engineering principles of bone regeneration utilized to produce 3D-printed ceramic scaffolds with the goal to create a viable alternative to autografts for craniofacial skeleton reconstruction. Part II comprehensively examines recent preclinical data to elucidate the potential clinical translation of such 3D-printed ceramic scaffolds.

Enhanced Release of Calcium Ions from Hydroxyapatite Nanoparticles with an Increase in Their Specific Surface Area

Synthetic calcium phosphates, e.g., hydroxyapatite (HAP) and tricalcium phosphate (TCP), are the most commonly used bone-graft materials due to their high chemical similarity to the natural hydroxyapatite-the inorganic component of bones. Calcium in the form of a free ion or bound complexes plays a key role in many biological functions, including bone regeneration. This paper explores the possibility of increasing the Ca2+-ion release from HAP nanoparticles (NPs) by reducing their size. Hydroxyapatite nanoparticles were obtained through microwave hydrothermal synthesis. Particles with a specific surface area ranging from 51 m2/g to 240 m2/g and with sizes of 39, 29, 19, 11, 10, and 9 nm were used in the experiment. The structure of the nanomaterial was also studied by means of helium pycnometry, X-ray diffraction (XRD), and transmission-electron microscopy (TEM). The calcium-ion release into phosphate-buffered saline (PBS) was studied. The highest release of Ca2+ ions, i.e., 18 mg/L, was observed in HAP with a specific surface area 240 m2/g and an average nanoparticle size of 9 nm. A significant increase in Ca2+-ion release was also observed with specific surface areas of 183 m2/g and above, and with nanoparticle sizes of 11 nm and below. No substantial size dependence was observed for the larger particle sizes.

Additive Manufacturing of α-Amino Acid Based Poly(ester amide)s for Biomedical Applications

α-Amino acid based polyester amides (PEAs) are promising candidates for additive manufacturing (AM), as they unite the flexibility and degradability of polyesters and good thermomechanical properties of polyamides in one structure. Introducing α-amino acids in the PEA structure brings additional advantages such as (i) good cytocompatibility and biodegradability, (ii) providing strong amide bonds, enhancing the hydrogen-bonding network, (iii) the introduction of pendant reactive functional groups, and (iv) providing good cell-polymer interactions. However, the application of α-amino acid based PEAs for AM via fused deposition modeling (FDM), an important manufacturing technique with unique processing characteristics and requirements, is still lacking. With the aim to exploit the combination of these advantages in the creation, design, and function of additively manufactured scaffolds using FDM, we report the structure-function relationship of a series of α-amino acid based PEAs. The PEAs with three different molecular weights were synthesized via the active solution polycondensation, and their performance for AM applications was studied in comparison with a commercial biomedical grade copolymer of l-lactide and glycolide (PLGA). The PEAs, in addition to good thermal stability, showed semicrystalline behavior with proper mechanical properties, which were different depending on their molecular weight and crystallinity. They showed more ductility due to their lower glass transition temperature (T_g; 18-20 °C) compared with PLGA (57 °C). The rheology studies revealed that the end-capping of PEAs is of high importance for preventing cross-linking and further polymerization during the melt extrusion and for the steadiness and reproducibility of FDM. Furthermore, our data regarding the steady 3D printing performance, good polymer-cell interactions, and low cytotoxicity suggest that α-amino acid based PEAs can be introduced as favorable polymers for future AM applications in tissue engineering. In addition, their ability for formation of bonelike apatite in the simulated body fluid (SBF) indicates their potential for bone tissue engineering applications.

Nano-hydroxyapatite incorporated quince seed mucilage bioscaffolds for osteogenic differentiation of human adipose-derived mesenchymal stem cells

In this study, the therapeutic hydrocolloid quince seed mucilage (QSM) from Cydonia oblonga Miller fruit is enriched with needle-like nano-hydroxyapatite (nHAp) crystals to fabricate a novel biomimetic osteogenic bioscaffold. The molecular weight (M_w) of water-based extracted QSM was measured with GPC (8.67 × 10⁵ g/mol), and the composite blend was prepared at a ratio of 1:1 (w/w) QSM_aq and nHAp. The porous bioscaffolds were manufactured by the freeze-drying method, and evaluated in-depth with advanced analyses. The XRD, ATR-FTIR, SEM-EDX, and elemental mapping analyses revealed a uniform coated semi-crystalline structure with no covalent bindings between QSM and nHAp. Moreover, due to the hydrocolloid backbone, a supreme swelling ratio (w/w, 6523 ± 190%) with suitable pore size (208.12 ± 99.22 μm) for osteogenic development was obtained. Further, the cytocompatible bioscaffolds were evaluated for osteogenic differentiation in vitro using human adipose-derived mesenchymal stem cells (hAMSCs). The immuno/histochemical (I/HC) staining revealed that the cells with the spherical morphology invaded the pores of the prepared bioscaffolds. Also, relatively early up-regulated osteogenic markers were observed by the qRT-PCR analyses. Overall, it is believed that the QSM-nHAp bioscaffolds might be favorable in non-load bearing applications, especially in the cranio-maxillofacial region, due to their regenerative, bendable, and durable features.

Sustainable Surface Modification of Polyetheretherketone (PEEK) Implants by Hydroxyapatite/Silica Coating-An In Vivo Animal Study

Polyetheretherketone (PEEK) has the potential to overcome some of the disadvantages of titanium interbody implants in anterior cervical and discectomy and fusion (ACDF). However, PEEK shows an inferior biological behavior regarding osseointegration and bioactivity. Therefore, the aim of the study was to create a bioactive surface coating on PEEK implants with a unique nanopore structure enabling the generation of a long-lasting interfacial composite layer between coating material and implant. Seventy-two PEEK implants-each thirty-six pure PEEK implants (PI) and thirty-six PEEK implants with a sprayed coating consisting of nanocrystalline hydroxyapatite (ncHA) embedded in a silica matrix and interfacial composite layer (SPI)-were inserted in the femoral condyles of adult rats using a split-side model. After 2, 4 and 8 weeks, the femur bones were harvested. Half of the femur bones were used in histological and histomorphometrical analyses. Additionally, pull-out tests were performed in the second half. Postoperative healing was uneventful for all animals, and no postoperative complications were observed. Considerable crestal and medullary bone remodeling could be found around all implants, with faster bone formation around the SPI and fewer regions with fibrous tissue barriers between implant and bone. Histomorphometrical analyses showed a higher bone to implant contact (BIC) in SPI after 4 and 8 weeks (p < 0.05). Pull-out tests revealed higher pull-out forces in SPI at all time points (p < 0.01). The presented findings demonstrate that a combination of a bioactive coating and the permanent chemical and structural modified interfacial composite layer can improve bone formation at the implant surface by creating a sustainable bone-implant interface. This might be a promising way to overcome the bioinert surface property of PEEK-based implants.

Electrosprayed calcium silicate nanoparticle-coated titanium implant with improved antibacterial activity and osteogenesis

To ensure clinical success, the implant and the surrounding bone tissue must not only be integrated, but also must not be suspected of infection. In this work, an antibacterial and bioactive nanostructured calcium silicate (CaSi) layer on titanium substrate by an electrospray deposition method was prepared, followed by annealing at 700, 750 and 800 °C to improve the bonding strength of the CaSi coating. The phase composition, microstructure and bonding strength of the CaSi coatings were examined. Human mesenchymal stem cells (hMSCs), Gram-negative Escherichia coli (E. coli) and Gram-positive Staphylococcus aureus (S. aureus) species were used to analyze the osteogenic and antibacterial activity of the coatings, respectively. Experimental results showed that the as-prepared CaSi coating was mainly composted of β-dicalcium silicate phase with a particle size of about 300 nm. After annealing, the thickness of the oxidation reaction layer increased obviously from 0.3 μm to 1 μm with increase in temperature, which was confirmed by the cross-sectional morphology and element depth profile. The bonding strength of the coating annealed at 750 °C (19.0 MPa) was significantly higher (p < 0.05) than that of the as-prepared coating (4.4 MPa) and the ISO 13,779 standard (15 MPa). The results of antibacterial efficacy and stem cell osteogenesis consistently elaborated that the 750 °C-annealed coating had higher activity than the as-prepared coating and the Ti control. It is concluded that after annealing at 750 °C, the CaSi nanoparticle-coated Ti implant had good bond strength, osteogenic and antibacterial activity.

Electrochemical Deposition of Nanostructured Hydroxyapatite Coating on Titanium with Enhanced Early Stage Osteogenic Activity and Osseointegration

Purpose

The aim of research is to fabricate nanostructured hydroxyapatite (HA) coatings on the titanium via electrochemical deposition (ED). Additionally, the biological properties of the ED-produced HA (EDHA) coatings with a plate-like nanostructure were evaluated in vitro and in vivo by undertaking comparisons with those prepared by acid/alkali (AA) treatment and by plasma spray-produced HA (PSHA) nanotopography-free coatings.

Materials and Methods

Nanoplate-like HA coatings were prepared through ED, and nanotopography-free PSHA coatings were fabricated. The surface morphology, phase composition, roughness, and wettability of these samples were investigated. Furthermore, the growth, proliferation, and osteogenic differentiation of MC3T3-E1 cells cultured on each sample were evaluated via in vitro experiments. Histological assessment and push-out tests for the bone–implant interface were performed to explore the effect of the EDHA coatings on the interfacial osseointegration in vivo.

Results

XRD analysis showed that the strongest intensity for the EDHA coatings was at the (002) plane rather than at the regular (211) plane. Relatively higher surface roughness and greater wettability were observed for the EDHA coatings. Cellular experiments revealed that the plate-like nanostructured EDHA coatings not only possessed an ability, similar to that of PSHA coatings, to promote the adhesion and proliferation of MC3T3-E1 cells but also demonstrated significantly enhanced early or intermediate markers of osteogenic differentiation. Significant osseointegration enhancement in the early stage of implantation period and great bonding strength were observed at the interface of bone and EDHA samples. In comparison, relatively weak osseointegration and bonding strength of the bone–implant interface were observed for the AA treatment.

Conclusion

The biological performance of the plate-like nanostructured EDHA coating, which was comparable with that of the PSHA, improves early-stage osteogenic differentiation and osseointegration abilities and has great potential for enhancing the initial stability and long-term survival of uncemented or 3D porous titanium implants.

Physical/Chemical Properties and Resorption Behavior of a Newly Developed Ca/P/S-Based Bone Substitute Material

Properly regulating the resorption rate of a resorbable bone implant has long been a great challenge. This study investigates a series of physical/chemical properties, biocompatibility and the behavior of implant resorption and new bone formation of a newly developed Ca/P/S-based bone substitute material (Ezechbone^® Granule CBS-400). Experimental results show that CBS-400 is comprised majorly of HA and CSD, with a Ca/P/S atomic ratio of 54.6/39.2/6.2. After immersion in Hank’s solution for 7 days, the overall morphology, shape and integrity of CBS-400 granules remain similar to that of non-immersed samples without showing apparent collapse or disintegration. With immersion time, the pH value continues to increase to 6.55 after 7 days, and 7.08 after 14 days. Cytotoxicity, intracutaneous reactivity and skin sensitization tests demonstrate the good biocompatibility features of CBS-400. Rabbit implantation/histological observations indicate that the implanted granules are intimately bonded to the surrounding new bone at all times. The implant is not merely a degradable bone substitute, but its resorption and the formation of new cancellous bone proceed at the substantially same pace. After implantation for 12 weeks, about 85% of the implant has been resorbed. The newly-formed cancellous bone ratio quickly increases to >40% at 4 weeks, followed by a bone remodeling process toward normal cancellous bone, wherein the new cancellous bone ratio gradually tapers down to about 30% after 12 weeks.

Collagen membranes of dermal and pericardial origin-In vivo evolvement of vascularization over time

Aim of the study was to compare the evolvement of vascularization over time of collagen membranes (CMs) of dermal and pericardial origin in an in vivo animal study. Twenty-eight mice underwent implantation of three commercially available CM derived from porcine dermis (homogenous structure: CM1 (Control 1) and bilayer structure: CM2 [Control 2]), from porcine pericardium (CM3; Test 1) as well as CM3 sprayed with silica-enhanced nanostructured hydroxyapatite (CM4, Test 2). After 3, 6, 9, and 12 days, intravital fluorescence microscopy was conducted for determination of capillary diameter, density, flow, and length. At Day 12, samples were examined immunohistologically for expression of fibroblast growth factor receptor 4 (FGFR4), CD11b, CD68, αSMA, and CD34. In all CM, intravital fluorescence microscopy over time showed increasing values for all parameters with the highest levels in CM4 and the lowest values in CM1. Significant lower amounts of FGFR4, CD11b, and CD68 were detected in CM4 when compared to CM2 (p < .05). In contrast to CM3, lower values of αSMA and higher numbers of CD34 positive-marked vessels were observed in CM4 (p < .05). In conclusion, dermal bilayer as well as pericardial CM seem to have a higher vascularization rate than dermal homogenous CM. Additional coating of pericardial CM with a silica-enhanced hydroxyapatite increases the speed of vascularization as well as biological remodeling processes.

A comparative in vivo study of strontium-functionalized and SLActive™ implant surfaces in early bone healing

Purpose

Studies have shown that strontium-doped medical applications benefit bone metabolism leading to improved bone healing and osseointegration. Based on this knowledge, the aim of the study was to evaluate the performance of an implant surface, functionalized by a physical vapor deposition (PVD) coating (Ti-Sr-O), designed to yield predictable release of strontium. The Ti-Sr-O functionalized surface is compared to a routinely used, commercially available surface (SLActive™) with respect to bone-to-implant contact (BIC%) and new bone formation (BF%) in two defined regions of interest (ROI-I and ROI-II, respectively).

Materials and methods:

Ti-Sr-O functionalized, SLActive, and Grade 4 titanium implants were inserted in the femoral condyle of adult male New Zealand White rabbits. The PVD magnetron-sputtered Ti-Sr-O surface coating was characterized using scanning electron microscopy (SEM) for morphology and coating thickness. Strontium release and mechanical stability of the coating, under simulated insertion conditions, were evaluated. Furthermore, histomorphometrical BIC and BF were carried out 2 weeks after insertion.

Results

Histomorphometry revealed increased bone formation of Ti-Sr-O with significant differences compared to SLActive and Grade 4 titanium in both regions of interest, ROI-I and ROI-II, at 0–250 µm and 250–500 µm distance from the implant surfaces. Analogous results of bone-to-implant contact were observed for the two modified surfaces.

Conclusion

The results show that a nanopatterned Ti-Sr-O functionalized titanium surface, with sustained release of strontium, increases peri-implant bone volume and could potentially contribute to enhancement of bone anchorage of osseointegrated implants.

Effect of strontium surface-functionalized implants on early and late osseointegration: A histological, spectrometric and tomographic evaluation

Numerous in vivo, in vitro and clinical studies report on beneficial effects of strontium with respect to increased bone growth. Based on this knowledge the aim of this study was to evaluate early and late osseointegration stages of functionalized titanium implants showing sustained release of strontium (Sr) and further investigate its potential systemic effect. Strontium functionalized (Ti-Sr-O) and Grade 4 (Control) titanium implants were inserted in the femoral condyle of New Zealand White rabbits. The Ti-Sr-O coating was characterized using Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectrometry (EDX) for structure, coating thickness and chemical composition. Inductively Coupled Plasma Atomic Emission Spectrometry (ICP-AES) was used to evaluate released strontium in vitro while Atomic Absorption Spectrometry (AAS) was utilized to monitor serum levels of strontium and calcium. Additionally, histological and tomographic analysis of bone-to-implant contact (BIC%) and bone formation (BF%) was performed, following implantation periods of two or twelve weeks, respectively. Median values for BIC% for Ti-Sr-O revealed significant differences within the two- and twelve-week observation periods, while exceeding BF% was discovered especially after twelve weeks when performing the histological evaluation. The results from the micro-computed tomography (µ-CT) showed no significant differences, when comparing the experimental groups. AAS measurements did not indicate a systemic effect by the local strontium release. Within the limitations of the study, it was shown that a Ti-Sr-O coating with sustained release characteristics of strontium, accelerates bone apposition and represents a potential potent surface modification for endosseous medical implant devices.

STATEMENT OF SIGNIFICANCE

This study presents first data with respect to early and late in vivo response on a strontium functionalized titanium surface comprising a nanotopography manufactured by a magnetron sputtering process. We investigated different osseointegration stages of screw-shaped implants with dental implant geometries in a rabbit femur model observing beneficial effects of the functionalized surface on bone-to-implant contact and bone formation caused by tailored release of the bone anabolic strontium. Histomorphometrical data revealed that a functionalized titanium surface with controlled liberation of strontium accelerates osseointegration while spectrometry measurements did not indicate a potential systemic effect of this osteoinductive agent and could thus have impact on modifications of medical implant devices.

Vapor pressure of ionic liquids at low temperatures from AC-chip-calorimetry

The very low vapor pressure of ionic liquids is challenging to measure. At elevated temperatures the liquids might start to decompose, and at relatively low temperatures the vapor pressure becomes too low to be measured by conventional methods. In this work we developed a highly sensitive method for mass loss determination at temperatures starting from 350 K. This technique is based on an alternating current calorimeter equipped with a chip sensor that consists of a free-standing SiNx-membrane (thickness <1 μm) and a measuring area with lateral dimensions of the order of 1 mm. A small droplet (diameter ca. 600 μm) of an ionic liquid is vaporized isothermally from the chip sensor in a vacuum-chamber. The surface-to-volume-ratio of such a droplet is large and the relative mass loss due to evaporation is therefore easy to monitor by the changing heat capacity (J K(-1)) of the remaining liquid. The vapor pressure is determined from the measured mass loss rates using the Langmuir equation. The method was successfully tested for the determination of the vapor pressure and the vaporization enthalpy of an archetypical ionic liquid 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide ([EMIm][NTf2]). The data set created in this way in an extremely broad temperature range from 358 K to 780 K has allowed the estimation of the boiling temperature of [EMIm][NTf2]. The value (1120 ± 50) K should be considered as the first reliable boiling point of the archetypical ionic liquid obtained from experimental vapor pressures measured in the most possible close proximity to the normal boiling temperature.

Influence of hydrothermal synthesis parameters on the properties of hydroxyapatite nanoparticles

Hydroxyapatite (HAp) nanoparticles of tunable diameter were obtained by the precipitation method at room temperature and by microwave hydrothermal synthesis (MHS). The following parameters of the obtained nanostructured HAp were determined: pycnometric density, specific surface area, phase purity, lattice parameters, particle size, particle size distribution, water content, and structure. HAp nanoparticle morphology and structure were determined using scanning electron microscopy (SEM) and transmission electron microscopy (TEM). X-ray diffraction measurements confirmed crystalline HAp was synthesized, which was pure in terms of phase. It was shown that by changing the synthesis parameters, the diameter of HAp nanoparticles could be controlled. The average diameter of the HAp nanoparticles was determined by Scherrer's equation via the Nanopowder XRD Processor Demo web application, which interprets the results of specific surface area and TEM measurements using the dark-field technique. The obtained nanoparticles with average particle diameter ranging from 8-39 nm were characterized by having homogeneous morphology with a needle shape and a narrow particle size distribution. Strong similarities were found when comparing the properties of some types of nanostructured hydroxyapatite with natural occurring apatite found in animal bones and teeth.

Osseointegration behavior of novel Ti-Nb-Zr-Ta-Si alloy for dental implants: an in vivo study

This study aimed to evaluate the effects of Ti-Nb-Zr-Ta-Si alloy implants on mineral apposition rate and new BIC contact in rabbits. Twelve Ti-Nb-Zr-Ta-Si alloy implants were fabricated and placed into the right femur sites in six rabbits, and commercially pure titanium implants were used as controls in the left femur. Tetracycline and alizarin red were administered 3 weeks and 1 week before euthanization, respectively. At 4 weeks and 8 weeks after implantation, animals were euthanized, respectively. Surface characterization and implant-bone contact surface analysis were performed by using a scanning electron microscope and an energy dispersive X-ray detector. Mineral apposition rate was evaluated using a confocal laser scanning microscope. Toluidine blue staining was performed on undecalcified sections for histology and histomorphology evaluation. Scanning electron microscope and histomorphology observation revealed a direct contact between implants and bone of all groups. After a healing period of 4 weeks, Ti-Nb-Zr-Ta-Si alloy implants showed significantly higher mineral apposition rate compared to commercially pure titanium implants (P < 0.05), whereas there was no significant difference between Ti-Nb-Zr-Ta-Si alloy implants and commercially pure titanium implants (P > 0.05) at 8 weeks. No significant difference of bone-to-implant contact was observed between Ti-Nb-Zr-Ta-Si alloy implants and commercially pure titanium implants implants after a healing period of 4 weeks and 8 weeks. This study showed that Ti-Nb-Zr-Ta-Si alloy implants could establish a close direct contact comparedto commercially pure titanium implants implants, improved mineral matrix apposition rate, and may someday be an alternative as a material for dental implants.

Fabrication of nano-structured calcium silicate coatings with enhanced stability, bioactivity and osteogenic and angiogenic activity

The bioactivity and stability of coatings on alloy implants play critical roles in the fast osseointegration and maintenance of a long-term life span of the implants, respectively. Herein, nano-sheet surface on bioactive calcium silicate (CaSiO3, CS) coatings on metal substrates was fabricated by combining atmosphere plasma spraying (APS) and hydrothermal technology (HT). The glassy phase in CS coatings generated by APS was converted into crystalline sheet-like nano-structures after HT treatment. Compared with the original CS coating samples, HT treatment decreased the degradation rate of the CS coatings. Moreover, the fabricated nano-structured topography of CS coatings increased the apatite mineralization ability and significantly enhanced the cell attachment, proliferation, differentiation, alkaline phosphatase (ALP) activity and expression of osteogenic genes and angiogenic factors of rat bone marrow stromal cells (bMSCs). Our results suggest that the nano-structured CS coatings have immense potential in improving the clinical performance of medical implants.