Glistenings in hydrophobic acrylic intraocular lenses do affect visual function

Comparative analysis of in vitro accelerated glistening formation in foldable hydrophobic intraocular lenses

PURPOSE

To analyse and compare the propensity to form glistenings in 4 different types of hydrophobic acrylic intraocular lenses (IOLs): Alcon AcrySof ® MA60AC, HOYA iSert® PC-60AD, Bausch&Lomb enVista, and Kowa Avansee™ PU6A.

METHODS

We used an accelerated laboratory method to create glistenings. IOLs were first immersed in saline at 45 °C for 24 h and then at 37 °C for 2.5 h. Microvacuole (MV) density and size were documented and calculated using an image analysis program.

RESULTS

Median density of glistenings [MV/mm2] for Alcon AcrySof ® MA60AC was 623 (range 507-804), for HOYA iSert® PC-60AD 1358 (range 684-2699), for Bausch&Lomb enVista 2 (range 1-2), and for Kowa Avansee™ PU6A 1 (range 1-4). The prevailing MV size was: 0-5 µm for Hoya IOLs, 5-10 µm for Alcon IOLs, 20-50 µm for Bausch&Lomb IOLs, and 5-50 µm for Kowa IOLs.

CONCLUSIONS

Glistenings could be induced in all studied IOLs using the accelerated laboratory method. The Alcon AcrySof ® MA60AC and HOYA iSert® PC-60AD IOLs showed MV of high density, while the glistenings in the Hoya IOLs were smaller in size compared to the Alcon IOLs. The MV density was minimal in the Bausch&Lomb enVista and Kowa Avansee™ PU6A IOLs. The propensity of the Alcon AcrySof ® MA60AC IOLs to form glistenings in vitro correlated with the findings of clinical results that are already published.

In-vitro glistening formation in six different foldable hydrophobic intraocular lenses

Background

Glistenings describe small, refractile microvacuoles that may arise within the intraocular lens (IOL) material and reduce the patients’ quality of vision. Lenses composed of hydrophobic acrylic material are particularly affected by glistening formation. In this study, we compared the tendency of glistening formation in six different types of hydrophobic acrylic intraocular lenses (IOLs).

Methods

We used a well-established accelerated laboratory method to develop glistenings in the following IOLs: Vivinex XY1 (Hoya), AcrySof SN60WF (Alcon), Tecnis ZCB00 (AMO), Avansee PN6A (Kowa), Aktis SP NS-60YG (Nidek), and CT Lucia 601P (Zeiss). IOLs were first immersed in saline at 45 °C for 24 h and then at 37 °C for 2.5 h in a water bath. Microvacuole (MV) density and size (Miyata grading) were documented and calculated using an image analysis program.

Results

The mean glistening density [MV/mm²] and mean Miyata grading (in brackets) were: Vivinex: 11.6 ± 5.7 (0), SN60WF: 264.4 ± 110.3 (2.6), Tecnis: 6.0 ± 2.8 (0), Avansee: 2.2 ± 0.7 (0), Aktis: 851.4 ± 59.4 (3+) and CT Lucia: 71.0 ± 71.6 (1).

Conclusions

While all tested IOLs showed glistenings with the accelerated laboratory method, the Aktis and SN60WF showed the highest microvacuole density, followed by the CT Lucia. In comparison, the Vivinex, Tecnis, and Avansee IOLs showed far fewer number of glistenings.