Degradation of fluorescent dye-Solvent Green 7 (HPTS) in wastewater by advanced oxidation process

Ultra-efficient catalytic degradation of malachite green dye wastewater by KMnO4-modified biochar (Mn/SRBC)

In this work, KMnO₄-modified biochar was prepared from spirulina residue as the research object. Herein, we report the synthesis, characterization, and catalytic degradation performance of KMnO₄-modified biochar, given that heterogeneous catalytic oxidation is an effective way to treat dye wastewater rapidly. The Mn/SRBC catalyst prepared by KMnO₄ modification was characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffractometry, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, nitrogen adsorption–desorption and laser Raman spectroscopy. In addition, we compared the results with that of the unmodified SRBC. The results showed that the Mn/SRBC catalyst prepared by KMnO₄ modification had a rich pore structure, which provided sufficient contact area for the catalytic reaction. In the presence of H₂O₂, the catalyst could be used to catalyze the oxidative degradation of malachite green in aqueous solution with ultra-high efficiency. In the experiment, the initial pH values of the reaction system had a significant influence on the reaction rate. The removal effect of biochar on the malachite green was poor in an alkaline environment. Within a specific range, the removal rate of malachite green was proportional to the concentration of H₂O₂ in the reaction system. The degradation rate of malachite green dye at 8000 mg L⁻¹ was about 99% in the presence of the catalyst over 5 mmol L⁻¹ hydrogen peroxide for 30 min. These results show the potential application of algae residue biochar and carbon-based composite catalysts for degrading and removing dye wastewater.

In this work, KMnO₄-modified biochar was prepared from spirulina residue as the research object.

Comparison of naphthalene removal performance using H2O2, sodium percarbonate and calcium peroxide oxidants activated by ferrous ions and degradation mechanism

The presence of polycyclic aromatic hydrocarbons (PAHs) in groundwater is making a great threat to human health in the world which has received an increasing environmental concern. Among various Fenton oxidation processes, 97.6%, 92.1% and 89.4% naphthalene (NaP) removals were observed using hydrogen peroxide (H₂O₂), sodium percarbonate (SPC) and calcium peroxide (CP) as oxidants activated by Fe(II) in ultrapure water tests, respectively. While, the inhibitory effect on NaP degradation caused by the weak alkaline solution pH and the presence of HCO₃^- in actual groundwater could be compensated by doubling dosages of oxidants and Fe(II) to different extent. 98.0%, 49.8% and 11.5% of NaP were degraded by using H₂O₂, SPC and CP, respectively, strongly suggesting the best H₂O₂ performance among them. It was observed that 83.3% and 9.6% inhibition on NaP degradation in H₂O₂/Fe(II)/NaP system occurred in the presence of isopropyl alcohol and chloroform, confirming that both hydroxyl radical (HO) and superoxide anion radical () contributed to NaP degradation in Fenton process and HO was the prominent radical. The presence of HO was further demonstrated by electro-spin resonance spectrometer analysis. The identification of transformation products of NaP revealed that hydroxylation and ring rupture were the main NaP degradation pathways.