Effect of Crystal Orientation on Amplitude-Dependent Damping in Magnesium

The Effect of Crystal Orientation on Damping Capacity in Rolled AZ31 Magnesium Alloy

The effect of crystal orientation on damping capacity is studied on hot rolled AZ31 magnesium alloy. AZ31 magnesium alloys which was machined out parallel to rolled direction and perpendicular to rolled direction were investigated about the relationship between the initial texture and damping capacity. The specimens are annealed at 623 K and time ranging from 30 to 180 minutes. After heat treatment recrystallization is occurred. Then, average grain size and damping capacity are increased with increasing annealing time. Two types of specimens show different main component of texture and damping capacity respectively. It is found that initial texture was affected on damping capacity.

Damping Measurements of the Magnesium Wrought Alloys AZ31, AZ61 and AZ80 after Indirect and Hydrostatic Extrusion

Magnesium cast parts as well as indirectly and hydrostatically extruded profiles were used in order to investigate the influence of different microstructures on the damping behaviour of magnesium AZ-alloys. Especially, hydrostatic extrusion leads to a significant grain refinement in the extruded profile compared to indirect extrusion. Strain dependent damping measurements were carried out at room temperature using alloys AZ31, AZ61 and AZ80. Damping was determined as the logarithmic decrement of free bending beam vibrations. The results of these measurements after indirect and hydrostatic extrusion are shown and discussed.