Effect of placement agitation and drying time on dentin shear bond strength: an in vivo study

Influence of different phosphoric acids before application of universal adhesive on the dental enamel

BACKGROUND

There are different etching gels available, which have different composition, different pH, and different viscosity, and there is little information in the literature comparing all these products.

OBJECTIVE

To evaluate the mean microshear bond strength and morphological characteristics of tooth enamel by evaluating different phosphoric acids combined with a universal adhesive system.

MATERIALS AND METHODS

Eighty-four enamel samples were used, which were divided according to the acid conditioning: G1: Scotchbond Etchant (3M Oral Care), G2: Ultra-Etch (Ultradent), G3: Eco-Etch (IvoclarVivadent), G4: ETCH-37 with BAC (Bisco), G5: Etching gel (Densell), G6: Condac 37 (FGM), and G7: Scotchbond Universal Adhesive (3M Oral Care) in self-etch mode. For the adhesive procedure, Scotchbond Universal Adhesive was the one used as indicated the manufacturer's instructions, 0.9-mm-diameter resin cylinders were placed. The microshear bond strength test was performed after being stored for 24 hours in water. The morphological characteristics of tooth enamel were analyzed using the Raman confocal microscope alpha300RA. The analysis of variance (ANOVA) test and Tukey post-test were used to analyze the differences between the groups.

RESULTS

The mean microshear bond strength values obtained for groups 1, 4, 5 were significantly greater than groups 2, 3, 6 and 7 (p < .05). All groups presented demineralization after the application of the etching acid, and few signs of demineralization were evident in group 7.

CONCLUSIONS

Acid-etching with ETCH-37 with BAC, Etching gel, and Scotchbond Etchant improved the adhesive strength in the enamel using an universal adhesive, and acid-etching with Condac 37, Ultra-Etch, and Eco-Etch provides similar adhesive strength values to self-etch mode of universal adhesive.

CLINICAL SIGNIFICANCE

All acid etchants should be considered as different. The test confirms that enamel etching prior to the application of a universal adhesive system depends on the selected acid etchand product.

Dentinal Hypersensitivity Treatment Using Diode Laser 980 nm: In Vivo Study

The discomfort of patients due to dentinal hypersensitivity (DH) is one of the main challenges that dentists face in daily practice. Difficulties in DH treatment gave rise to many protocols which are currently used. The aim of this clinical study is to evaluate the effectiveness of a new protocol on the reduction of dentinal hypersensitivity with diode laser 980 nm and the application of a graphite paste. 184 patients enrolled in the study, the degree of pain was evaluated by visual analog scale (VAS), graphite paste was applied on the exposed dentine before irradiation, the application of diode laser 980 nm with continuous mode, backward motion, tangential incidence of the beam in non-contact mode and a delivery output of 1 W. Fiber’s diameter was 320 μm and total exposure time depended on the time necessary to remove the graphite paste from the teeth. Statistical analyses were performed with Prism 5^® software. Pain in post-operative significantly decreased immediately after the treatment. Mean values stayed stable until a 6-month follow-up. The application is considered to be safe with long-term effectiveness.

Clinical Effectiveness of a Resin-modified Glass Ionomer Cement and a Mild One-step Self-etch Adhesive Applied Actively and Passively in Noncarious Cervical Lesions: An 18-Month Clinical Trial

OBJECTIVES:

To evaluate the clinical effectiveness of two methods of application of a mild one-step self-etch adhesive and composite resin as compared with a resin-modified glass ionomer cement (RMGIC) control restoration in noncarious cervical lesions (NCCLs).

METHODS:

A total of 294 restorations were placed in 56 patients, 98 in each one of the following groups: 1) G-Bond active application combined with Solare-X composite resin (A-1SEA), 2) G-Bond passive application combined with Solare-X composite resin (P-1SEA), and 3) GC II LC RMGIC. The restorations were evaluated at baseline and after six, 12, and 18 months according to the FDI criteria for fractures/retention, marginal adaptation, marginal staining, postoperative sensitivity, and secondary caries. Cumulative failure rates were calculated for each criterion at each recall period. The effect of adhesive, method of application, and recall period were assessed. The Kruskal-Wallis test for intergroup comparison and Friedman and Wilcoxon signed ranks tests for intragroup comparison were used for each criterion ( α=0.05).

RESULTS:

The retention rates at 18 months were 93.26% for the A-1SEA group, 86.21% for the P-1SEA group, and 90.91% for the RMGIC group. The active application improved the retention rates compared with the passive application of mild one-step self-etch adhesive; however, no statistically significant difference was observed between the groups. Marginal staining was observed in 13 restorations (1 in A-1SEA, 4 in P-1SEA, and 8 in RMGIC) with no significant difference between the groups. The RMGIC group showed a significant increase in marginal staining at 12 and 18 months from the baseline. There was no significant difference between the groups for marginal adaptation, secondary caries, or postoperative sensitivity.

CONCLUSION:

Within the limitations of the study, we can conclude that mild one-step self-etch adhesive followed by a resin composite restoration can be an alternative to RMGIC with similar retention and improved esthetics in restoration of NCCLs. Agitation could possibly benefit the clinical performance of mild one-step self-etch adhesives, but this study did not confirm that the observed benefit was statistically significant.

Effect of rubbing force magnitude on bond strength of universal adhesives applied in self-etch mode

This study investigated the effect of rubbing force magnitude on dentin bond strengths of multi-mode adhesives applied in self-etch mode. Seventy-two extracted human molar teeth were used. Two different universal adhesives Single Bond Universal (SB) and Clearfil Universal (CL) were applied onto dentin surfaces in three different modes: without rubbing (NR), rubbing with 40 gf (gram-force) (40) or 80 gf (80) load. Teeth were restored with a resin composite. Half of the specimens were subject to thermal aging (10,000 cycles). Microtensile bond strength was measured and data were statistically analyzed with two-way analysis of variance and Tukey's test (α=0.05). Baseline bond strength values for CL adhesive were improved by rubbing (40 and 80 gf) as compared to no rubbing (p<0.05). Rubbing did not significantly improve bond strength values for SB, regardless of aging (p>0.05). Rubbing improves bonding performance of some universal adhesives to dentin when applied in self-etch mode.

Dentinal tubules sealing by means of diode lasers (810 and 980 nm): a preliminary in vitro study

OBJECTIVE

The aim of this study was to evaluate the effect on dentinal surfaces of diode lasers (810 and 980 nm) at different parameters.

MATERIALS AND METHODS

Twenty-four caries-free human impacted wisdom teeth were used. The crowns were sectioned transversely in order to expose the dentin. The smear layer was removed by a 1 min application of ethylenediaminetetraacetic acid (EDTA). Each surface was divided into four quadrants irradiated at a different output power setting for each kind of laser: 0.8, 1, 1.6, and 2 W (energy densities: 2547, 3184, 5092, and 6366 J/cm(2), irradiation speed 1 mm/sec; optical fiber diameter: 200 μm; continuous and noncontact mode). Half of the samples were stained with a graphite paste. All specimens were sent for scanning electron microscopic (SEM) analysis. Pulp temperature increases in additional 20 teeth were measured by a thermocouple.

RESULTS

Diode laser irradiations at 0.8 and 1 W led to occlusion or narrowing of dentin tubules without provoking fissures or cracks. The application of graphite paste increased the thermal effects in dentin. Measurements of pulp temperature showed that irradiations at 0.8 and 1 W for a period of 10 sec in continuous mode increased pulp temperature (T ≤2°C).

CONCLUSIONS

Diode lasers (810 and 980 nm) used at 0.8 and 1 W for 10 sec in continuous mode were able to seal the dentin tubules. These parameters can be considered harmless for pulp vitality, and may be effective in the treatment of dentinal hypersensitivity.