Bond durability of self-etch adhesive to ethanol-based chlorhexidine pretreated dentin after storage in artificial saliva and under intrapulpal pressure simulation

The Effect of Thermocycling on Interfacial Bonding Stability of Self-Etch Adhesives: OCT Study

Objective

The aim of this study was to monitor the behavior of interfacial gaps formed under different bonded polymeric restorations before and after thermocycling (TC), using swept-source optical coherence tomography (SS-OCT) and confirming the obtained findings with confocal laser scanning microscopy (CLSM).

Materials and Methods

Cylindrical class I cavities were prepared in twenty noncarious human premolar teeth (1.5 mm depth × 3.5 mm diameter) and divided randomly into two groups: TS and SN, according to the adhesive system (n = 10). In the TS group, one-step self-etch adhesive Clearfil Tri-S Bond Plus (Kuraray Noritake Dental, Japan) was used, followed by composite restoration using Estelite Sigma Quick (Tokuyama Dental, Japan). In the SN group, the cavities were restored with the two-step self-etch/composite silorane-based resin restoration system (3M ESPE, USA). All specimens were restored in bulk filling technique and cured in accordance with the manufacturers' instructions. Both groups were imaged under SS-OCT after 24 h and recorded as controls. Then, each group was subjected to thermal challenge using the TC machine (5–55°C) and B-scans were recorded at different TC intervals (2600, 5200, and 10000). In order to confirm the SS-OCT findings, additional specimens were prepared, scanned, and sectioned for CLSM observation.

Results

B-scans demonstrated white clusters at the tooth-resin interface that corresponded to the gap location on CLSM images. The TS group showed significantly less gap formation than the SN group before and after TC (p < 0.001).

Conclusions

An optimal composite adaptation can be achieved when the bonded restoration comprises a combination of an adhesive containing 10-MDP monomer and a considerable highly filled composite.

MMP Inhibitors and Dentin Bonding: Systematic Review and Meta-Analysis

Objectives

Resin-dentin bond strength decreases over time. This reduction is related to the loss of hybrid layer integrity. Collagenolytic enzymes, especially matrix metalloproteinases (MMPs), are responsible for the degradation of the collagen matrix of the hybrid layer. Various MMP inhibitors with the ability to prevent enzymatic degradation have been identified. This study aimed to systematically review the literature for studies which evaluated the effect of MMP inhibitors on the immediate and aged dentin bond strengths. Study SelectionScreening and analysis were carried out by two reviewers. Two databases were searched, and from a total of 740 articles, 43 were accepted for full review. 21 articles with 0.2%–2% chlorhexidine (CHX) treatments were included for meta-analysis. A risk of bias assessment was performed on all studies chosen for meta-analysis. A variety of MMP inhibitors have been studied, CHX being the most widely used.

Conclusions

A clear trend for a lower loss of dentin bond strength was observed with different MMP inhibitors. In meta-analysis, no significant difference was seen between the CHX and control in the immediate bond strengths. Bond strengths in the CHX group were significantly higher than the control group after aging (P < 0.001). The percentage of fractures occurring at the adhesive interface increased after aging. Five out of 21 studies included in the meta-analysis had high and the rest medium risk of bias. More long-term studies with lower risks of bias should be carried out to increase the reliability of results. Clinical RelevanceThe use of MMP inhibition with chlorhexidine can be recommended to increase the longevity of resin-dentin bond strength.

Physicochemical and biological properties of novel chlorhexidine-loaded nanotube-modified dentin adhesive

A commercially available three-step (etch-and-rinse) adhesive was modified by adding chlorhexidine (CHX)-loaded nanotubes (Halloysite®, HNT) at two concentrations (CHX10% and CHX20%). The experimental groups were: SBMP (unmodified adhesive, control), HNT (SBMP modified with HNT), CHX10 (SBMP modified with HNT loaded with CHX10%), and CHX20 (SBMP modified with HNT loaded with CHX20%). Changes in the degree of conversion (DC%), Knoop hardness (KHN), water sorption (WS), solubility (SL), antimicrobial activity, cytotoxicity, and anti-matrix metalloproteinase [MMP-1] activity (collagenase-I) were evaluated. In regards to DC%, two-way ANOVA followed by Tukey's post-hoc test revealed that only the factor "adhesive" was statistically significant (p < 0.05). No significant differences were detected in DC% when 20 s light-curing was used (p > 0.05). For Knoop microhardness, one-way ANOVA followed by the Tukey's test showed statistically significant differences when comparing HNT (20.82 ± 1.65) and CHX20% (21.71 ± 2.83) with the SBMP and CHX10% groups. All adhesives presented similar WS and cytocompatibility. The CHX-loaded nanotube-modified adhesive released enough CHX to inhibit the growth of S. mutans and L. casei. Adhesive eluates were not able to effectively inhibit MMP-1 activity. The evaluation of higher CHX concentrations might be necessary to provide an effective and predictable MMP inhibition. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res B Part B, 2018. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 868-875, 2019.

Effect of digluconate chlorhexidine on bond strength between dental adhesive systems and dentin: A systematic review

Aim:

This study aimed to systematically review the literature for the effect of digluconate chlorhexidine (CHX) on bond strength between dental adhesive systems and dentin of composite restorations.

Materials and Methods:

The electronic databases that were searched to identify manuscripts for inclusion were Medline via PubMed and Google search engine. The search strategies were computer search of the database and review of reference lists of the related articles. Search words/terms were as follows: (digluconate chlorhexidine*) AND (dentin* OR adhesive system* OR bond strength*).

Results:

Bond strength reduction after CHX treatments varied among the studies, ranging 0-84.9%. In most of the studies, pretreatment CHX exhibited lower bond strength reduction than the control experimental groups. Researchers who previously investigated the effect of CHX on the bond strength of dental adhesive systems on dentin have reported contrary results, which may be attributed to different experimental methods, different designs of the experiments, and different materials investigated.

Conclusions:

Further investigations, in particular clinical studies, would be necessary to clarify the effect of CHX on the longevity of dentin bonds.

Dentin bonding: can we make it last?

In dentin bonding, contemporary dental adhesive systems rely on formation of the hybrid layer, a biocomposite containing dentin collagen and polymerized resin adhesive. They are usually able to create at least reasonable integrity of the hybrid layer with high immediate bond strength. However, loss of dentin-bonded interface integrity and bond strength is commonly seen after aging both in vitro and in vivo. This is due to endogenous collagenolytic enzymes, matrix metalloproteinases, and cysteine cathepsins, responsible for the time-dependent loss of hybrid layer collagen. In addition, the hydrophilic nature of adhesive systems creates problems that lead to suboptimal hybrid layers. These problems include, for example, insufficient resin impregnation of dentin, phase separation, and a low rate of polymerization, all of which may reduce the longevity of the bonded interface. Preservation of the collagen matrix integrity by inhibition of endogenous dentin proteases is key to improving dentin bonding durability. Several approaches to retain the integrity of the hybrid layer and to improve the long-term dentin bond strength have been tested. These include the use of enzyme inhibitors, either separately or as incorporated into the adhesive resins; increase of collagen resistance to enzymatic degradation; and elimination of water from the interface to slow down or eliminate hydrolytic loss of the hybrid layer components. This review looks at the principles, current status, and future of the different techniques designed to prevent the loss of hybrid layer and bond strength.

MMP Inhibitors on Dentin Stability: A Systematic Review and Meta-analysis

The aim of this study was to systematically review the literature for in vitro and ex vivo studies that evaluated the effect of matrix metalloproteinase (MMP) inhibitors during the adhesive procedure on the immediate and long-term resin-dentin bond strength. The search was conducted in 6 databases with no publication year or language limits, following the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) statement. From 1,336 potentially eligible studies, 48 were selected for full-text analysis, and 30 were included for review, with 17 considered in the meta-analysis. Two reviewers independently selected the studies, extracted the data, and assessed the risk of bias. Pooled effect estimates were expressed as the weighted mean difference between groups. The most used MMP inhibitor was chlorhexidine (CHX). Immediate bond strength results showed no difference between 2% CHX and control; however, a difference was found between 0.2% CHX and control at baseline. After aging, CHX presented higher bond strength values compared to control groups (p < .05). However, this was not observed for longer periods of aging. High heterogeneity was found in some comparisons, especially for the water storage aging subgroup. Subgroup analyses showed that self-etching and etch-and-rinse adhesives are benefited by the CHX use. From the studies included, only 1 presented low risk of bias, while the others showed medium or high risk of bias. The use of MMP inhibitors did not affect the immediate bond strength overall, while it influenced the aged bond strength. Aging procedures influenced bond strength values of the dentin adhesion stability.