Bond Stability of a Universal Adhesive System to Eroded/Abraded Dentin After Deproteinization

Evaluation of Color Stability and Translucency of Different Composite Resins Exposed to Alcohol

BACKGROUND

As there is evidence showing the effects of alcohol on the surface properties of composite resins, it is of great importance to understand the effects of commonly consumed beverages on the discoloration of composite restorations in people who consume alcohol.

AIM

The aim of this study was to investigate the changes in the color and translucency of composite resins immersed in different beverages after exposure to alcohol.

METHODS

Disk-shaped samples from each composite resin (Filtek Z250 (Z250), Clearfil Majesty Esthetic (CME), and Esthelite Bulk Fill Flow (EBF), were prepared (n = 60) and randomly divided into two groups (exposed or unexposed to alcohol). The samples were immersed in distilled water, black tea, and coffee. The color parameter (∆E00) and translucency parameter (∆TP) were calculated after 24 h, 1 week, and 3 weeks. Four-way ANOVA and Tukey's post-hoc analysis were used for the statistical analysis (α = 0.05).

RESULTS

Alcohol significantly increased the discoloration of Z250 and EBF in black tea. The discoloration of CME was not affected by alcohol exposure. Z250 and EBF showed clinically unacceptable discoloration (ΔE00 > 2.25) after immersion in black tea and coffee, whereas CME showed clinically unacceptable discoloration after immersion in black tea. Black tea caused the greatest color change in all composite materials regardless of alcohol exposure. EBF showed the lowest ΔTP values (∆TP = -1.82) at 3 weeks of immersion in black tea.

CONCLUSIONS

The effect of alcohol on discoloration depended on the composite type used. The translucency of bulk-fill flowable composite decreased with alcohol exposure.

The Effect of a Deproteinizing Pretreatment on the Bonding Performance and Acid Resistance of a Two-step Self-etch Adhesive on Eroded Dentin

OBJECTIVES

This study evaluated how deproteinization using sodium hypochlorite (6% NaOCl) or hypochlorous acid (50 ppm HOCl) with or without the subsequent use of an arylsulfinate salt-containing agent (Clearfil DC Activator; DCA; Kuraray Noritake Dental) affects the micro-tensile bond strength (μTBS) and formation of an acid-base resistant zone (ABRZ) of a two-step self-etch adhesive on eroded dentin.

METHODS

Coronal dentin surfaces of sound human molars were exposed to 48 cycles of demineralization (1% citric acid; 5 minutes) and remineralization (buffer solution with pH=6.4; 3.5 hours). They were then assigned to experimental groups according to the pretreatment used: none (negative control), NaOCl, NaOCl+DCA, HOCl, and HOCl+DCA. Sound dentin surfaces with no pretreatment were used as a positive control. The dentin surfaces were bonded with Clearfil SE Bond 2 (Kuraray Noritake Dental), and μTBS was measured either after 24 hours or 20,000 thermal cycles (TC). The μTBS data were statistically analyzed using a mixed-model analysis of variance (ANOVA) and t-tests with Bonferroni correction. Failure mode was determined with scanning electron microscopy (SEM), which was also used for the observation of ABRZ.

RESULTS

Among experimental groups, there was no significant difference between the negative control, HOCl, and HOCl+DCA after 24 hours, but the HOCl-pretreated groups exhibited significantly higher μTBS than the negative control after TC (p<0.01). Pretreatment with NaOCl and NaOCl+DCA resulted in significantly higher μTBS (p<0.001), but the highest μTBS was measured on sound dentin (p<0.001). TC decreased μTBS significantly in all groups (p<0.001) except for sound dentin and NaOCl+DCA (p>0.05). Adhesive failures prevailed in eroded groups, whereas cohesive failures were predominant on sound dentin. ABRZ was recognized in all groups but marked morphological differences were observed.

CONCLUSIONS

The combined use of 6% NaOCl and the arylsulfinate salt-containing agent partially reversed the compromised bonding performance on eroded dentin, while the effect of 50 ppm HOCl was negligible.

Comparison of Different Dentin Deproteinizing Agents on Bond Strength and Microleakage of Universal Adhesive to Dentin

Aim:

To evaluate the effects of papain (Brix 3000), bromelain, sodium hypochlorite (NaOCl), and chlorine dioxide (ClO2) application to the deep dentin surface on shear bond strength (SBS), microleakage, and dentin surface properties.

Materials and Methods:

Deep dentin surface ( n = 100) for evaluating SBS, class V preparation at the buccal surface for testing microleakage ( n = 100), and deep dentin slices ( n = 20) for evaluating surface properties were conducted on the 220 molar teeth. Four different deproteinizing agents (Brix 3000, 40% bromelain, 5.25% NaOCl (Chloraxid), and 0.12% ClO2) were applied to the dentin, and then the universal adhesive was used in self-etch (SE) and etch&rinse (E&R). Deproteinizing agents were not applied to the control group. All of the samples were subjected to 5000 cycles of thermal aging at 5ºC–55ºC. SBS (MPa) was tested by a universal testing machine. The microleakage of resin composite bonded with different adhesive modes was evaluated under a stereomicroscope. The changes in the surface morphology were examined with scanning electron microscopy (SEM) and attenuated total reflection – fourier transform infrared spectroscopy (ATR-FTIR).

Results:

ClO2 exhibited the highest bond strength among deproteinizing agents. Compared to the SE mode, E&R mode significantly showed higher bond strength ( p < .05). In gingival margin, bromelain SE exhibited the highest marginal leakage, while Brix 3000 SE had the lowest mean microleakage score.

Conclusion:

Deproteinizing with ClO2 was effective in improving the SBS of universal adhesive in the E&R mode to deep dentin. Deproteinization with bromelain before universal adhesive in SE mode showed more microleakage on both the occlusal and gingival surfaces.

Resin infiltrant protects deproteinized dentin against erosive and abrasive wear

Objectives

This study aimed to investigate the anti-erosive/abrasive effect of resin infiltration of previous deproteinized dentin.

Materials and Methods

Dentin slabs were randomly assigned to 3 groups (n = 15): Control (no deproteinization; no resin infiltrant applied), RI (no deproteinization; resin infiltrant applied), and DRI (deproteinization; resin infiltrant applied). After undergoing the assigned treatment, all slabs were subjected to an in vitro cycling model for 5 days. The specimens were immersed in citric acid (0.05 M, pH = 3.75; 60 seconds; 3 times/day) and brushed (150 strokes). Between the challenges, the specimens were exposed to a remineralizing solution (60 minutes). The morphological alterations were analyzed by mechanical profilometry (µm) and scanning electron microscopy (SEM). Data were submitted to one-way analysis of variance (ANOVA) and Tukey tests (p < 0.05).

Results

Control and RI groups presented mineral wear and did not significantly differ from each other (p = 0.063). DRI maintained a protective layer preserving the dentin (p < 0.001). After erosive/abrasive cycles, it was observed that in group RI, only 25% of the slabs partially evidenced the presence of the infiltrating, while, in the DRI group, 80% of the slabs presented the treated surface entirely covered by a resin-component layer protecting the dentin surface as observed in SEM images.

Conclusions

The removal of the organic content allows the resin infiltrant to efficiently protect the dentin surface against erosive/abrasive lesions.

Sodium p-Toluenesulfinate Enhances the Bonding Durability of Universal Adhesives on Deproteinized Eroded Dentin

The effects of deproteinization using sodium hypochlorite (NaOCl) and the subsequent application of an antioxidant (sodium p-toluenesulfinate, STS) onto the bonding durability of universal adhesives on eroded dentin were investigated. Untreated sound dentin served as the control, whereas eroded dentin, which had been prepared by pH-cycling in 1% citric acid and a remineralization solution, was either untreated, deproteinized with a 10% NaOCl gel or deproteinized with the 10% NaOCl gel and subsequently treated with an STS-containing agent. The dentin surfaces were bonded using a universal adhesive (Clearfil Universal Bond Quick, Scotchbond Universal or G-Premio Bond), and the micro-tensile bond strength (µTBS) test was performed after 24 h or 10,000 thermal cycles. The µTBS data were statistically analyzed using a three-way ANOVA and Tukey’s HSD post hoc tests. The lowest µTBS was measured on untreated eroded dentin (p < 0.001). Deproteinization of eroded dentin resulted in µTBS similar to untreated sound dentin (p > 0.05), but the highest µTBS was obtained if deproteinization was followed by the application of STS. Thermocycling significantly decreased µTBS in all groups (p < 0.001), except for STS-treated deproteinized eroded dentin (p > 0.05). This indicated that deproteinization, followed by the application of STS, could enhance the bonding durability of universal adhesives on eroded dentin.

Biodentine or Mineral Trioxide Aggregate as Direct Pulp Capping Material in Mature Permanent Teeth with Carious Exposure? A Systematic Review and Meta-analysis

OBJECTIVE

To evaluate the success rate of direct pulp capping (DPC) with Biodentine in mature permanent teeth with carious vital pulp exposure compared to that of DPC with mineral trioxide aggregate (MTA) by means of a systematic review and meta-analysis.

DATA SOURCES

The two authors searched independently the literature published through July 31, 2020, in five electronic databases (PubMed, the Cochrane Central Register of Controlled Trials, Web of Science Core Collection, the Wiley Online Library, and the SCOPUS database).

STUDY SELECTION

The research protocol was previously registered in the PROSPERO database (CRD42020192511). Clinical studies that met the inclusion criteria were chosen and independently screened by the authors.

DATA EXTRACTION

A custom-designed spreadsheet was used to extract the data. The quality of each study was evaluated by means of the revised Cochrane risk of bias (ROB) tool or the ROB of nonrandomized studies of interventions tool.

DATA SYNTHESIS

Three randomized controlled trials and one retrospective study met the inclusion criteria. Only one study had a high risk of bias. The included studies reported data on a total of 95 participants with an age range of 8-51 years. No significant difference was observed in the overall treatment outcome when comparing Biodentine with MTA (Risk ratio=1.00, 95% confidence interval [0.93-1.07], p=1.00).

CONCLUSIONS

Biodentine had comparable clinical and radiographic success to that of MTA when used as a DPC agent in mature permanent teeth with carious vital pulp exposure. Additional high-quality studies are needed.

Adhesion to eroded enamel and dentin: systematic review and meta-analysis

OBJECTIVE

The aim of this systematic review and meta-analysis was to compare the bond strength between eroded and sound permanent enamel and dentin and to assess whether bonding performance (immediate and after aging) differs between etch&rinse and self-etch adhesives and can be improved by surface pretreatment prior to bonding.

METHODS

Electronic databases (PubMed, Scopus, Embase, Web of Science, CENTRAL, LILACS, BBO) were searched by two reviewers. Random-effect meta-analyses were performed to compare bond strength to sound and eroded dental hard tissues without and with surface pretreatment prior to bonding, respectively. The effect of adhesive mode (etch&rinse vs. self-etch) and aging (immediate vs. aged) was compared using subgroup analyses. Statistical heterogeneity was assessed using Cochran's Q and I²-statistic. Funnel plots and Egger's regression intercept tests were used to evaluate publication bias. Quality and risk of bias of included studies were also assessed.

RESULTS

Fourty-seven studies (45 in vitro, 2 in situ) were included in the systematic review and meta-analyses. Erosion impairs bond strength to dentin (p < 0.001; mean difference: -10.2 MPa [95%CI: -11.9 to -8.6 MPa]), but not to enamel (p = 0.260). Surface pretreatment measures removing or stabilizing the collagenous matrix can improve dentin bond strength (maximum mean difference: +12.4 MPa). Etch&rinse and self-etch adhesives did not perform significantly different on eroded enamel (p = 0.208) and dentin (p = 0.353). The majority of studies (32 of 47) presented a medium risk of bias.

SIGNIFICANCE

Data from in vitro and in situ studies showed that erosion impairs dentin bonding of etch&rinse and self-etch adhesives and makes surface pretreatment prior to bonding of composite restorations necessary.

Analysis of laboratory adhesion studies in eroded enamel and dentin: a scoping review

Aim

To summarize and report laboratory studies of adhesion in eroded substrates, which used bond strength as an outcome measure. To determine the strategies available to overcome bonding difficulties, the quality and consistency of the methodology and to find evidence gaps.

Materials and Methods

The present review followed PRISMA-ScR guidelines. A search was conducted on PubMed/Medline, Scopus and EMBASE (Ovid) databases to identify published peer-reviewed papers (2010–2020). For final qualitative synthesis, 29 articles were selected which respected the inclusion criteria. Data charting was carried out, independently, by two reviewers and quality assessment of the articles was performed.

Results

The primary studies included fall into four major categories: comparison of restorative materials and application modes, enzymatic inhibitors, surface pretreatments or remineralization strategies. Most studies found evaluated dentin (76%), while 17% evaluated enamel, and 7% evaluated both substrates. The majority of the studies reported an effective intervention (83%). Bond strength to eroded dentin is significantly reduced, while in enamel erosion is beneficial. The bond strength to eroded dentin is material-dependent and favored in systems containing 10-MDP. Great disparities among the erosion models used were found, with citric acid in different concentrations being the preferred method, although standardization is lacking.

Conclusions

Adhesives containing 10-MDP show beneficial results in eroded dentin, and surface preparation methods should be considered. Studies which evaluated adhesion to eroded enamel/dentin show high heterogeneity in what concerns aims and methodology. Strategies that focus on remineralizing dentin and strategies to protect bond longevity in this substrate require further research.

The effect of temporary sealing materials and cleaning protocols on the bond strength of resin cement applied to dentin using the resin-coating technique

This study evaluated the effect of temporary sealing materials and cleaning protocols on the bond strength of resin cement applied to dentin using resin-coating technique. Scotchbond Universal Adhesive and Filtek Supreme Ultra Flowable were applied to bovine dentin. Forty-five specimens were divided into the following three groups according to the temporary sealing materials: Cav-: CAVITON EX, Vas-: COCOA BUTTER and FIT SEAL, and Sep-: Washable SEP and FIT SEAL. Each material was placed on resin-coated dentin. After 1-week water storage, one of the following three cleaning protocols was performed: -WA: washed with water, -BR: brushed with PRESSAGE, and -AF: cleaned with AIR-FLOW. Microtensile bond strength test and EDS analysis were conducted. Irrespective of the cleaning protocol used, Washable SEP demonstrated less residual debris on resin-coated dentin, resulting in high bond strength. Regardless of the temporary sealing material applied, AIR-FLOW demonstrated less residual debris, resulting in high bond strength.

Resistência da união de restaurações confeccionadas com sistemas adesivos universais em dentes acometidos por erosão ácida

Objetivos: Avaliar a resistência adesiva de diferentes sistemas adesivos universais em esmalte e dentina erodidos. Métodos: As unidades experimentais foram compostas por 30 fragmentos de esmalte bovino e 30 fragmentos de dentina bovina divididos aleatoriamente em três grupos experimentais de acordo com os sistemas adesivos universais utilizados (n = 10): Single Bond Universal (3M ESPE), Peak Universal (Ultradent) e Ambar Universal (FGM). Previamente as restaurações, os fragmentos de esmalte e dentina foram submetidos à desafio erosivo em ácido cítrico a 0,3% (pH = 2,6) durante cinco minutos, quatro vezes por dia por cinco dias. Um cilindro de resina composta (Forma, Ultradent) com 2mm de diâmetro foi construído em cima de cada fragmento. A resistência ao cisalhamento foi avaliada em máquina de ensaio universal (1mm/min). Os valores obtidos de resistência da união (MPa) foram analisados por ANOVA dois fatores e teste de Bonferroni (α=0,05). Resultados: Não houve diferença significativa entre os sistemas adesivos testados no mesmo substrato. O esmalte apresentou maiores valores de resistência da união que a dentina. Houve predomínio da falha coesiva em resina no esmalte e falha adesiva na dentina. Conclusão: Os sistemas adesivos universais testados apresentaram resistência adesiva semelhantes entre si dentro do mesmo substrato erodido.