Effect of Various Bleaching Agents on the Surface Composition and Bond Strength of a Calcium Silicate-based Cement

Assessing the bleaching effect of an experimental stabilized chlorine dioxide agent used for internal bleaching purposes

Aim: Assessing the intracoronal bleaching effectiveness of an experimental chlorine dioxide product, based on the walking bleach technique. Methods: Extracted bovine incisors were artificially stained with bovine blood and filled with zinc phosphate cement at cementoenamel junction level. Teeth were divided into 3 groups (n=10): (SP) sodium perborate added with distilled water, (CD) chlorine dioxide and (C) control – dry cotton inserted into the pulp chamber. Bleaching agents were used at 0, 7 and 14 days. VITA Easyshadetm (ΔEab) was used to analyze tooth color at the 7th, 14th and 21st days, based on the CIE2000 system. Data were analyzed through ANOVA and Tukey’s test. Results: There were no statistically significant differences in Δb, ΔE, ΔE00 and ΔWID between CD and the control group. These parameters have shown significant differences between CD and SP, which differed from the control. However, they did not show significant differences either in the control group or in CD at the 7th, 14th and 21st days. Values recorded for SP at the 7th day differed from those recorded at the 14th and 21st days. Δa has shown differences within the same group at the 7th, 14th and 21st days. There was no difference between groups, when they were compared at the same day (7th and 14th). The control group differed from SP at the 21st day. CD did not differ from the other two groups. ΔL did not show differences between groups and times. Conclusion: Stabilized chlorine dioxide (0.07%, at pH 3.5) should not be used as intracoronal bleaching agent along with the walking bleach technique.

Influence of intracoronal bleaching agents on the bond strength of MTA cements to composite resin and their surface morphology

The objective of the present in vitro study was to evaluate micro-tensile bond strength (µSBS) of MTA cements to composite resin using a universal adhesive after internal bleaching procedure, and to examine surface characteristics of MTA cements exposed to bleaching agents. MTA specimens were divided into three subgroups according to the bleaching agent used which were, 37% carbamide peroxide (CP), 35% hydrogen peroxide (HP), and no exposure as a control group (n = 12). After exposure to bleaching agent, composite resins were applied to MTA surfaces using a universal adhesive in self-etch mode. The specimens were exposed to a shear force until failure to evaluate bond strength. MTA surfaces were investigated using scanning electron microscopy (SEM) to observe the effects of the bleaching agents. Differences between groups were analyzed using two-way ANOVA test and intergroup comparisons were assessed with Tukey test (p < 0.05). Although there was a slight difference in bond strength between bleaching agents (CP and HP), no significant difference was found, irrespective of MTA cement. After the HP application, the bond strength values decreased approximately by half compared with the controls. SEM results demonstrated distinct morphological differences between the intact MTA surface (control) and treated MTA surface. Distinct micro-cracks, surface irregularities, and capillary voids formed due to the superficial dissolution caused by peroxides. Exposure to the intra-coronal bleaching agents had a negative influence on the surface morphology of MTA cements and their bond strength to composite resin.