Streptococcus mutans Biofilm Formation and Cell Viability on Polymer-infiltrated Ceramic and Yttria-stabilized Polycrystalline Zirconium Dioxide Ceramic

A new technique for incorporation of TiO2 nanotubes on a pre-sintered Y-TZP and its effect on bond strength as compared to conventional air-borne particle abrasion and silicatization TiO2 nanotubes application on pre-sintered Y-TZP

OBJECTIVE

This study evaluated the microshear bond strength of a resin cement to Y-TZP after different methods of TiO₂ nanotubes (nTiO₂) incorporation on pre-sintered Y-TZP surfaces.

METHODS

nTiO₂ were synthesized and incorporated on Y-TZP slices as follows (n = 15): 1) nTiO₂ mixed with isopropyl alcohol/manual application (MAl); 2) nTiO₂ mixed with acetone/manual application (MAc); 3) nTiO₂ mixed with isopropyl alcohol/high-pressure vacuum application (HPVAl); 4) nTiO₂ mixed with acetone/high-pressure vacuum application (HPVAc). As controls, surfaces were sandblasted with Al₂O₃ (OX) or Rocatec silicatization (ROC). All ceramics were sintered after nTiO₂ incorporation. Surface treatments of OX and ROC were made after sintering. Surfaces were characterized by confocal laser microscopy, scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy (EDS). Resin composite cylinders (1.40 mm diameter and 1 mm height) were cemented with a resin cement, stored in water at 37 °C for 24 h and thermocycled for 10 000 cycles before microshear bond strength evaluation. Data were analyzed with one-way ANOVA and Games-Howell (α = 0.05), and fracture analysis was performed using a stereomicroscope.

RESULTS

EDS confirmed the presence of TiO₂ on treated Y-TZP. The confocal analysis showed higher roughness for HPVAc and OX. There were significant differences between surface treatments (p < 0.001). HPVAl (22.96 ± 10.3), OX (34.16 ± 7.9) and ROC (27.71 ± 9.4) showed higher microshear bond strengths and were statistically similar (p > 0.05). MAC showed intermediary values, and HPVAc and MAl presented decreased bond strength, with a high percentage of premature debonding.

CONCLUSION

High-pressure vacuum application of nTiO₂ mixed with isopropyl alcohol was able to produce bond strength values compared to conventional air abrasion and Rocatec silicatization.

SIGNIFICANCE

The infiltration of TiO₂ nanostructures on the pre-sintered Y-TZP is an interesting approach that can improve bond strength without the need of sandblasting methods.

Novel Approaches to Combat Medical Device-Associated BioFilms

Biofilms are aggregates formed as a protective survival state by microorganisms to adapt to the environment and can be resistant to antimicrobial agents and host immune responses due to chemical or physical diffusion barriers, modified nutrient environments, suppression of the growth rate within biofilms, and the genetic adaptation of cells within biofilms. With the widespread use of medical devices, medical device-associated biofilms continue to pose a serious threat to human health, and these biofilms have become the most important source of nosocomial infections. However, traditional antimicrobial agents cannot completely eliminate medical device-associated biofilms. New strategies for the treatment of these biofilms and targeting biofilm infections are urgently required. Several novel approaches have been developed and identified as effective and promising treatments. In this review, we briefly summarize the challenges associated with the treatment of medical device-associated biofilm infections and highlight the latest promising approaches aimed at preventing or eradicating these biofilms.

Antimicrobial Capacity and Surface Alterations Using Photodynamic Therapy and Light Activated Disinfection on Polymer-Infiltrated Ceramic Material Contaminated with Periodontal Bacteria

This study determined the antimicrobial efficiency of light-activated disinfection (LAD) and photodynamic therapy (PDT) on polymer-infiltrated ceramic network (PICN) material contaminated with three periodontal bacteria and explored if PDT and LAD cause PICN surface alterations. Sixty PICN discs were contaminated with Tannerella forsythia, Porphyromonas gingivalis, and Treponema denticola and randomly divided into five groups (n = 12 samples/each) according to the treatment groups: Group PDT-PDT (630 ± 10 nm diode laser) with methylene blue; Group DL-808 nm diode laser in contact mode without photosensitizer; Group MB-methylene blue without light application; Group CHX-0.12% chlorhexidine digluconate solution and; Group NT-no treatment. Each disc was then placed in tubes containing phosphate buffered saline (PBS) and vortexed for 30 s to remove the remaining bacteria from the discs. A total of 10× serial dilutions were performed followed by plating of 30 μL of suspension on Brucella agar plates. The colony forming units (CFU) were calculated after 72 h. PICN discs with the attached biofilms were used for confocal microscopy investigation for live/dead bacterial viability. A random single sample from each group was selected to study the bacterial adherence and topographical alterations on PICN discs under scanning electron microscope (SEM). The PDT group showed higher reduction for each bacterial species and total counts of bacteria assessed followed by the DL group (p < 0.05). When compared with MB group, the two laser groups were significantly superior (p < 0.05). The MB group did not show significant differences for any bacteria when compared to NT. The bacteria with the CHX group and DL groups appeared dead with few areas of surviving green stained bacteria. The PDT group showed the highest dead cell count (p < 0.05). PDT and DL groups indicate no significant changes on the surface compared to the sterile PICN discs on visual assessment. Photodynamic therapy produced superior periodontal bacteria reduction over the surface of PICN surface. PDT group showed higher reduction for each bacterial species and total counts of bacteria assessed followed by the DL group. Both PDT and DL treatment strategies are effective without producing surface alterations on PICN.

Effect of erosive and abrasive challenges on the glaze layer applied to ceramic materials

PURPOSE

This study aims to evaluate the effect of erosive, abrasive, and erosive/abrasive challenges on the glaze layer of ceramic materials.

METHODS

Ninety-five samples of monolithic zirconia (MZ) (LuxaCam Zircon HT-Plus) and lithium disilicate (LD) (IPS e.max CAD) were divided according to the response variables: Surface roughness and surface loss (n = 10), evaluated with optical profilometry; surface topography, with scanning electron microscopy SEM (n = 3); and biofilm deposition, with microbiological assay (n = 5). The evaluations were performed in three different time evaluations: (a) Sintered, (b) Glaze, and (c) Challenge (Erosion, Abrasion, and Erosion/Abrasion). Erosion consisted in immersing specimens in HCl solution, abrasion was performed with brushing machine, and erosion/abrasion consisted of a combination of the two previous protocols. Data were analyzed with parametric tests (P < 0.05).

RESULTS

MZ glaze layer presented significantly higher surface roughness (P = 0.00), surface loss (P = 0.03), and biofilm deposition (P = 0.00) than LD. Abrasion and erosion/abrasion showed similar outcomes, generating significantly higher surface roughness (P = 0.00), surface loss (P = 0.00), and biofilm deposition (P = 0.01) than erosion.

CONCLUSIONS

Glaze layer properties were altered by the challenges, with abrasion and erosion/abrasion generating higher surface roughness, surface loss, and biofilm deposition than erosion. A significant correlation was found between the surface roughness and biofilm deposition.

CLINICAL SIGNIFICANCE

The glaze layer is susceptible to challenges, especially to abrasion and erosion/abrasion, which generated greater surface roughness and surface loss than erosion. The greater surface roughness lead to a greater biofilm deposition on the glaze layer.