Time-dependent Microhardness Gradients of Self-adhesive Resin Cements Under Dual- and Self-curing Modes

Effects of Sr/F-Bioactive Glass Nanoparticles and Calcium Phosphate on Monomer Conversion, Biaxial Flexural Strength, Surface Microhardness, Mass/Volume Changes, and Color Stability of Dual-Cured Dental Composites for Core Build-Up Materials

This study prepared composites for core build-up containing Sr/F bioactive glass nanoparticles (Sr/F-BGNPs) and monocalcium phosphate monohydrate (MCPM) to prevent dental caries. The effect of the additives on the physical/mechanical properties of the materials was examined. Dual-cured resin composites were prepared using dimethacrylate monomers with added Sr/F-BGNPs (5 or 10 wt%) and MCPM (3 or 6 wt%). The additives reduced the light-activated monomer conversion by ~10%, but their effect on the conversion upon self-curing was negligible. The conversions of light-curing or self-curing polymerization of the experimental materials were greater than that of the commercial material. The additives reduced biaxial flexural strength (191 to 155 MPa), modulus (4.4 to 3.3), and surface microhardness (53 to 45 VHN). These values were comparable to that of the commercial material or within the acceptable range of the standard. The changes in the experimental composites’ mass and volume (~1%) were similar to that of the commercial comparison. The color change of the commercial material (1.0) was lower than that of the experimental composites (1.5–5.8). The addition of Sr/F-BGNPs and MCPM negatively affected the physical/mechanical properties of the composites, but the results were satisfactory except for color stability.

Impact of adhesive primer and light-curing on polymerization kinetics of self-adhesive resin cement in association with free radical reaction

This study analyzed the impact of adhesive primer and light-curing on the polymerization kinetics of urethane dimethacrylate-based self-adhesive resin cement combined with free radical reaction. Specimens were prepared by mixing the cement paste with or without adhesive primer. Subsequently, specimens were light-cured or set without light-curing. The degree of conversion (DC), Vickers hardness (Hv), and free radical concentrations were repeatedly measured up to 168 h after the curing initiation. Irrespective of the curing procedures, DC, Hv, and free radical concentration rapidly increased during the initial 30 min of curing. The specimens cured with adhesive primer and/or light-curing generally showed higher values of DC, Hv, and radical concentration than those set by chemical curing alone, especially during the initial polymerization phase. Kinetic analysis using a linear mixed model revealed that the adhesive primer had a higher coefficient estimate than light-curing, indicating that the former had a higher impact on the polymerization. Additionally, the adhesive primer alleviated the Hv reduction caused by water and air during the initial polymerization phase, although light-curing hardly prevented the polymerization inhibition. Therefore, we suggest that application of adhesive primer is beneficial to achieve higher degree of conversion and better mechanical properties of self-adhesive resin cements by enhancing free radical reactions.