Evaluation of the Solubility, Calcium-Release Ability, and Apatite-Forming Ability of a Novel Chemically Curable Mineral Trioxide Aggregate Material

Proposing new standards for testing solubility of pulp preservation materials

OBJECTIVES

Quality control testing of dental materials requires a standard to enable the generation of reproducible and comparable data. Currently there are no standards for testing materials used for vital pulp therapy. The aim of this study was to develop a new standard to evaluate solubility of pulp preservation materials.

METHODS

The solubility of three materials used for vital pulp therapy: Biodentine, TheraCal and Activa was evaluated using two international standards for dental materials ISO 4049:2019 (S1) and ISO 6876:2012 (S2). For both standards, a modified methodology was evaluated. This included changing the volume of the solution used (S1M, S2M), using Dulbecco's modified eagle medium (DMEM) as an alternative to water (S1D, S2D) and periodic solution change for the ISO 4049 method (S1P, S1MP). Materials were characterised before and after completion of solubility test using scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis.

RESULTS

The test materials exhibited different solubility values depending on the methodology used. Biodentine exhibited significantly lower solubility when lower volumes of solution were used when tested using both ISO methods (p ≤ 0.05). TheraCal and Activa showed negative solubility values after desiccation when tested using ISO 4049:2019. The Biodentine exhibited changes in its microstructure which was dependent on the method used to test solubility.

CONCLUSIONS

The solubility values obtained were dependent on the method used. It is thus important to use methods that replicate the clinical environment for meaningful evaluations.

Resin-based dental pulp capping restoration enclosing silica and portlandite nanoparticles from natural resources

Natural-based materials represent green choices for biomedical applications. In this study, resin pulp capping restoration enclosing strengthening silica and bioactive portlandite nanofillers were prepared from industrial wastes. Silica nanoparticles were isolated from rice husk by heat treatment, followed by dissolution/precipitation treatment. Portlandite nanoparticles were prepared by calcination of carbonated lime waste followed by ultrasonic treatment. Both were characterized using x-ray diffraction, energy dispersive x-ray, and transmission electron microscopy. For preparing pulp capping restoration, silica (after silanization) and/or portlandite nanoparticles were mixed with 40/60 weight ratio of bisphenol A-glycidyl methacrylate and triethylene glycol dimethacrylate. Groups A, B, and C enclosing 50 wt.% silica, 25 wt.% silica + 25 wt.% portlandite, and 50 wt.% portlandite, respectively, were prepared. All groups underwent microhardness, compressive strength, calcium release, pH, and apatite forming ability inspection in comparison to mineral trioxide aggregate (MTA) positive control. In comparison to MTA, all experimental groups showed significantly higher compressive strength, group B showed comparable microhardness, and group C showed significantly higher calcium release. Groups B and C showed prominent hydroxyapatite formation. Thus, the preparation of economic, silica-fortified, bioactive pulp capping material from under-utilized agricultural residues (rice husk) and zero-value industrial waste (carbonated lime from sugar industry) could be achieved.

In Vivo Assessment of the Apatite-Forming Ability of New-Generation Hydraulic Calcium Silicate Cements Using a Rat Subcutaneous Implantation Model

Hydroxyapatite formation on endodontic hydraulic calcium silicate cements (HCSCs) plays a significant role in sealing the root canal system and elevating the hard-tissue inductivity of the materials. This study evaluated the in vivo apatite-forming ability of 13 new-generation HCSCs using an original HCSC (white ProRoot MTA: PR) as a positive control. The HCSCs were loaded into polytetrafluoroethylene tubes and implanted in the subcutaneous tissue of 4-week-old male Wistar rats. At 28 days after implantation, hydroxyapatite formation on the HCSC implants was assessed with micro-Raman spectroscopy, surface ultrastructural and elemental characterization, and elemental mapping of the material-tissue interface. Seven new-generation HCSCs and PR had a Raman band for hydroxyapatite (v1 PO₄^3- band at 960 cm^-1) and hydroxyapatite-like calcium-phosphorus-rich spherical precipitates on the surfaces. The other six HCSCs with neither the hydroxyapatite Raman band nor hydroxyapatite-like spherical precipitates did not show calcium-phosphorus-rich hydroxyapatite-layer-like regions in the elemental mapping. These results indicated that 6 of the 13 new-generation HCSCs possessed little or no ability to produce hydroxyapatite in vivo, unlike PR. The weak in vivo apatite-forming ability of the six HCSCs may have a negative impact on their clinical performance.

Calcium Silicate-Based Biocompatible Light-Curable Dental Material for Dental Pulpal Complex

Dental caries causes tooth defects and clinical treatment is essential. To prevent further damage and protect healthy teeth, appropriate dental material is a need. However, the biocompatibility of dental material is needed to secure the oral environment. For this purpose, biocompatible materials were investigated for incorporated with dental capping material. Among them, nanomaterials are applied to dental materials to enhance their chemical, mechanical, and biological properties. This research aimed to study the physicochemical and mechanical properties and biocompatibility of a recently introduced light-curable mineral trioxide aggregate (MTA)-like material without bisphenol A-glycidyl methacrylate (Bis-GMA). To overcome the compromised mechanical properties in the absence of Bis-GMA, silica nanoparticles were synthesized and blended with a dental polymer for the formation of a nano-network. This material was compared with a conventional light-curable MTA-like material that contains Bis-GMA. Investigation of the physiochemical properties followed ISO 4049. Hydroxyl and calcium ion release from the materials was measured over 21 days. The Vickers hardness test and three-point flexural strength test were used to assess the mechanical properties. Specimens were immersed in solutions that mimicked human body plasma for seven days, and surface characteristics were analyzed. Biological properties were assessed by cytotoxicity and biomineralization tests. There was no significant difference between the tested materials with respect to overall physicochemical properties and released calcium ions. The newly produced material released more calcium ions on the third day, but 14 days later, the other material containing Bis-GMA released higher levels of calcium ions. The microhardness was reduced in a low pH environment, and differences between the specimens were observed. The flexural strength of the newly developed material was significantly higher, and different surface morphologies were detected. The recently produced extract showed higher cell viability at an extract concentration of 100%, while mineralization was clear at the conventional concentration of 25%. No significant changes in the physical properties between Bis-GMA incorporate material and nanoparticle incorporate materials.