Design of cationic surfactant reinforced carrageenan waterproof composite films and applied as water induced electricity generator

Carrageenan (CR) is a renewable polysaccharide material for packaging application due to its good film-forming property, but its use can be limited by the water solubility. In this research, CR hydrogels were modified by quaternary ammonium surfactants with different length of hydrocarbon tails (n, 8≦n≦16) by adsorption method and waterproof films were obtained after drying. The composition and charge interaction of composite films was confirmed by FTIR. Both thermogravimetric analysis and energy dispersive spectrometer indicated that the surfactant ions replaced K+ to form complexes with CR. The X-ray diffraction revealed the decreased amorphous nature of composite films compared to neat CR film. Water-related physical properties, such as water content, weight percentage change after contact with water, water vapor transmission, and water contact angle were intimately related to n. When 8≦n≦14, the waterproof properties were enhanced with the increase of n. Meanwhile, the waterproof property of composite film was ascertained by the no leakage result in the boiling water packaging experiment. When n = 16, sandwich structure was found in the sectional micromorphology images, and water bag structure formed after immersed into water. By comparing the mechanical properties of the composite films in different condition, we found that quaternary ammonium surfactants improved significantly the tensile strength in water and increased elongation at break in dry state. The composite films can be used as water induced voltage generator for their polyelectrolyte nature. Benefiting from the high stability of the composite films in water, their water-induced voltage generation process had good recyclability. Due to the antimicrobial activity of the quaternary ammonium salts and the waterproof property, composite films were more stable and degraded more slowly than neat CR film in nature environment.

Dissolution of cellulose into supercritical water and its dissolving state followed by structure formation from the solution system

Cellulose was treated with supercritical water at 668 K and 25 MPa for 0.04 s in this study. The cellulose/water system was transparent at room temperature for a while after supercritical water treatment before a precipitate gradually appeared over several hours. The precipitation process was monitored by synchrotron X-ray scattering. The scattering functions of fractal systems and flat-like structures were utilized to explain the experimentally observed small-angle scattering profiles. Immediately after supercritical water treatment, the cellulose appeared to dissolve with a fractal dimension D of approximately 1, indicating that the cellulose molecules were rigid, followed by aggregation into a 5-nm-thick flat-like structure. The flat-like structure was determined to be similar to the molecular sheets observed during the early stages of precipitation in the cellulose/aqueous sodium hydroxide and cellulose/aqueous lithium hydroxide/urea systems. Resultant regenerated cellulose had high crystallinity, large crystal size, and a low degree of polymerization.

Studies on methylcellulose/pectin/montmorillonite nanocomposite films and their application possibilities

Films based on methylcellulose (MC) and pectin (PEC) of different ratios were prepared. MC/PEC (90:10) (MP10) gave the best results in terms of mechanical properties. Sodium montmorillonite (MMT) (1, 3 and 5 wt%) was incorporated in the MP10 matrix. The resulting films were characterized by X-ray diffraction and transmission electron microscopy, and it was found that nanocomposites were intercalated in nature. Mechanical studies established that addition of 3 wt% MMT gave best results in terms of mechanical properties. However, thermo-gravimetric and dynamic mechanical analysis proved that decomposition and glass transition temperature increased with increasing MMT concentration from 1 to 5 wt%. It was also observed that moisture absorption and water vapor permeability studies gave best result in the case of 3 wt% MMT. Optical clarity of the nanocomposite films was not much affected with loading of MMT. In vitro drug release studies showed that MC/PEC/MMT based films can be used for controlled transdermal drug delivery applications.